Preparation method and device for decreasing sintered NdFeB declination

A magnetic declination, NdFeB technology is applied in the field of preparation and device for reducing the magnetic declination angle of sintered NdFeB, which can solve the problems of damage to the performance of the magnet, inability to control the production, reduce the magnetic declination angle of the magnet, etc. , Improve material utilization, reduce the effect of magnetic declination

Active Publication Date: 2015-04-08
NINGBO KETIAN MAGNET +1
View PDF12 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, in order to meet the requirement that the magnetic declination angle is less than 3°, for the magnetized products, the manufacturers of magnetic materials only pick out the parts with uniform magnetic force lines and small magnetic declination angles through full inspection for processing, which increases the amount of processing waste and the utilization rate of materials. Only 30-40%, far lower than the 60% material utilization rate of ordinary products, and the production cost is greatly increased
For products that are shipped without magnetization, many companies cannot produce control to ensure that the magnetic declination angle is within 3°
CN101447273A proposes a method and device for overcoming the magnetic declination of permanent magnets. The method uses its device to machine two magnetic field orientation surfaces of sintered permanent magnets, so that the magnetic field orientation surfaces are perpendicular to the magnetic field orientation lines. This method and device Only mechanical cutting of permanent magnets will cause damage to the performance of the magnets, and there is no substantial improvement in reducing the magnetic declination of the magnets

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and device for decreasing sintered NdFeB declination
  • Preparation method and device for decreasing sintered NdFeB declination
  • Preparation method and device for decreasing sintered NdFeB declination

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The finished product specification is 20mm×4mm×9mm↓ (orientation direction), the production process of the brand N40 product.

[0022] Ingredients: according to the following composition ratio weight ingredients, praseodymium neodymium alloy 30.2% by weight, gadolinium 2.0% by weight, boron 1.03% by weight, aluminum 0.64% by weight, zirconium 0.3% by weight, copper 0.02% by weight, and the balance is iron and other impurities, Wherein in the praseodymium neodymium alloy, praseodymium accounts for 25% by weight, neodymium accounts for 75% by weight, boron is added in the state of BFe alloy, the boron content is 19%, and the iron content is 81%; Gadolinium is added in the state of GdFe alloy, and the content of gadolinium is 75%. The iron content is 25%.

[0023] Melting: Put the prepared raw materials into a vacuum induction furnace, vacuum the induction furnace to 4.5-5Pa, heat and melt until the raw materials in the furnace turn red, close the vacuum valve, fill in arg...

Embodiment 2

[0042] The finished product specification is Φ100mm×3mm↓ (orientation direction), the production process of the brand N38 product.

[0043] Ingredients: According to the following composition ratio weight ingredients, praseodymium neodymium alloy 31% by weight, gadolinium 2.5% by weight, boron 1.02% by weight, aluminum 0.64% by weight, zirconium 0.1% by weight, copper 0.02% by weight, and the balance is iron and other impurities, Wherein in the praseodymium neodymium alloy, praseodymium accounts for 25% by weight, neodymium accounts for 75% by weight, boron is added in the state of BFe alloy, the boron content is 19%, and the iron content is 81%; Gadolinium is added in the state of GdFe alloy, and the content of gadolinium is 75%. The iron content is 25%.

[0044] Melting: Put the prepared raw materials into the vacuum induction furnace, vacuum the induction furnace to 4.0-4.5Pa, heat and melt until the raw materials in the furnace turn red, close the vacuum valve, fill with a...

Embodiment 3

[0063] The finished product specification is Φ21mm×3mm↓ (orientation direction), the production process of the brand N45 product.

[0064]Ingredients: Ingredients are prepared according to the weight ratio of the following ingredients: 28% neodymium, 1.02% boron, 1.0% dysprosium, 1.5% holmium, 0.2% aluminum, 1.5% gadolinium, 0.4% niobium, 0.2% copper, 0.2% cobalt, 0.1% gallium , iron and other impurities are 65.88%, of which boron is added in the state of BFe alloy, the content of boron is 19%, and the content of iron is 81%; holmium is added in the state of alloy with HoFe purity of 99.50%, the content of holmium is 80%, and the content of iron is 20% Gadolinium is added in the state of GdFe alloy, the content of gadolinium is 75%, and the content of iron is 25%; niobium is added in the state of NbFe alloy, of which the content of niobium is 65% and the content of iron is 35%.

[0065] Melting: Put the prepared raw materials into the vacuum induction furnace, vacuum the induc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Cross-sectional areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for decreasing sintered NdFeB declination. The preparation method includes preparing materials, performing smelting, processing powder, performing forming and performing sintering; to be specific, adding addition agent during powder processing to improve powder liquidity; increasing magnetic field intensity H during forming; reducing mold orientation length L; enlarging section area A in the vertical magnetic line direction; feeding mixture powder in a forming mold of a press; adjusting a center, on a coil pole, of the forming mold on a mold frame to allow the presses powder to stay in the center of the coil magnetic field during forming orientation pressing; by adjusting four relative parameters, the declination of the sintered NdFeB is decreased to 3 degrees from 10 degrees, use ratio of material with declination qualified is increased to 60% or above from 35%, production cost is remarkably decreased, and economic benefit is enhanced.

Description

technical field [0001] The invention relates to a permanent magnet manufacturing method and a device thereof, in particular to a manufacturing method and a device for reducing the magnetic declination of sintered NdFeB. Background technique [0002] Sintered NdFeB permanent magnet materials have been widely used in the field of motor manufacturing due to their excellent magnetic properties. Theoretically, the magnetic pole axis on the physical shape of the NdFeB permanent magnet should coincide with the magnetic pole direction after the magnet is magnetized, but due to the influence of various factors during the magnet preparation process, especially the molding process and processing technology, the actual physical shape of the magnet There is an angle between the magnetic pole axis on the magnet and the magnetic pole direction after the magnet is magnetized, and this angle is the magnetic declination angle φ. Due to the existence of magnetic declination, the non-magnetize...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F3/16H01F1/057
Inventor 王育平邓晓飞周子翔郑敦敦
Owner NINGBO KETIAN MAGNET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap