High-performance water-based fluorocarbon paint

A technology of water-based fluorocarbon and water-based fluorocarbon emulsion, applied in the direction of coating, etc., can solve the problems of poor water resistance, alkali resistance, aging resistance, poor mildew and moisture resistance, and weak solvent resistance, etc., to improve anti-fouling Ability, strong solvent resistance, good effect of anti-fouling ability

Active Publication Date: 2014-05-14
广东黑马新材料科技有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, many fluorocarbon wall paints have poor anti-fouling, poor solvent resistance, poor water and alkali resistance, poor aging resistance, poor mildew and moisture resistance, high surface tension of the paint film, and volatile gases, which are not safe and environmentally friendly. Solve or not completely solve these problems, especially the problem that the stains are difficult to remove after the wall is pasted indiscriminately and graffiti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high-performance water-based fluorocarbon paint, calculated by 100% by mass, includes:

[0027] Water-based fluorocarbon emulsion 50%;

[0028] Silicone crosslinker 0.4%;

[0029] SURFLON S-386 0.1%;

[0030] Defoamer 0.5%;

[0031] Kathon LXE 0.5%;

[0032] Polyurethane thickener 10%;

[0033] Ethylene glycol 4.0%;

[0034] Tripropylene glycol butyl ether 5.5%;

[0035] Dow's AMP-95 0.3%;

[0036] Rutile titanium dioxide 30%;

[0037] The remainder is water;

[0038] The water-based fluorocarbon emulsion is perfluoroalkane ethyl acrylate or dodecafluoroheptyl methacrylate and dodecyl methacrylate, p-chloromethyl styrene, hydroxypropyl acrylate or N-methylol propylene Anionic seed emulsion copolymerization of amide, vinyltriethoxysilane or γ-methacryloxypropyltrimethoxysilane in water phase, the reaction temperature is 80°C, the reaction time is 4h, and the solid content of the emulsion is 30% , pH is 6.0, viscosity is 5.0mPa·s.

[0039] The defoamer has a ...

Embodiment 2

[0041] A high-performance water-based fluorocarbon paint, calculated by 100% by mass, includes:

[0042] Water-based fluorocarbon emulsion 80%;

[0043] Silicone crosslinker 0.3%;

[0044] SURFLON S-386 0.05%;

[0045] Defoamer 0.3%;

[0046] Kathon LXE 0.4%;

[0047] Polyurethane thickener 2%;

[0048] Ethylene glycol 4.0%;

[0049] Tripropylene glycol butyl ether 2.5%;

[0050] Dow's AMP-95 0.2%;

[0051] Rutile titanium dioxide 7.5%;

[0052] The remainder is water;

[0053] The water-based fluorocarbon emulsion is perfluoroalkane ethyl acrylate or dodecafluoroheptyl methacrylate and dodecyl methacrylate, p-chloromethyl styrene, hydroxypropyl acrylate or N-methylol propylene Anionic seed emulsion copolymerization of amide, vinyltriethoxysilane or γ-methacryloxypropyltrimethoxysilane in water phase, the reaction temperature is 80°C, the reaction time is 4h, and the solid content of the emulsion is 30% , pH is 6.0, viscosity is 4mPa·s.

[0054] The defoamer has a t...

Embodiment 3

[0056] A high-performance water-based fluorocarbon paint, calculated by 100% by mass, includes:

[0057] Water-based fluorocarbon emulsion 60%;

[0058] Silicone crosslinking agent 0.2%;

[0059] SURFLON S-386 0.03%;

[0060] Defoamer 0.3%;

[0061] Kathon LXE 0.3%;

[0062] Polyurethane thickener 5%;

[0063] Ethylene glycol 2.5%;

[0064] Tripropylene glycol butyl ether 3%;

[0065] Dow's AMP-95 0.2%;

[0066] Rutile titanium dioxide 20%;

[0067] The remainder is water;

[0068] The water-based fluorocarbon emulsion is perfluoroalkane ethyl acrylate or dodecafluoroheptyl methacrylate and dodecyl methacrylate, p-chloromethyl styrene, hydroxypropyl acrylate or N-methylol propylene Anionic seed emulsion copolymerization of amide, vinyltriethoxysilane or γ-methacryloxypropyltrimethoxysilane in water phase, the reaction temperature is 80°C, the reaction time is 4h, and the solid content of the emulsion is 30% , pH is 6.0, viscosity is 3mPa·s.

[0069]The defoamer has ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-performance water-based fluorocarbon paint which comprises the following components in percentage by mass based on 100% in total: 50-80% of water-based fluorocarbon emulsion, 0.1-0.4% of siloxane crosslinking agent, 0.01-0.1% of surfactant, 0.2-0.5% of antifoaming agent, 0.2-0.5% of preservative, 2.0-4.0% of ethylene glycol, 2.0-5.5% of film forming aid, 0.05-0.3% of multifunctional auxiliary, 7.5-30% of titanium dioxide and the balance of water. According to the high-performance water-based fluorocarbon paint disclosed by the invention, through the improvement of the water-based fluorocarbon emulsion and in combination with the siloxane crosslinking agent and other related auxiliaries, the adhesion of the water-based fluorocarbon paint can be effectively improved; the improved fluorocarbon emulsion and the selected fluorine surfactant SURFLONS-386 promote each other; in combination with other related auxiliaries, the antifouling capacity of the water-based fluorocarbon paint can be effectively improved; by adopting the improved fluorocarbon emulsion, siloxane and fluorine surfactant SURFLONS-386 as main functional materials and in combination with the effects of the auxiliaries such as antifoaming agent, a preservative, ethylene glycol, a film forming aid, a multifunctional aid, titanium dioxide, water and the like, the prepared water-based fluorocarbon paint has the advantages of water and alkali resistance, strong solvent resistance, mildew and moisture prevention, high adhesion and good antifouling capacity.

Description

technical field [0001] The invention relates to the technology in the field of water-based paint, in particular to a high-performance water-based fluorocarbon paint. Background technique [0002] Ordinary walls have poor stain resistance, are prone to rain marks, and the walls are prone to cracking, blooming, powdering, peeling, and mildew. Many walls have problems such as pasting, graffiti, etc., which affect people's homes. The beauty of life and the city. People usually use top paint to improve the above problems. The main development direction of exterior wall decoration materials in my country should be environmentally friendly high-performance exterior wall coatings. Among high-performance exterior wall coatings, fluorocarbon paints should be the first choice. However, at present, many fluorocarbon wall paints have poor anti-fouling, poor solvent resistance, poor water and alkali resistance, poor aging resistance, poor mildew and moisture resistance, high surface tens...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D7/12
Inventor 黄宏亭蔡森桂玲谢志超王悦辉王先兰高小兵王海洋刘辉魏婷婷王方圆
Owner 广东黑马新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com