Cutting-resistant conveying belt covering glue and preparation method thereof

A technology of conveyor belt and covering glue, applied in the field of conveyor belt, can solve the problem of covering glue without cutting resistance and other problems, and achieve the effect of comprehensive reinforcement, increase of benzene ring content, and comprehensive processability.

Inactive Publication Date: 2015-09-09
WUXI BOTON TECH CO LTD
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the commercially available cut-resistant conveyor belts mainly use high-modulus fiber materials or steel mesh as the skeleton material, but the covering rubber that carries the material itself has no obvious cut-resistant performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Mastication: Take 80 parts of nano-clay styrene-butadiene masterbatch and 20 parts of natural rubber to masticate on the open mill with a roller distance of 2 mm and a roller temperature of 45° C., and masticate for 20 minutes to obtain the masticated rubber;

[0025] (2) One-stage mixing: Put the plasticized rubber prepared in step (1) into the internal mixer, and banbury for 2 minutes; then lift the top bolt and add 3 parts of nano-zinc oxide, 1 part of stearic acid, and 1 part of anti-aging agent RD 2 parts, anti-aging agent 4020 2 parts, microcrystalline wax 2 parts, basalt fiber 3 parts, carbon black N115 35 parts, carbon black N330 15 parts, aromatic oil 5 parts, high styrene resin 10 parts, banburying 5min, debinding temperature Controlled at 150°C, after 5 minutes of kneading, the sheet is produced according to the thickness of 8mm, cooled by a fan at room temperature to obtain a section of mixed rubber, and parked for 8 hours;

[0026] (3) Two-stage mixing:...

Embodiment 2

[0029] (1) Mastication: Take 60 parts of nano-clay styrene-butadiene masterbatch and 40 parts of natural rubber to masticate on the open mill with a roller distance of 3 mm and a roller temperature of 40° C., and masticate for 10 minutes to obtain the masticated rubber;

[0030] (2) One-stage mixing: Put the plasticized rubber prepared in step (1) into the internal mixer, and banbury for 1 minute; then lift the top bolt and add 6 parts of nano-zinc oxide, 3 parts of stearic acid, and 4020 1 parts of anti-aging agent 1 part, 1 part of aramid fiber, 30 parts of carbon black N234, 2 parts of octylphenolic BN-1, 3 parts of aromatic oil, banburying for 3 minutes, the temperature of debinding is controlled at 145 ° C, and the sheet is produced according to the thickness of 10 mm after smelting. A section of mixed rubber was obtained by cooling with a fan at room temperature, and parked for 6 hours;

[0031] (3) Two-stage mixing: Take the first-stage compound rubber prepared in step ...

Embodiment 3

[0034] (1) Mastication: Take 20 parts of nano-clay styrene-butadiene masterbatch and 80 parts of natural rubber to masticate on the open mill, with a roller distance of 2 mm and a roller temperature of 60° C., and masticate for 15 minutes to obtain the masticated rubber;

[0035] (2) One-stage mixing: put the plasticized rubber prepared in step (1) into the internal mixer, and banbury for 2 minutes; then lift the top bolt and add 5 parts of nano-zinc oxide, 1 part of stearic acid, and 1 part of anti-aging agent BLE 2 parts, anti-aging agent 4020 2 parts, protective wax 2 parts, ultra-high molecular weight polyethylene fiber 4 parts, carbon black N550 30 parts, carbon black N220 40 parts, coumarone 5 parts, aromatic oil 10 parts, octylphenolic BN- 2. 5 parts, 5 parts of high styrene resin, banburying for 4 minutes, the glue discharge temperature is controlled at 130 ° C, after 7 minutes of smelting, the sheet is produced according to the thickness of 12 mm, cooled by a fan at ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to cutting-resistant conveying belt covering glue and a preparation method thereof and belongs to the technical field of conveying belts. The preparation method includes: adding nano-clay butylbenzene masterbatch and natural rubber into an internal mixer, sequentially adding zinc oxide, stearic acid, antiager, short fiber, reinforcing agent and softener, and mixing before stopping to obtain first-stage mixing glue; adding sulphur and promoter into the first-stage mixing glue for second-stage mixing; vulcanizing to obtain the cutting-resistant conveying belt covering glue. The nano-clay utylbenzene masterbatch and the natural rubber are adopted as a rubber matrix, so that modulus, elasticity and aging resistance of the rubber matrix are taken into consideration; the short fiber is adopted to enhance modulus of a rubber system and absorb energy generated by colloid cutting; highly-combined styrene resin is adopted to increase benzene ring content and increase modulus of the rubber system; soft carbon black and hard carbon black are adopted, so that reinforcing performance and processability are integrated.

Description

technical field [0001] The invention relates to a cutting-resistant conveyor belt covering glue and a preparation method thereof. The prepared product has good cutting resistance, is used in conveyor belt products, and can be widely used in coal mines, metal mines and other working conditions, and belongs to the conveyor belt technology field. Background technique [0002] Conveyor belts are widely used in cement, mines, ports and other industries, and the working conditions of the conveyor belt and the characteristics of the transported materials determine the characteristics that the conveyor belt should have. For example, the cement industry generally needs high temperature resistant conveyor belts, and the coal mining industry needs flame retardant conveyor belts. [0003] It is reported that when foreign mines transport bulky, sharp-edged materials, there is a height difference of more than 2m between the material and the horizontally running conveyor belt, causing the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L9/06C08L7/00C08K13/02C08K3/22C08K5/09C08K3/06C08K3/04B29B7/74
CPCC08L9/06B29B7/74C08K2201/011C08K2201/014C08L7/00C08L2205/035C08L2205/16C08L2207/068C08L91/06C08L91/00C08L51/04C08K13/04C08K7/10C08K3/346C08K2003/2296C08K5/09C08K3/04C08L77/10C08L61/06C08K13/02C08L23/06C08L45/02C08K7/06C08K7/14
Inventor 范旭梦吴建国孙业斌萨日娜吴宇航徐春安
Owner WUXI BOTON TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka