Ultrathin leisure fabric with windproof and breathable functions and manufacturing method thereof

A windproof, breathable, ultra-thin technology applied to the field of fabrics to achieve light weight effects

Inactive Publication Date: 2014-07-23
HUZHOU SENNUO FLUORINE MATERIAL TECH
View PDF19 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the improvement of people's living standards, people's requirements for quality of life are getting higher and higher. For example, people's requirements for sports and leisure clothing are not only comfortable to wear, light in weight, but also breathable, windproof, waterproof, UV-resistant, Moisture permeability and other functions, but the products on the existing market cannot achieve the above functions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Embodiment 1, a kind of windproof breathable polytetrafluoroethylene film and preparation method thereof for ultra-thin casual fabrics, its steps are as follows:

[0023] (1) Mixing: Fully mix Sichuan Chenguang 216G PTFE dispersion resin powder (standard specific gravity is 2.165) and ExxonMobil’s ISOPARK hydrocarbon extrusion aid in proportion, and let it stand at 55°C After 24 hours, a mass was formed.

[0024] (2) Billet making: pre-press the material into a cylindrical billet of Φ120mm at 45°C.

[0025] (3) Pushing: Place the cylindrical billet on the pushing machine, and push it into a round bar of Φ18 under the condition of 55℃~60℃.

[0026] (4) Calendering: place the round bar on a calender, and calender it at 50°C to form an oil-containing base belt with a thickness of 140um.

[0027] (5) Degreasing treatment: Degrease the oil-containing base tape at 270°C, remove the extrusion aid, and obtain a degreased base tape.

[0028] (6) Longitudinal stretching: The d...

Embodiment 2

[0033] Embodiment 2, a kind of windproof breathable polytetrafluoroethylene film and preparation method thereof for ultra-thin casual fabrics, its steps are as follows:

[0034] (1) Mixing: Fully mix Sichuan Chenguang 216G PTFE dispersion resin powder (standard specific gravity 2.165) and ExxonMobil’s ISOPARK hydrocarbon extrusion aid in proportion, and let stand at 70°C After 24 hours, a mass was formed.

[0035] (2) Billet making: pre-press the material into a cylindrical billet of Φ120mm at 55°C.

[0036] (3) Pushing: Place the cylindrical billet on a pushing machine, and push it into a Φ25mm round bar at 60°C.

[0037] (4) Calendering: Place the round bar on a calender, and calender it at 50°C to form an oil-containing base belt with a thickness of 180um.

[0038] (5) Degreasing treatment: Degrease the oil-containing base tape at 280°C, remove the extrusion aid, and obtain a degreased base tape.

[0039] (6) Longitudinal stretching: The degreased base tape is stretched ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Apertureaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultrathin leisure fabric with windproof and breathable functions and a manufacturing method of the ultrathin leisure fabric with the windproof and breathable functions. The method includes the steps that material is mixed; a blank is manufactured; pushing and pressing are performed; calendaring is performed; ungreasing treatment is performed; longitudinal stretching is performed; bi-directional stretching is performed in an arc shape; after transverse stretching, agglomeration and solidification are performed; films are attached through a release paper transferring method; the ultrathin leisure fabric is formed through glue compositing on textile fabric. The ultrathin leisure fabric manufactured through the steps is used for the fields of down garments, leisure sportswear, shoemaking and others, the thickness of the teflon microporous film is 2 micrometers-5 micrometers, the pore diameter is 0.5 micrometer-2 micrometers, and the porosity is over 80%. The ultrathin leisure fabric has the multiple functions of being light in weight, windproof, waterproof, breathable and resistant to ultraviolet and corrosion, discharging sweat and keeping warm and is suitable for various products, which are made of functional materials, for kinds of sports, leisure and women and children.

Description

Technical field: [0001] The invention relates to the field of fabrics, in particular to an ultra-thin casual fabric with windproof and breathable functions and a preparation method thereof. Background technique: [0002] Expanded PTFE microporous membrane is a porous material formed by multi-directional stretching (i.e. expansion treatment), calendering, heat treatment and other processes. It is a flexible and elastic microporous material with high porosity and pore size distribution. Uniform membrane with sterilization and filtration functions. The surface of the material is smooth and soft. However, under the scanning electron microscope, it can be seen that there are a large number of micropores of 0.4 μm to 1 μm inside the material, and its porosity can account for more than 80%. This material has the following characteristics: non-hazardous, light in weight, corrosion-resistant, resistant to environmental changes, overcomes the cold flow (creep) of pure PTFE sealing mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A41D31/02B32B27/12B32B27/08B32B37/02B32B37/26
Inventor 王中华
Owner HUZHOU SENNUO FLUORINE MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com