Three-color energy-storage luminescent composite wood-grain stone material

A technology of energy storage and luminescence, wood grain stone waste, applied in the field of colored luminescent composite wood grain stone and its preparation, can solve the problems of waste of resources, limited effect, lack of development prospects, etc., and achieve improved strength and wear resistance, good Color and texture patterns, the effect of broad market prospects

Inactive Publication Date: 2015-08-12
WUDING COUNTY STONE CO LTD TIAN HAO
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, the generation of a large amount of waste will seriously restrict the development of wood grain stone industry
[0003] Although there are related technologies of artificial stone in the prior art, such as "a method for making artificial marble" (patent application number: 200910192348.4), which can make use of waste stone and solve the problem of waste of resources, artificial marble has strength Low, radioactive pollution, and poor aesthetics for viewing at night, so the usage has been shrinking, lacking development prospects
[0004] Literature Chinese patent literature "Yingming Marble Pattern Decorative Board" (Application No.: 87200699) discloses a stone material with ornamental value at night, but it is based on a prefabricated concrete board, which is layered and compounded with luminescent powder And resin, because this kind of board adopts the method of layered processing, the process is complicated, the product cost is high, the strength of the material is low, and the texture and color are not bright enough.
[0005] The Chinese patent document "Energy Storage Luminous Composite Stone" (Application No.: 200510136868.5) discloses an artificial luminescent stone made of translucent marble mixed with resin. Increased manufacturing costs over the previous patent application
However, as mentioned in the article, the strength of natural marble is low. Although the strength can be increased by the amount of resin, the effect is limited; in addition, the light transmission of light-transmitting marble is not good enough, and the luminous effect of the finished product is not satisfactory. , but also lacks the beauty of color; marble has certain radioactive pollution, and this product should not be used in high-grade building materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Example 1: The percentage by weight of each grade of glass sand is: 5~6#34.5%, 6~8#23%, 8~10#15%, 10~16#14.5% and 16~30#13%. The weight percentage of each grade of light yellow wood grain stone waste is: 5# 37%, 6# 38%, 4~325 mesh fine powder 25%. The proportion of raw materials by weight is 5% of glass sand, 13% of epoxy resin, 0.26% of curing agent, 0.3% of coupling agent, each accounting for one-third of the red, green and blue Yu Changhui energy-storage luminescent raw materials, a total of 4% , titanium dioxide 1.5%, wood grain stone powder 75.94%, and an accelerator with a total amount of 0.64‰. First, mix glass sand and light yellow wood grain stone waste stone powder evenly, then add epoxy resin and titanium dioxide and stir evenly for 8-11 minutes, then add coupling agent and stir for 8-11 minutes, and finally add curing agent and stir for 1 ~ 3 minutes, sent to the press machine for film forming, and then sent to the dryer to dry at 65 ~ 80 ° C for 3.5 ~ 4.5 ...

Embodiment 2

[0013] Example 2: The weight percentages of each grade of glass sand are: 5~6#25%, 6~8#26%, 8~10#17%, 10~16#17% and 16~30#15%. The weight percentage of each grade of red wood grain stone waste is: 5# 39%, 6# 41%, 4~325 mesh fine powder 20%. The proportion of raw materials by weight is 7% of glass sand, 15% of epoxy resin, 0.65% of curing agent, 0.6% of coupling agent, and one-third of red, green and blue alumina activated by rare earth elements A total of 6% of salt and silicate self-luminous materials, 2.5% of titanium dioxide, 68.25% of wood grain stone powder, and an accelerator of 0.64‰ in total. First, mix glass sand and wood grain stone waste stone powder evenly, then add epoxy resin and titanium dioxide and stir evenly for 8-11 minutes, then add coupling agent and stir for 8-11 minutes, and finally add curing agent and stir for 1-2 minutes After 3 minutes, send it to the platen machine for film forming, and then send it to the dryer to dry for 3.5-4.5 hours at 65-80°C....

Embodiment 3

[0014] Embodiment 3: The percentage by weight of each grade of glass sand is: 5~6#: 30%, 6~8#24%, 8~10#16%, 10~16#16% and 16~30#14%. The weight percentage of each grade of wood grain stone waste is: 5# 38%, 6# 39%, 4~325 mesh fine powder 23%. The ratio of raw materials by weight is 6% of glass sand, 14% of epoxy resin, 0.5% of curing agent, and 0.5% of coupling agent. %, titanium dioxide 2.5%, wood grain stone powder 72%, and an accelerator with a total amount of 0.64‰. First, mix glass sand and wood grain stone waste stone powder evenly, then add epoxy resin and titanium dioxide and stir evenly for 8-11 minutes, then add coupling agent and stir for 8-11 minutes, and finally add curing agent and stir for 1-2 minutes After 3 minutes, send it to the platen machine for film forming, and then send it to the dryer to dry for 3.5-4.5 hours at 65-80°C. The thickness is fixed in the thickness-calibrating machine, polished and trimmed to obtain red, green and blue colors. of three-co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technology of processing of artificial stone materials and especially relates to a colorized three-color energy-storage luminescent composite wood-grain stone material and a preparation method of the same. The stone material includes following components, by weight: 4.5-7% of glass sand (which is granules after glass waste materials crushed), 12.5-15.5% of epoxy resin, 0.26-0.65% of a curing agent, 0.3-0.7% of a coupling agent, 4-6% of luminescent stone powder comprising three colors, wherein each color accounts for 1 / 3 of the total amount, 1.5-2.5% of titanium dioxide and the balance being a wood-grain stone waste material, wherein the granularity distribution of the glass sand is 2-70 meshes and the granularity distribution of the wood-grain stone waste material is 4-325 meshes. The cured moulded stone material is dried at 65-80 DEG C. The stone material is good in night luminescent effect, is high in strength, is colorful, is free or radiation pollution and is low in production cost.

Description

technical field [0001] The invention belongs to the processing technology of artificial stone, in particular to a colored luminescent composite wood-grain stone and a preparation method thereof. Background technique [0002] Wood grain stone is produced in the bottom of Cambrian system, which belongs to marine sediments, and is iron-rich argillaceous dolomite. High-quality sandstone has a compact structure, uniform particles, fine texture, high water absorption, and has the characteristics of sound insulation, moisture absorption, damage resistance, weathering resistance, fading resistance, insolubility in water, and no radioactivity. Wood grain stone has good ornamental value due to its powder crystal, fine crystal structure and pattern similar to wood texture. Therefore, it is often used in indoor and outdoor decoration, furniture, sculpture art, and garden building materials. It is a rare Class A stone. Wuding County, Yunnan Province is rich in wood-grained stone resour...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B26/14C04B14/02C04B14/22
Inventor 田莉
Owner WUDING COUNTY STONE CO LTD TIAN HAO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products