Continuous preparation method for catalytically synthesizing polyvinyl butyral resin through organic acid

The technology of polyvinyl butyral resin and polyvinyl alcohol is applied in the field of continuous preparation of organic acid catalyzed synthesis of polyvinyl butyral resin, and achieves the effects of uniform particles, high acetal degree and good product quality

Inactive Publication Date: 2015-10-28
SICHUAN DONGFANG INSULATING MATERIAL
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention aims at the problem that in the existing heterogeneous synthesis process of polyvinyl butyral resin, the mixing effect of PVA and n-butyraldehyde cannot be effectively combined, the effective control of reaction rate and the continuous preparation can be effectively combined, and an effective method is provided. Continuous preparation method for synthesizing polyvinyl butyral resin with organic acid as catalyst, improved production efficiency, reduced energy consumption, good and stable product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous preparation method for catalytically synthesizing polyvinyl butyral resin through organic acid
  • Continuous preparation method for catalytically synthesizing polyvinyl butyral resin through organic acid
  • Continuous preparation method for catalytically synthesizing polyvinyl butyral resin through organic acid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～8

[0035] The continuous preparation method of polyvinyl butyral resin synthesized by organic acid catalysis, the steps are:

[0036] a. Preparation of polyvinyl alcohol-n-butyraldehyde aqueous emulsion:

[0037] Add 565-1900 parts by mass of water into the dissolution kettle, add 100 parts by mass of polyvinyl alcohol under stirring, keep warm at 60°C±2°C for 0.5h, raise the temperature to 95°C±2°C and keep warm for 2h to make the polyvinyl alcohol Dissolve completely, cool down to 40°C-60°C and filter to obtain 665-2000 parts by mass of polyvinyl alcohol aqueous solution, then put the obtained polyvinyl alcohol aqueous solution and 55-80 mass parts of n-butyraldehyde that have been filtered at 30°C-50°C Stir with an emulsifier for 20 to 60 minutes, so that polyvinyl alcohol and n-butyraldehyde are fully mixed, and 720 to 2080 parts by mass of polyvinyl alcohol-n-butyraldehyde aqueous emulsion are obtained;

[0038] b. Preparation of polyvinyl butyral resin:

[0039] The 500 m...

Embodiment 9

[0051] The continuous preparation method of polyvinyl butyral resin synthesized by organic acid catalysis, the steps are:

[0052] a. Preparation of polyvinyl alcohol-n-butyraldehyde aqueous emulsion:

[0053] Add 565 parts by mass of water into the dissolution kettle, add 100 parts by mass of polyvinyl alcohol under stirring, keep the temperature at 58°C for 0.5h, raise the temperature to 93°C and keep it warm for 2h (to completely dissolve the polyvinyl alcohol), and cool down to Filtrate at 40°C to obtain a polyvinyl alcohol aqueous solution, then mix the polyvinyl alcohol aqueous solution and 55 parts by mass of n-butyraldehyde at a temperature of 30°C through an emulsifier for 20 to 60 minutes to fully mix the polyvinyl alcohol and n-butyraldehyde to obtain polyethylene Alcohol-n-butyraldehyde aqueous emulsion;

[0054] b. Preparation of polyvinyl butyral resin:

[0055] Take 500 mass parts of the polyvinyl alcohol-n-butyraldehyde aqueous emulsion and 100 mass parts of ...

Embodiment 10

[0058] The continuous preparation method of polyvinyl butyral resin synthesized by organic acid catalysis, the steps are:

[0059] a. Preparation of polyvinyl alcohol-n-butyraldehyde aqueous emulsion:

[0060] Add 1900 parts by mass of water into the dissolution kettle, add 100 parts by mass of polyvinyl alcohol under stirring, keep the temperature at 62°C for 0.5h, raise the temperature to 97°C and keep it warm for 2h (to completely dissolve the polyvinyl alcohol), and cool down to Filtrate at 60°C to obtain an aqueous solution of polyvinyl alcohol, then stir the aqueous solution of polyvinyl alcohol and 80 parts by mass of n-butyraldehyde at a temperature of 50°C through an emulsifier for 60 minutes to fully mix the polyvinyl alcohol and n-butyraldehyde to obtain polyvinyl alcohol- Butyraldehyde aqueous emulsion;

[0061] b. Preparation of polyvinyl butyral resin:

[0062] Get 500 mass parts of polyvinyl alcohol-n-butyraldehyde aqueous emulsion and (configured, preferably ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a continuous preparation method for catalytically synthesizing polyvinyl butyral resin through organic acid. The continuous preparation method is characterized in that by mass, 500 parts of polyvinyl alcohol-n-butyl aldehyde aqueous emulsion is prepared and continuously and simultaneously put into a high-shear mixer with 100 parts of 2.5% organic acid aqueous emulsion, and the polyvinyl alcohol-n-butyl aldehyde aqueous emulsion and the 2.5% organic acid aqueous emulsion are mixed and react for 10 min-20 min at shearing rate of 50S-1-150S-1 with the shear force 50 Pa-150 Pa at 30 DEG C-40 DEG C, then are sent to an aging kettle and sequentially processed through first-stage reaction at 39-41 DEG C for 3-4 h and second-stage reaction at 59-61 DEG C for 2-3 h to complete the polymerization process; mother liquid is removed through a centrifugal machine, solid substances are processed through water washing, alkali washing, water washing and drying, and then the powder polyvinyl butyral resin is prepared. The continuous preparation method is continuous in preparation, high in efficiency, low in energy consumption and stable in product quality; the prepared polyvinyl butyral resin is suitable for the fields of photovoltaicpackaging materials, architectural safety glass, safety glass for cars and the like.

Description

technical field [0001] The invention belongs to the preparation of organic macromolecular compounds, and relates to a continuous preparation method for synthesizing polyvinyl butyral resin by organic acid catalysis. The polyvinyl butyral resin product produced by the invention is suitable for the fields of safety glass for automobiles, photovoltaic encapsulation materials, safety glass for buildings, inks, paints, adhesives and the like. Background technique [0002] Polyvinyl butyral (PVB for short) is obtained by acetalization reaction of polyvinyl alcohol (PVA for short) and n-butyraldehyde (BA for short) under acid catalysis. Due to the good flexibility of PVB molecules, PVB resin has good film-forming properties, mechanical properties, optical properties, insulation, solubility, etc., and is widely used in automotive safety glass, photovoltaic packaging materials, architectural safety glass, inks, coatings , Adhesives and other fields. [0003] The synthesis process o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F8/28C08F16/06
Inventor 刘明徐康林陈小强廖曦唐安斌
Owner SICHUAN DONGFANG INSULATING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap