Novel adhesive for plywood

A plywood and adhesive technology, applied in the direction of adhesives, starch adhesives, adhesive additives, etc., can solve the problems of low bonding strength, easy to mildew when exposed to moisture, etc., achieve excellent environmental performance, low volatile organic compounds, and simple preparation process Effect

Inactive Publication Date: 2015-01-28
王璐
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, starch adhesives have disadvantages such as low bonding strength and easy mildew when exposed to moisture, which limits the application in the bonding of wood products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The invention is a novel plywood adhesive, which is made of the following raw materials in parts by weight:

[0011] 2.5 parts of talcum powder, 4.5 parts of high molecular weight thermoplastic resin, 1.5 parts of pentaerythritol, 2.5 parts of starch, 2.3 parts of polyether polyol, 0.3 part of propyl starch ether, 2 parts of hydroxyl-terminated polyester cyclic polyol and 0.5 parts of modified tree ash share.

Embodiment 2

[0013] The invention is a novel plywood adhesive, which is made of the following raw materials in parts by weight:

[0014] 4 parts of talcum powder, 8 parts of high molecular weight thermoplastic resin, 2.7 parts of pentaerythritol, 6 parts of starch, 4.2 parts of polyether polyol, 1.2 parts of propyl starch ether, 3.5 parts of hydroxyl-terminated polyester cyclic polyol and 0.9 parts of modified tree ash share.

Embodiment 3

[0016] The invention is a novel plywood adhesive, which is made of the following raw materials in parts by weight:

[0017] 3.2 parts of talcum powder, 5.2 parts of high molecular weight thermoplastic resin, 2.4 parts of pentaerythritol, 5.2 parts of starch, 3.3 parts of polyether polyol, 0.7 part of propyl starch ether, 2.4 parts of hydroxyl-terminated polyester cyclic polyol and 0.6 part of modified tree ash share.

[0018] Compared with the existing adhesives, the present invention can be implemented on conventional adhesive production equipment without additional investment in processing equipment; the preparation process of the present invention is simple, the reaction conditions are mild, and the process stability is high; the main raw materials used are cheap Moreover, renewable starch does not release toxic and harmful gases, and has good environmental coordination; compared with ordinary white latex, this adhesive has lower total volatile organic compounds and better ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel adhesive for plywood. The novel adhesive for the plywood is prepared from the following raw materials in parts by weight: 2.5-4 parts of talcum powder, 4.5-8 parts of high molecular weight thermoplastic resin, 1.5-2.7 parts of pentaerythritol, 2.5-6 parts of starch, 2.3-4.2 parts of polyether polyol, 0.3-1.2 parts of propyl starch ether, 2-3.5 parts of hydroxyl-terminated polyester crico-polyol and 0.5-0.9 part of modified tree ash. Compared with an existing adhesive, the novel adhesive for the plywood has the advantages that the novel adhesive for the plywood can be produced by adopting the conventional adhesive production equipment without investing additional processing equipment; a method and a preparation technology are simple, reaction conditions are mild, and process stability is high; cheap and reproducible starch is adopted as a main raw material, and no hazardous gas is released, so that the novel adhesive for the plywood has good environmental friendliness; and the novel adhesive for the plywood is lower in total volatile organic compound content and better in environmental performance compared with common white latex.

Description

technical field [0001] The invention relates to a novel plywood adhesive, which belongs to the field of building materials. Background technique [0002] As a kind of natural adhesive, starch adhesive has the advantages of light weight, no corrosion, no pollution, easy to obtain raw materials, low price, and convenient use. It is widely used for bonding paper, cotton fabrics, trademarks, etc. However, starch adhesives have disadvantages such as low bonding strength and easy mildew when exposed to moisture, which limits the application in the bonding of wood products. Contents of the invention [0003] In view of the deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a new type of plywood adhesive, which has high bonding strength, is not prone to mildew when exposed to moisture, is relatively low in cost, and is environmentally friendly. [0004] In order to solve the above-mentioned technical problems, the technical so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J201/00C09J11/04C09J11/06
Inventor 王璐
Owner 王璐
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com