Biaxially oriented polyethylene terephthalate film and method for producing same
A polyethylene terephthalate film, polyethylene terephthalate technology, applied in the field of biaxially oriented polyethylene terephthalate film, can solve thermal dimensional stability, curling To avoid problems such as deterioration of properties, to achieve the effects of excellent thermal dimensional stability, small curl, and excellent processing adaptability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0126] Embodiments of the present invention will be described based on examples.
reference example 1
[0128] 194 parts by mass of dimethyl terephthalate and 124 parts by mass of ethylene glycol were put into a transesterification apparatus, and the contents were heated to a temperature of 140° C. to dissolve them. Thereafter, while stirring the contents, 0.1 parts by mass of magnesium acetate tetrahydrate and 0.03 parts by mass of antimony trioxide were added, and methanol was distilled off at a temperature of 140 to 230° C. to carry out a transesterification reaction. Next, 1 mass part (0.05 mass part as trimethyl phosphate) of the 5 mass % ethylene glycol solution of trimethyl phosphate was added. When an ethylene glycol solution of trimethyl phosphate is added, the temperature of the reaction content decreases. Then, stirring was continued until the temperature of the reaction content returned to a temperature of 230° C. while distilling off excess ethylene glycol. In this way, after the temperature of the reaction content in the transesterification reaction apparatus reac...
reference example 2
[0130] Using a rotary vacuum polymerization device, the PET particles X obtained in the above-mentioned Reference Example 1 were 0.65 Solid state polymerization was carried out at a temperature of 230°C for 15 hours under a reduced pressure of 0.1 kPa to obtain PET particles with an intrinsic viscosity of 0.77 X 0.77 .
PUM
Property | Measurement | Unit |
---|---|---|
hazing | aaaaa | aaaaa |
heat shrinkage ratio | aaaaa | aaaaa |
heat shrinkage ratio | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap