Anti-static optical adhesive

A technology of antistatic agent and optical glue, which is applied in the direction of adhesives, conductive adhesives, adhesive types, etc., can solve the problems that optical glue adhesives do not have antistatic properties, and cannot eliminate the hazards of electrostatic radiation, etc., and achieve high triggering Efficiency and curing speed, low curing shrinkage, fast curing effect

Inactive Publication Date: 2015-01-21
TIANNUO PHOTOELECTRIC MATERIAL
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the reported patents and documents of optical adhesives, none of the described optical adhesives has antistatic function and cannot eliminate the harm caused by static radiation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Example 1 Preparation of Antistatic Optical Adhesive

[0027] The formula is (each component is calculated by mass percentage): N-(3-dodecyloxy-2-hydroxypropyl)ethanolamine 4%, polyurethane acrylate 40%, pentaerythritol triacrylate 40%, polymethyl Methyl acrylate 6%, photoinitiator 1%, diethylenetriamine 4%, ethylenediaminepropylmethyldimethoxysilane 5%.

[0028] The 1% photoinitiator is composed of 0.2% α-hydroxyalkyl phenone, 0.2% isopropylthioxanthone, 0.4% diphenyliodonium hexafluorophosphate and 0.2% difluorinated Composed of phenyl titanocenes.

[0029] Proceed as follows:

[0030] (1) Add 40% polyurethane acrylate, 20% pentaerythritol triacrylate, and 6% polymethyl methacrylate to the reaction kettle, stir at a speed of 120r / min and heat in a water bath. to a steady state of reflux.

[0031] (2) The photoinitiator (0.2% of α-hydroxyalkyl phenone, 0.2% of isopropylthioxanthone, 0.4% of diphenyliodonium hexafluorophosphate, which accounts for 1% of the total ma...

Embodiment 2

[0033] Example 2 Preparation of Antistatic Optical Adhesive

[0034] The formula is (each component is calculated by mass percentage): 4% glyceryl monopalmitate, 32% polyurethane acrylate, 50% methyl methacrylate, 5% polyvinyl acetate, 2% photoinitiator, polyamide Polyamine Epichlorohydrin 3%, Vinyl Triethoxysilane 4%.

[0035] The 2% photoinitiator is composed of 0.3% α-hydroxyalkyl phenone, 0.3% isopropyl thioxanthone, 0.6% diphenyliodonium hexafluorophosphate and 0.8% difluorinated difluoride Composed of phenyl titanocenes.

[0036] Proceed as follows:

[0037] (1) Add 35% polyurethane acrylate, 25% methyl methacrylate and 5% polyvinyl acetate into the reaction kettle, stir at a speed of 100r / min and heat in a water bath until Reflow steady state.

[0038] (2) The photoinitiator (0.3% of α-hydroxyalkyl phenone, 0.3% of isopropylthioxanthone, 0.6% of diphenyliodonium hexafluorophosphate, which accounts for 2% of the total mass percentage) and 0.8% fluorinated diphenyl t...

Embodiment 3

[0040] Example 3 Preparation of Antistatic Optical Adhesive

[0041] The formula is (each component is calculated by mass percentage): N-(3-dodecyloxy-2-hydroxypropyl)ethanolamine 3%, polyurethane acrylate 30%, dipentaerythritol pentaacrylate 50%, polyphenylene Ethylene 8%, photoinitiator 1.5%, epoxy resin 3.5%, ethylenediaminepropylmethyldimethoxysilane 4%.

[0042] The 1.5% photoinitiator is composed of 0.3% α-hydroxyalkyl phenone, 0.3% isopropyl thioxanthone, 0.6% diphenyliodonium hexafluorophosphate and 0.3% difluorinated difluoride Composed of phenyl titanocenes.

[0043] Proceed as follows:

[0044] (1) Add 30% polyurethane acrylate, 25% dipentaerythritol pentaacrylate and 8% polystyrene to the reaction kettle, stir at a speed of 150r / min and heat in a water bath until reflux stable state.

[0045] (2) The photoinitiator (0.3% of α-hydroxyalkyl phenone, 0.3% of isopropylthioxanthone, 0.6% of diphenyliodonium hexafluorophosphate, which accounts for 1.5% of the total m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
curing timeaaaaaaaaaa
curing timeaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-static optical adhesive which is prepared from the following raw materials in percentage by weight: 1-5% of an antistatic agent, 30-60% of polyurethane acrylate, 20-50% of an acrylate monomer, 5-10% of unsaturated polyester, 0-2% of a photoinitiator (excluding 0%), 3-6% of a crosslinking agent and 1-5% of a coupling agent. The preparation method comprises the following steps: (1) adding polyurethane acrylate, part of the acrylate monomer and unsaturated polyester into a reaction kettle, stirring and heating in a water bath to a stable backflow state; (2) uniformly mixing residual raw materials, putting into the reaction kettle and stirring for polymerization reaction; and (3) finishing the polymerization reaction to obtain the anti-static optical adhesive. The anti-static optical adhesive disclosed by the invention is a colorless transparent viscous liquid matter, has the characteristics of being anti-static, high in light transmittance, high in curing speed, low in cure shrinkage rate and low in haze and the like and can be widely applied to fitting an optical protective thin film base material and a release film.

Description

technical field [0001] The invention relates to an antistatic optical adhesive, which belongs to the technical field of chemical industry. Background technique [0002] In recent years, with the rapid development of the modern electronics industry, LCD TVs, tablet computers and smart phones have been widely used, which has brought more and more electrostatic radiation hazards. Therefore, antistatic protective films with certain optical properties have attracted more and more attention. Antistatic optical adhesive is a special adhesive used for bonding transparent optical components. It is an essential key material in the production process of antistatic protective film. It is mainly used for laminating optical protective film base material and release film. The main features of this anti-static optical adhesive are: anti-static, high light transmittance, fast curing speed, low curing shrinkage, low haze, etc. [0003] At present, there are few reports on optical adhesives ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/00C09J151/08C09J11/06C09J9/02C08F291/00
Inventor 朱焰焰徐刚郑杰马苹苹张茂功郭涵
Owner TIANNUO PHOTOELECTRIC MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com