High-barrier HDPE (high-density polyethylene) membrane production process

A production process and high-barrier technology, applied in the field of film manufacturing, can solve the problems of affecting appearance, catalyst poisoning, film yellowing, etc., and achieve the effect of preventing film yellowing, good barrier properties, and avoiding yellowing

Active Publication Date: 2014-08-27
UPASS MATERIAL TECH JIANGSU
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing HDPE black and white two-color and other colored membranes, in the production and use of waterproof membranes, the yellow waste engine oil in the asphalt penetrates into the surface of the HDPE membrane, making the membrane yellow and affecting the appearance. At the same time, there is nitrogen in production. Catalyst poisoning caused by silicone oil process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-barrier HDPE (high-density polyethylene) membrane production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The following will clearly and completely describe the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only some of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0017] see figure 1 , the embodiment of the present invention includes:

[0018] A high-barrier HDPE film production process, including: 1) Primer formulation, including: mixing solvent-based acrylic adhesive: ethyl acetate at a volume ratio of 1:5 and then mixing PVDC emulsion: water with 1:1 volume ratio mixing, 2) Unwind the film raw material with constant tension, 3) Corona treat the unwinded film, 4) Put the corona treated film through the metal chrome-plated anilox roller for bottoming 5) Dry the film after p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-barrier HDPE (high-density polyethylene) membrane production process which comprises the steps: blending of a bottom coating solution, unreeling, corona treatment, bottom coating, drying, surface coating, surface coating drying, and reeling. By adopting the manner, the high-barrier HDPE membrane production process disclosed by the invention has the advantages of good barrier property, simple production process, high chemical stability, long service life, good temperature resistance, and high membrane strength; a release member is effectively prevented from yellowing, and the problem of catalyst poisoning during production is solved.

Description

technical field [0001] The invention relates to the field of film manufacturing, in particular to a high barrier HDPE film production process. Background technique [0002] High-density polyethylene is a highly crystalline, non-polar thermoplastic resin. PE has excellent resistance to most domestic and industrial chemicals. The polymer is non-hygroscopic and has good water vapor resistance for packaging purposes. HDPE has good electrical properties, especially the high dielectric strength of the insulation, making it very suitable for wires and cables. The existing HDPE black and white two-color and other colored membranes, in the production and use of waterproof membranes, the yellow waste engine oil in the asphalt penetrates into the surface of the HDPE membrane, making the membrane yellow and affecting the appearance. At the same time, there is nitrogen in production. Catalyst poisoning caused by silicone oil process. Contents of the invention [0003] The technical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08J7/04C08J7/00C08L23/06C09D127/16
CPCY02P20/52
Inventor 易向阳
Owner UPASS MATERIAL TECH JIANGSU
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com