Environment-friendly antistatic anti-corrosion paint and preparation method thereof

An anti-corrosion coating and anti-static technology, applied in anti-corrosion coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems affecting people's health, toxic volatiles, carcinogenicity, etc., and achieve excellent anti-corrosion performance, easy to obtain, and easy to use long life effect

Inactive Publication Date: 2015-12-23
刘广利
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most anti-corrosion coatings currently on the market contain volatile organic solvents, some of which are toxic or even carcinogenic, seriously affecting people's health; in addition, with the popularization of electronic products, the electromagnetic wave signals in the surrounding environment are getting stronger and stronger, and radiation interference It is also becoming more and more serious, so higher requirements are put forward for the antistatic ability of equipment products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The preparation method of the environment-friendly antistatic anticorrosion coating, the specific preparation steps include:

[0020] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 40 parts of water-based polyurethane emulsion, 30 parts of water-based acrylic resin, 5 parts of copper sulfide, 5 parts of montmorillonite, 3 parts of conductive mica powder, potassium titanate 10 parts of whiskers, 10 parts of zinc oxide whiskers, 3 parts of calcium carbonate, 3 parts of zinc oleate, 3 parts of polyoxypropylene laurate, 3 parts of sodium lauryl sulfate, 1 part of leveling agent, defoamer 0.3 parts, 10 parts ethanol and 80 parts deionized water. ;

[0021] Step 2: Dissolve sodium lauryl sulfate in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 1 hour, then grind and disperse the slurry to 2500 Mesh fineness;

[0022] Step 3: Add water-based ...

Embodiment 2

[0025] The preparation method of the environment-friendly antistatic anticorrosion coating, the specific preparation steps include:

[0026] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 65 parts of water-based polyurethane emulsion, 45 parts of water-based acrylic resin, 15 parts of copper sulfide, 15 parts of montmorillonite, 12 parts of conductive mica powder, potassium titanate 20 parts of whiskers, 20 parts of zinc oxide whiskers, 12 parts of calcium carbonate, 8 parts of zinc oleate, 8 parts of polyoxypropylene laurate, 6 parts of sodium lauryl sulfate, 2 parts of leveling agent, defoamer 2 parts, 25 parts ethanol and 100 parts deionized water. ;

[0027] Step 2: Dissolve sodium lauryl sulfate in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 4 hours, then grind and disperse the slurry to 2500 Mesh fineness;

[0028] Step 3: Add water-b...

Embodiment 3

[0031] The preparation method of the environment-friendly antistatic anticorrosion coating, the specific preparation steps include:

[0032] Step 1: Weigh raw materials according to certain parts by weight: according to parts by weight: 45 parts of water-based polyurethane emulsion, 33 parts of water-based acrylic resin, 8 parts of copper sulfide, 8 parts of montmorillonite, 5 parts of conductive mica powder, potassium titanate 12 parts of whiskers, 12 parts of zinc oxide whiskers, 5 parts of calcium carbonate, 4 parts of zinc oleate, 4 parts of polyoxypropylene laurate, 4 parts of sodium lauryl sulfate, 1.2 parts of leveling agent, defoamer 0.5 parts, 12 parts of ethanol and 82 parts of deionized water;

[0033] Step 2: Dissolve the sodium lauryl sulfate in the raw material in deionized water, then add copper sulfide, montmorillonite, conductive mica powder, calcium carbonate and ethanol, stir and mix for 2.5 hours, then grind and disperse the slurry to 2500 mesh fineness; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly antistatic anti-corrosion paint and a preparation method thereof. The environment-friendly antistatic anti-corrosion paint is prepared from, by weight, 40-65 parts of waterborne polyurethane emulsion, 30-45 parts of waterborne acrylic resin, 5-15 parts of copper sulphide, 5-15 parts of montmorillonite, 3-12 parts of conductive mica powder, 10-20 parts of potassium titanate whiskers, 10-20 parts of zinc oxide whiskers, 3-12 parts of calcium carbonate, 3-8 parts of zinc oleate, 3-8 parts of poly[oxy(methyl-1,2-ethanediyl)], 3-6 parts of lauryl sodium sulfate, 1-2 parts of flatting agents, 0.3-2 parts of defoaming agents, 10-25 parts of ethyl alcohol and 80-100 parts of deionized water. The surface resistance of the prepared paint is large, and good anti-static capacity is displayed. Besides, the conductive mica powder and the copper sulphide are low in cost of raw materials, easy to obtain and suitable for being widely used. The prepared paint has good water resistance and acid resistance, shows excellent corrosion resistance, and is long in actual service life and stable.

Description

technical field [0001] The invention belongs to the field of anti-corrosion coatings, in particular to an environment-friendly anti-static anti-corrosion coating and a preparation method thereof. Background technique [0002] Among the many protective measures, painting is one of the most convenient, quick and effective protective measures. Coating is to apply paint on the surface of equipment products, which can play an insulating role to reduce the corrosion of equipment products by the external environment, prolong the service life of equipment, and reduce the cost of use. As people's requirements for the living environment are getting higher and higher, more and more attention is paid to environmental protection issues. However, most anti-corrosion coatings currently on the market contain volatile organic solvents, some of which are toxic or even carcinogenic, seriously affecting people's health; in addition, with the popularization of electronic products, the electroma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D133/00C09D7/12C09D5/08
Inventor 刘广利
Owner 刘广利
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com