Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Rust-proof paste for treating surface corrosion of metal material

A metal material and anti-rust paste technology, which is applied in the field of anti-rust paste to deal with the surface corrosion of metal materials, can solve the problems of high labor intensity, complicated process operation, and endangering the health of operators, so as to achieve simple and easy operation and shorten process steps , the effect of improving the working environment

Inactive Publication Date: 2014-10-15
梁胜光
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And most of them adopt a single treatment method, that is, degreasing, derusting, phosphating, and passivation treatment are carried out separately and in sequence, and are carried out step by step in several tanks (that is, setting up degreasing, derusting pools, passivation pools, clear water tank), etc., so it occupies a large area, consumes a lot of water, causes serious pollution, complex process operation, high labor intensity, and endangers the health of operators.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A kind of antirust paste for treating metal material surface corrosion described in the present embodiment 1 is made up of the following raw material components: 10 parts of sodium hydroxide, 20 parts of soda ash, 50 parts of nitric acid, 5 parts of charcoal powder, 10 parts of Corn cob powder, 12 parts of bauxite powder, 5 parts of fireproof clay, 12 parts of ethylenediamine, 3 parts of chrome black t, 5 parts of thiourea, 2 parts of formaldehyde, 50 parts of deionized water.

Embodiment 2

[0011] A kind of antirust paste for treating metal material surface corrosion described in the present embodiment 2 is made up of the raw material components of the following parts: 15 parts of sodium hydroxide, 25 parts of soda ash, 80 parts of nitric acid, 10 parts of charcoal powder, 12 parts Corn cob powder, 15 parts of bauxite powder, 10 parts of fireproof clay, 15 parts of ethylenediamine, 5 parts of chrome black t, 8 parts of thiourea, 5 parts of formaldehyde, 80 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses rust-proof paste for treating surface corrosion of a metal material. The rust-proof paste consists of the following raw materials in parts: 10-15 parts of sodium hydroxide, 20-25 parts of sodium carbonate, 50-80 parts of nitric acid, 5-10 parts of charcoal powder, 10-12 parts of corncob powder, 12-15 parts of bauxite powder, 5-10 parts of fireproofing mud glue, 12-15 parts of ethylenediamine, 3-5 parts of eriochrome black t, 5-8 parts of thiourea, 2-5 parts of formaldehyde, and 50-80 parts of de-ionized water. The rust-proof paste for treating the surface corrosion of the metal material is paste at the normal temperature, and can be utilized to coat a metal rust place, then the paste is scraped off after several minutes, and the rust-proof purpose can be achieved after the water cleaning. The rust-proof paste is low in production cost, can help to improve the working environment and shorten the process steps, and is easy to operate and master.

Description

technical field [0001] The invention relates to the technical field of rust removing paste, in particular to an antirust paste for treating surface corrosion of metal materials. Background technique [0002] At present, before the ferrous metal is coated, the surface should be pretreated to remove the oil stains, impurities and rust layers on the surface, and the general treatment method is to use a liquid rust remover. And most of them adopt a single treatment method, that is, degreasing, derusting, phosphating, and passivation treatment are carried out separately and in sequence, and are carried out step by step in several tanks (that is, setting up degreasing, derusting pools, passivation pools, Clean water tank), etc., so it occupies a large area, consumes a lot of water, causes serious pollution, complex process operation, high labor intensity, and endangers the health of operators. Contents of the invention [0003] The purpose of the present invention is in order ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/00
Inventor 梁胜光
Owner 梁胜光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products