A kind of preparation method of graphene oxide composite material containing lactobionic acid modification

A composite material and graphene technology, applied in the field of preparation of graphene oxide composite materials, can solve problems such as increasing cytotoxicity, achieve the effects of mild experimental conditions, overcoming easy agglomeration, and simple operation

Inactive Publication Date: 2016-08-17
DONGHUA UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, too many surface amino groups also increase its cytotoxicity, thus limiting the application of PEI.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of graphene oxide composite material containing lactobionic acid modification
  • A kind of preparation method of graphene oxide composite material containing lactobionic acid modification
  • A kind of preparation method of graphene oxide composite material containing lactobionic acid modification

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Dissolve GO (344.9mg) in 40mL DMSO, then add EDC (354.32mg) to activate and stir for 3h. While stirring, 10 mL of DMSO solution containing PEI (540.01 mg) was added dropwise, and the reaction was stirred ultrasonically at room temperature for 24 h. Finally, the reaction solution was put into a dialysis bag (MW=100,000), and the unreacted impurities and by-products were removed by dialysis. First, it was dialyzed twice with PBS buffer, 2 L each time, and then dialyzed seven times with distilled water. Finally, the product was freeze-dried to obtain GO-PEI.

[0034] (2) Weigh 100 mg LA, add 35 mg EDC and 21 mg NHS to phosphate buffer to activate for three hours, add 400 mg NH2-mPEG-COOH, stir for 24 hours, and finally put the reaction solution into a dialysis bag (MW=1,000), and use dialysis to remove the unreacted To remove impurities and by-products, dialyze twice with PBS buffer, 2L each time, and then dialyze seven times with distilled water. Finally the product...

Embodiment 2

[0038] (1) Dissolve GO (300mg) in 30mL DMSO, then add EDC (304mg) to activate and stir for 3h. Under the condition of stirring, 10 mL of DMSO solution containing PEI (452.3 mg) was added dropwise, and the reaction was stirred ultrasonically at room temperature for 24 h. Finally, the reaction solution was put into a dialysis bag (MW=100,000), and the unreacted impurities and by-products were removed by dialysis. First, it was dialyzed twice with PBS buffer, 2 L each time, and then dialyzed seven times with distilled water. Finally, the product was freeze-dried to obtain GO-PEI.

[0039] (2) Weigh 23 mg LA, add 8.01 mg EDC and 4.8 mg NHS to phosphate buffer to activate for three hours, add 100 mg NH2-mPEG-COOH, stir for 24 hours, and finally put the reaction solution into a dialysis bag (MW=1,000), and use dialysis to dissolve To remove unreacted impurities and by-products, dialyze twice with PBS buffer, 2 L each time, and then dialyze seven times with distilled water. Finally...

Embodiment 3

[0043] (1) Dissolve GO (50mg) in 10mL DMSO, then add EDC (33mg) to activate and stir for 3h. With stirring, 10 mL of DMSO solution containing PEI (75 mg) was added dropwise, and the reaction was stirred ultrasonically at room temperature for 24 h. Finally, the reaction solution was put into a dialysis bag (MW=100,000), and the unreacted impurities and by-products were removed by dialysis. First, it was dialyzed twice with PBS buffer, 2 L each time, and then dialyzed seven times with distilled water. Finally, the product was freeze-dried to obtain GO-PEI.

[0044] (2) Weigh 44 mg LA, add 21 mg EDC and 11 mg NHS to phosphate buffer to activate for three hours, add 180 mg NH2-mPEG-COOH, stir for 24 hours, and finally put the reaction solution into a dialysis bag (MW=1,000), and use dialysis to remove the unreacted To remove impurities and by-products, dialyze twice with PBS buffer, 2L each time, and then dialyze seven times with distilled water. Finally the product is freeze-dr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a graphene oxide composite material modified with lactobionic acid, comprising: producing chemical bonds between graphene oxide and PEI through the action of an activator EDC in dimethyl sulfoxide, dialysis and freeze-drying, and synthesizing GO ‑PEI; Dissolve LA in phosphate buffer, add EDC, activate with NHS, add NH 2 ‑mPEG‑COOH, at room temperature, react for 12‑24 hours, dialyze, freeze-dry to obtain PEG‑LA; dissolve the above GO‑PEI in water, add FITC solution; add the above PEG‑LA to EDC and NHS for activation, add GO‑LA PEI solution, react to get GO‑PEI‑FI‑PEG‑LA, add triethylamine to mix, add acetic anhydride, react at room temperature, dialyze, freeze-dry to obtain. The preparation process of the invention is simple, the experimental conditions are normal temperature and pressure, and the operation is easy.

Description

technical field [0001] The invention belongs to the field of preparation of graphene oxide composite materials, in particular to a method for preparing graphene oxide composite materials modified with lactobionic acid. Background technique [0002] As a new type of two-dimensional nanomaterial, graphene has become a research hotspot due to its unique and excellent electrical, optical, and mechanical properties, as well as its wide application prospects. [0003] Graphene derivatives that are widely used in the biomedical field are mainly functionalized graphene oxide (or graphene oxide). Graphene oxide is usually prepared from graphite through chemical oxidation and ultrasound. Due to the different oxidation conditions, the size of the obtained graphene oxide is generally between nanometers to hundreds of nanometers or even micrometers. Graphene oxide contains a large number of oxygen-containing groups. In recent years, the application prospects of graphene derivatives in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B31/04
Inventor 朱利民陶磊杨卉卉公晓曹欣乐
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com