A kind of hollow fiber composite nanofiltration membrane and preparation method thereof

A fiber composite and nanofiltration membrane technology, which is applied in chemical instruments and methods, membrane technology, semi-permeable membrane separation, etc., can solve the problem of not being able to effectively obtain commercially applicable hollow fiber nanofiltration membranes and restrict the application and promotion of nanofiltration membrane technology , Increase user cost and other issues, achieve good industrialization advantages and commercial application prospects, improve working water flux, and stabilize product quality

Inactive Publication Date: 2016-09-28
HUNAN OVAY TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned existing hollow fiber nanofiltration membrane preparation process has not yet achieved industrialization, nor has it been able to effectively obtain commercially applicable hollow fiber nanofiltration membranes
In addition, the water flux of the nanofiltration membrane prepared by the existing technology is low, which increases the user's use cost and restricts the application and promotion of the nanofiltration membrane technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hollow fiber composite nanofiltration membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] (1) Preparation of casting liquid: The casting liquid is divided into an inner layer casting liquid and an outer layer casting liquid. The inner layer casting liquid is composed of 18wt% polyvinylidene fluoride, 2wt% Tween-80, 10wt% Polyethylene glycol 400, 5wt% lithium chloride and 65wt% N,N-dimethylacetamide; outer layer casting liquid is composed of 15wt% polyetherimide (molecular weight 50000), 5wt% magnesium chloride and 80wt% of N,N-dimethylacetamide; the casting liquid was stirred evenly at 50°C, and was subjected to static defoaming treatment.

[0038] (2) extrusion molding: the above-mentioned outer layer casting liquid and inner layer casting liquid are respectively added to the outer layer and the second outer layer of the spinneret of a core double-layer structure, the center layer is passed into the core liquid, and the core liquid is The water is extruded and then coagulated in a coagulation bath. The coagulation bath is composed of 80wt% water, 0.5wt% sod...

Embodiment 2

[0042] (1) Preparation of casting solution: The casting solution is divided into inner layer casting solution and outer layer casting solution. The inner layer casting solution is composed of 18wt% polyacrylonitrile, 2wt% sorbitan fatty acid ester, 15wt% It is composed of polyvinylpyrrolidone, 5wt% lithium nitrate and 60wt% N,N-dimethylformamide; the outer layer casting liquid is composed of 15wt% polyether ether ketone (molecular weight 100000), 3wt% magnesium sulfate and It is composed of 82wt% N,N-dimethylformamide; the casting liquid is stirred evenly at 60°C and subjected to static defoaming treatment.

[0043] (2) extrusion molding: the above-mentioned outer layer casting liquid and inner layer casting liquid are respectively added to the outer layer and the second outer layer of the spinneret of a core double-layer structure, the center layer is passed into the core liquid, and the core liquid is The water is extruded and then coagulated in a coagulation bath. The coagu...

Embodiment 3

[0047] (1) Preparation of casting liquid: The casting liquid is divided into an inner layer casting liquid and an outer layer casting liquid. The inner layer casting liquid is composed of 22wt% polyvinyl chloride, 5wt% fatty alcohol polyoxyethylene ether, 10wt% It is composed of polyethylene glycol 400, 3wt% of nano-hydrophobic calcium carbonate and 60wt% of N-methylpyrrolidone; the outer casting liquid is composed of 18wt% of sulfonated polyetheretherketone (molecular weight 120000), 4wt% of lithium nitrate and 78 wt % of N-methylpyrrolidone; the casting liquid was stirred evenly at 65° C., and was subjected to static defoaming treatment.

[0048] (2) extrusion molding: the above-mentioned outer layer casting liquid and inner layer casting liquid are respectively added to the outer layer and the second outer layer of the spinneret of a core double-layer structure, the center layer is passed into the core liquid, and the core liquid is The water is extruded and then coagulated...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a hollow fiber compound nanofiltration membrane. The nanofiltration membrane takes a porous supporting layer as an inner layer and a separating function layer as an outer layer. A casting membrane solution of the porous supporting layer contains an inner layer macromolecular polymer which is selected from one or more of polysulfone, polyether sulfone, polyvinylidene fluoride, polyvinyl chloride and polyacrylonitrile; a casting membrane solution of the separating function layer contains an outer layer macromolecular polymer which is selected from one or more of polyetherimide, polyether-ether-ketone, sulfonated polyether-ether-ketone, polymethyl methacrylate and polyvinyl alcohol; a preparation method comprises the following steps: synchronously extruding and molding the inner layer casting membrane solution and the outer layer casting membrane solution; solidifying to obtain a membrane filament in a nascent state; and carrying out an oxidizing agent aqueous solution to obtain the hollow fiber compound nanofiltration membrane. The invention further provides the preparation method of the nanofiltration membrane correspondingly. According to the hollow fiber compound nanofiltration membrane provided by the invention, the flux of the nanofiltration membrane is remarkably improved, and moreover, the nanofiltration membrane further has the certain desalinization rate.

Description

technical field [0001] The invention relates to a separation membrane with a structure of polymer material and a preparation method thereof, in particular to a hollow fiber composite nanofiltration membrane and a preparation method thereof. Background technique [0002] Nanofiltration (NF) is a pressure-driven membrane separation process between reverse osmosis (RO) and ultrafiltration (UF), and it is one of the most rapidly developing membrane separation technologies. It is generally believed that the pore size of nanofiltration membranes is 0.5 to 2 nm, and it is often used to separate monovalent salts, divalent salts, and organic compounds with a molecular weight (MWCO) between 200 and 2000. Divalent salts and high valence salts have better retention rates and allow monovalent salts to pass more freely, so that the separation of ions of different valence states can be achieved. Due to the presence of charged groups on the membrane surface or in the membrane of most nanof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D69/12B01D69/10B01D71/68B01D67/00B01D71/34B01D71/42B01D71/40
Inventor 贺攀路宏伟刘旦彭博胡群辉喻慧王进刘鹏君王纯清陈超刘畅叶明明黄涛刘元利
Owner HUNAN OVAY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com