Fireproof thermal-insulation composite slurry with strong adhesive force

A technology with fire protection, heat preservation and strong adhesion, which is applied in the field of construction slurry, which can solve the problems of building energy saving and leakage prevention, fire prevention, poor crack resistance and waterproof ability, easy cracking and leakage, etc., so as to achieve good fire prevention effect and prevent Effects of shrinkage cracking and thermal insulation improvement

Inactive Publication Date: 2015-05-20
青岛诚运建筑工程有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polystyrene particle mortar system in the prior art is simple in construction, but its disadvantages are poor bonding strength, high water absorption, and easy cracking and leakage
The blocking effect on heat convection and sunlight radiation is poor, and the crack resistance and waterproof ability are also poor, which cannot meet the new requirements of building energy saving, leakage prevention and fire prevention.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A fire-resistant and heat-insulating composite slurry with strong adhesion, characterized in that the components of the slurry are composed as follows in parts by weight:

[0017] Cement 15 parts, latex powder 3 parts, hydroxyethyl methyl cellulose, polypropylene anti-cracking fiber and polypropylene fiber according to 2:1:1 composition of cellulose ether 5 parts, fly ash, calcium carbonate and clay according to 4 :2:1 composition of fiber additives 1.5 parts, perlite 8 parts, melting point 25-28°C, 0.7 parts coconut oil with fatty acid content above 90%, vitamin E 0.1 part, polystyrene foam powder 12 parts, dispersible glue 0.8 parts of powder, 0.5 parts of sodium alginate, 0.5 parts of vinegar-soluble chitosan, 0.8 parts of sodium polyacrylate, 0.3 parts of sodium lauryl sulfonate, and 100 parts of water.

Embodiment 2

[0019] A fire-resistant and heat-insulating composite slurry with strong adhesion, characterized in that the components of the slurry are composed as follows in parts by weight:

[0020] 18 parts of cement, 4 parts of latex powder, 6 parts of cellulose ether composed of hydroxyethyl methyl cellulose, polypropylene anti-cracking fiber and polypropylene fiber according to 2:1:1 composition, fly ash, calcium carbonate and clay according to 4 :2:1 composition fiber additives 1.3 parts, perlite 10 parts, melting point 25-28°C, 0.5 parts coconut oil with fatty acid content above 90%, vitamin E 0.2 parts, polystyrene foam powder 13 parts, dispersible glue 0.9 parts of powder, 0.5 parts of sodium alginate, 0.5 parts of vinegar-soluble chitosan, 0.7 parts of sodium polyacrylate, 0.5 parts of sodium lauryl sulfate, and 100 parts of water.

Embodiment 3

[0022] A fire-resistant and heat-insulating composite slurry with strong adhesion, characterized in that the components of the slurry are composed as follows in parts by weight:

[0023] 20 parts of cement, 5 parts of latex powder, 7 parts of cellulose ether composed of hydroxyethyl methyl cellulose, polypropylene anti-cracking fiber and polypropylene fiber according to 2:1:1, fly ash, calcium carbonate and clay according to 4 :1 part of 2:1 fiber additive, 8 parts of perlite, melting point 25-28℃, 0.6 part of coconut oil with fatty acid content of 90% or more, 0.2 part of vitamin E, 15 parts of polystyrene foam powder, dispersible glue 1 part of powder, 0.6 part of sodium alginate, 0.7 part of vinegar-soluble chitosan, 0.6 part of sodium polyacrylate, 0.5 part of alkylbenzene sulfonate, and 100 parts of water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fireproof thermal-insulation composite slurry with a strong adhesive force. The slurry is characterized by being composed of the following components in parts by weight: 15 to 20 parts of cement, 3 to 5 parts of latex powder, 5 to 7 parts of cellulose ether, 1 to 1.5 parts of fiber additive, 8 to 12 parts of perlite, 0.4 to 0.7 part of coconut oil, 0.1 to 0.3 part of vitamin E, 12 to 15 parts of polystyrene foamed powder, 0.8 to 1 part of dispersible rubber powder, 0.5 to 0.6 part of sodium alginate, 0.5 to 0.8 part of vinegar-dissolved chitosan, 0.6 to 0.8 part of sodium polyacrylate, 0.3 to 0.6 part of air entraining agent, and 100 parts of water. The obtained slurry has the characteristics of excellent adhesive strength, thermal insulation performance and overall strength, good waterproof and fireproof effect, and improved adhesive force, is capable of effectively preventing the shrinking and cracking of cement, and has the advantages of energy efficiency, environment-friendliness, no toxicity, no pollution, high value, and low cost.

Description

Technical field [0001] The invention relates to the field of building slurry, in particular to a fireproof and thermal insulation composite slurry with strong adhesion. Background technique [0002] A large number of air conditioners are used every summer, which brings environmental problems that cannot be ignored. Building constant temperature materials can not only be mixed with water-based coatings, but also can be combined with cement, mortar, lime, gypsum, fly ash, and concrete to form a constant temperature layer for indoor and outdoor walls to achieve the purpose of indoor and outdoor wall cooling in summer and warm in winter. [0003] At present, my country implements building energy-saving projects, external wall insulation, and many projects choose polymer mortar insulation products such as rubber powder polystyrene particles, expanded perlite, etc., but in actual use, cracking, deformation, and shedding have occurred to varying degrees. , There are serious quality proble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B24/38C04B14/18C04B16/08
Inventor 孙瑞
Owner 青岛诚运建筑工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products