High-molecular hot-melt adhesive for preventing air leakage of automobile tyre, and manufacturing method of high-molecular hot-melt adhesive

A manufacturing method and polymer technology, applied in coatings, rosin coatings, etc., to achieve superior elasticity and ductility, improve driving safety, and prevent leakage.

Inactive Publication Date: 2014-05-21
LUOYANG JUNTENG ENERGY TECH
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve the above-mentioned problems, relevant manufacturers, research institutes and institutes have worked hard to find a solution, but no suitable polymer hot melt adhesive has been found for a long time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Proportion and components of polymer hot melt adhesive (based on weight %) 48% thermoplastic elastomer, 43% tackifier, 8% plasticizer, 1% anti-aging agent and antioxidant, 1% crosslinking agent , Filler 3%; Weigh thermoplastic elastomer SEBSS 660g, thermoplastic elastomer SBS 300g; Tackifier: Coumarone resin 600g, Pentaerythritol ester 260g; Plasticizer: Aromatic hydrocarbon oil 120g, Dioctyl phthalate 40g ;Antioxidant 300 10g, anti-aging agent RD 10g; crosslinking agent: zinc oxide 20g; filler: quartz powder 60g.

[0044] The preparation method is as follows: using material crushing equipment to crush the solid material into particles of <150 mesh; using a continuous mixing device planetary mixer to uniformly mix the crushed solid material and liquid material, and then measure and bag the mixture after uniform mixing.

Embodiment 2

[0046] Proportion and components of polymer hot melt adhesive (based on weight %) 50% thermoplastic elastomer, 42% tackifier, 7% plasticizer, 1% antioxidant, 1% crosslinking agent, filler 5 %; Weigh thermoplastic elastomer SEPS 800g, thermoplastic elastomer SBS 100g, thermoplastic elastomer SEBS 100g; tackifier: coumarone resin rosin 500g, coumarone resin 340g; plasticizer: aromatic oil 100g, phthalate Diisooctyl formate 40g; antioxidant 2246 10g, antioxidant 300 10g; crosslinking agent: phenolic resin 20g; filler: quartz powder 50g, carbon black 50g.

[0047] The preparation method is as follows: using material crushing equipment to crush the solid material into particles of <150 mesh; using a continuous mixing device propeller agitator to uniformly mix the crushed solid material and liquid material, and measure and pack the powder after mixing evenly.

Embodiment 3

[0049] Proportion and components of polymer hot melt adhesive (based on weight %) 49% thermoplastic elastomer, 45% tackifier, 5% plasticizer, 1% anti-aging agent and antioxidant, 0.5% crosslinking agent , Filler 4%; Weigh thermoplastic elastomer SBS 580g, thermoplastic elastomer SEBS 400g; Tackifier: Coumarone resin 900g; Plasticizer: aromatic hydrocarbon oil 50g, diisooctyl phthalate 50g; Antiaging agent RD 10g, antioxidant 300 10g; crosslinking agent: zinc oxide 10g; filler: quartz powder 50g, carbon black 30g.

[0050] The preparation method is as follows: using material crushing equipment to crush the solid material into particles of <150 mesh; using a continuous mixing equipment high-shear disperser to uniformly mix the crushed solid material and liquid material, and measure and pack the powder after mixing evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-molecular hot-melt adhesive for security upgrade of an automobile tyre. The high-molecular hot-melt adhesive comprises the following components in percentage by weight: 40%-60% of thermoplastic elastomers, 34%-51% of thickening agents, 5%-8% of plasticizing agents, 0.5%-1.5% of anti-aging agents, 0.2%-1% of cross-linking agents and 3%-5% of filling agents. By using a glue sprayer of the automobile tyre, the high-molecular hot-melt adhesive is sprayed to the inner wall of a tyre after being hot-melted, the inner wall of the tyre is only subjected to mould release agent removal washing and drying treatment without being subjected to any damaging processing; the tyre can be upgraded to normally operate between low temperature of -40 DEG C and high temperature of +120 DEG C by spraying a layer of the high-molecular hot-melt adhesive with the thickness more than 3.5 mm on the integral part or crown type body part of the inner wall of the tyre, and the tyre has bullet-proof, leakage-proof and anti-puncturing properties. The invention also discloses a manufacturing method of the high-molecular hot-melt adhesive.

Description

technical field [0001] The invention relates to a polymer hot-melt adhesive capable of preventing air leakage of automobile tires and a manufacturing method thereof. Background technique [0002] At present, there are two types of car wheels used in vehicles, one with inner tubes and the other without tubes. At present, almost all of the passenger vehicles use tubeless wheels. The country requires gradual promotion of heavy-duty vehicles. Use tubeless car wheels. Because the tubeless car wheel has the advantages of good heat dissipation, softness, sealing, comfortable ride, good performance and long interval between inflation and use, but when the tire of the tubeless car wheel is punctured by a sharp object, due to the sharp object remaining on the car In the tire body, the high-pressure gas of the car tire will leak out or blow out at the punctured part; when the sharp object pierces the car tire and breaks away from the car tire, the high-pressure gas in the tubeless car...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D153/02C09D193/04C09D145/02C09D7/12C09D5/00
Inventor 周仁福王自新刘宽亮史惠娟周强
Owner LUOYANG JUNTENG ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap