Antibacterial and antistatic ultraviolet-curable coating and preparation method thereof

A technology of curing coatings and ultraviolet light, which is applied in the direction of conductive coatings, fireproof coatings, polyester coatings, etc., to achieve the effects of mild conditions, simple preparation methods, and small changes in surface resistance

Inactive Publication Date: 2015-04-22
HUZHOU NANXUN SHUANGLIN ZHENSEN WOOD PROCESSING FACTORY
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, coatings with both antistatic and antibacterial properties have not been reported. Therefore, in order to meet the needs of both antibacterial and antistatic properties, it is particularly necessary to develop a coating that has both functions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An antibacterial and antistatic UV-curable coating consists of base resin 87g, reactive diluent monomer 56g, photoinitiator 6g, antistatic agent 14g, flame retardant 23g, antibacterial agent 17g, leveling agent 15g, defoamer 16g, Thickener 10g and light stabilizer 6g are made.

[0028] The preparation method includes the following steps: (1) Weigh the base resin and active diluent monomer into the reaction container, mix and ultrasonically disperse for 45 minutes; (2) Weigh the photoinitiator, antistatic agent, flame retardant and antibacterial Add the agent into the reaction vessel, heat up to 110°C while stirring, and react for 2 hours; (3) Cool down to 75°C, add leveling agent, defoamer, thickener and light stabilizer according to the amount, react for 1 hour, and you get it.

Embodiment 2

[0030] An antibacterial and antistatic UV-curable coating, consisting of base resin 107g, reactive diluent monomer 68g, photoinitiator 10g, antistatic agent 24g, flame retardant 35g, antibacterial agent 23g, leveling agent 18g, defoamer 20g, Thickener 16g and light stabilizer 12g are made.

[0031] The preparation method includes the following steps: (1) Weigh the base resin and active diluent monomer into the reaction container, mix and ultrasonically disperse for 45 minutes; (2) Weigh the photoinitiator, antistatic agent, flame retardant and antibacterial Add the agent into the reaction vessel, heat up to 110°C while stirring, and react for 4 hours; (3) Cool down to 75°C, add leveling agent, defoamer, thickener and light stabilizer according to the amount, react for 3 hours, and you get it.

Embodiment 3

[0033] An antibacterial antistatic UV-curable coating, consisting of base resin 92g, reactive diluent monomer 57g, photoinitiator 8g, antistatic agent 16g, flame retardant 26g, antibacterial agent 19g, leveling agent 16g, defoamer 18g, Thickener 15g and light stabilizer 9g are made.

[0034] The preparation method includes the following steps: (1) Weigh the base resin and active diluent monomer into the reaction container, mix and ultrasonically disperse for 45 minutes; (2) Weigh the photoinitiator, antistatic agent, flame retardant and antibacterial Add the agent into the reaction vessel, heat up to 110°C while stirring, and react for 3.5 hours; (3) Cool down to 75°C, add leveling agent, defoamer, thickener and light stabilizer according to the amount, react for 2.5h, that is have to.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial and antistatic ultraviolet-curable coating and a preparation method thereof. The method comprises the following steps: (1) weighing the following raw material in parts by weight: 87-107 parts of substrate resin and 56-68 parts of an active diluting monomer, mixing and ultrasonically dispersing; (2) adding 6-10 parts of a photoinitiator, 14-24 parts of an antistatic agent, 23-35 parts of a fire retardant and 17-23 parts of an antibacterial agent, stirring and heating to 110 DEG C, and reacting for 2-4 hours; and (3) cooling to 75 DEG C, adding 15-18 parts of a flatting agent, 16-20 parts of an antifoaming agent, 10-16 parts of a thickening agent and 6-12 parts of a light stabilizer, and reacting for 1-3 hours, so as to obtain the antibacterial and antistatic ultraviolet-curable coating. The coating disclosed by the invention is short in cuing time, high in hardness, and relatively high in surface resistance, shows a good antistatic function, and also has excellent antibacterial property and flame retardant property; a barrier protection effect can be effectively provided for the coated combustible material; and the preparation method disclosed by the invention is simple, mild in condition and easy to control.

Description

technical field [0001] The invention relates to an antibacterial and antistatic ultraviolet light curing coating and a preparation method thereof, belonging to the field of light curing coatings. Background technique [0002] UV-curable coatings are environmentally friendly and energy-saving coatings that have been successfully developed in recent decades. It has many advantages that traditional coatings cannot match: energy saving, high energy utilization rate; no solvent emissions, safe and pollution-free; fast curing speed, high production efficiency; heat-sensitive substrates can be coated; Layer performance is excellent. Entering the 21st century, people's awareness of environmental protection is constantly increasing, and more and more people choose environmentally friendly products. In the future, this green environmental protection product will surely get greater development. Over the past few years, UV-curable coatings have grown rapidly in fiber optic coatings, C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D5/14C09D5/24C09D5/18C09D7/12
CPCC09D167/06C08K2201/014C08K2201/017C08L2205/035C09D5/14C09D5/18C09D5/24C09D7/63
Inventor 俞金根柴凌燕
Owner HUZHOU NANXUN SHUANGLIN ZHENSEN WOOD PROCESSING FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com