Material for sculpture imitating iron or copper and its construction technology

A technology of sculpture and copper imitation, which is applied in the field of iron or copper imitation sculpture materials and its construction technology. high degree of effect

Active Publication Date: 2019-05-10
泉州市嘉利来石材工艺有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The manufacturing method of this imitation copper handicraft has the following disadvantages: the formation operation of the imitation copper layer on the surface is complicated; This surface coating is filled and leveled, which in turn affects the visual effect of handicrafts; outdoor handicrafts will accelerate the delamination of the surface coating and the substrate after being exposed to the sun and rain; the copper layer on the surface of handicrafts cannot be refurbished after long-term oxidation; existing handicrafts Most of them are heavier than FRP products; existing handicrafts are easy to be damaged and have high requirements for packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material for sculpture imitating iron or copper and its construction technology
  • Material for sculpture imitating iron or copper and its construction technology
  • Material for sculpture imitating iron or copper and its construction technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A copper-like sculpture material, the formula of which includes 5 parts by weight of solid materials, 1 part by weight of blended glue solution and 0.01-0.1 parts by weight of acid dye;

[0032] Described solid material is made up of the component of following parts by weight:

[0033]

[0034]

[0035] Described blending glue solution is made up of the component of following parts by weight:

[0036] 65 parts of water

[0037] 901 construction glue 35 parts

[0038] Polycarboxylate superplasticizer 1 part.

[0039] Further, the acidic coloring agent is sea blue coloring agent.

[0040] The construction technology of the bronze-like sculpture material comprises the following steps:

[0041] (1) Prepare solid materials: weigh various materials according to the ratio of solid materials, pour them into a mixer, and stir them for 1 to 2 hours at normal temperature at a speed of 400 to 500 rpm, then pour them out and set aside;

[0042] (2) Prepare the blended glu...

Embodiment 2

[0050] A copper-like sculpture material, the formula of which includes 5 parts by weight of solid materials, 1 part by weight of blended glue solution and 0.01-0.1 parts by weight of acid dye;

[0051] Described solid material is made up of the component of following parts by weight:

[0052]

[0053]

[0054] Described blending glue solution is made up of the component of following parts by weight:

[0055] 89.5 parts of water

[0056] 901 construction glue 10 parts

[0057] Polycarboxylate superplasticizer 0.5 part.

[0058] The acidic dyes are sea blue, reddish brown and burnt brown dyes.

[0059] The construction technology of the bronze-like sculpture material comprises the following steps:

[0060] (1) Prepare solid materials: weigh various materials according to the ratio of solid materials, pour them into a mixer, and stir them for 1 to 2 hours at normal temperature at a speed of 400 to 500 rpm, then pour them out and set aside;

[0061] (2) Prepare the blen...

Embodiment 3

[0069] A copper-like sculpture material, the formula of which includes 5 parts by weight of solid materials, 1 part by weight of blended glue solution and 0.01-0.1 parts by weight of acid dye;

[0070] Described solid material is made up of the component of following parts by weight:

[0071]

[0072]

[0073] Described blending glue solution is made up of the component of following parts by weight:

[0074] 70 parts of water

[0075] 901 construction glue 30 parts

[0076] Polycarboxylate superplasticizer 1 part.

[0077] The acidic dyes are dark brown dyes and burnt brown dyes.

[0078] The construction technology of the bronze-like sculpture material comprises the following steps:

[0079] (1) Prepare solid materials: weigh various materials according to the ratio of solid materials, pour them into a mixer, and stir them for 1 to 2 hours at normal temperature at a speed of 400 to 500 rpm, then pour them out and set aside;

[0080] (2) Prepare the blended glue sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a material for an iron- or copper-imitated sculpture, which is prepared from 5 parts by weight of solid materials, 1 part by weight of a blending glue solution and 0.01-0.1 part by weight of an acidic dyeing agent, wherein the solid materials comprise the following components in parts by weight: 19.2-24 parts of common 425 cement, 24-28.8 parts of common 425 white cement, 4.8-6.35 parts of 40-mesh sand, 24-30 parts of 60-mesh sand, 3.2-4.5 parts of 80-mesh sand, 1-3 parts of 4A zeolite powder, 18.5-25 parts of white bravertine, 0.03-0.1 part of PP fibers and 0.3-1.4 parts of yellow toner for cement. The material for the iron- or copper-imitated sculpture disclosed by the invention is low in raw material price, and simple in construction process, and the made sculpture is high in product simulation degree, green and environmentally friendly, firm and weather-resistant, free of peeling, and coating-free.

Description

technical field [0001] The invention relates to a sculpture material, in particular to an iron-like or copper-like sculpture material and a construction process thereof. Background technique [0002] Imitation iron or imitation copper crafts are common crafts with metal texture. [0003] At present, imitation copper handicrafts are basically made by spraying or brushing the metal layer on the surface of the substrate. [0004] For example, the Chinese invention patent "copper imitation paint and its preparation method and construction technology" whose publication number is CN101962508B discloses a kind of copper imitation paint and its preparation method and construction technology. [0005] The imitation copper paint includes epoxy gray primer, copper powder baking paint, the first finish matte paint, translucent black topcoat and the second finish matte paint on the surface to be constructed layer by layer; It is made by spraying imitation copper paint on the surface. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B14/06C04B16/06
Inventor 张俊平陈菊燕王进平刑应明刘丽萍
Owner 泉州市嘉利来石材工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com