Magnetic-induction charged ceramic ultra-filtration membrane and preparation method thereof

A ceramic ultrafiltration membrane and magnetic induction technology, applied in the field of membrane separation, can solve the problems of short service life and low ion retention rate of charged ultrafiltration membrane, and achieve the effects of low cost, high ion retention rate and low production cost.

Active Publication Date: 2014-04-30
钱陈
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the defects of short service life and low ion rejection rate of the current charged ultrafiltration membrane, a magnetic induction charged ceramic ultrafiltration membrane and its preparation method are proposed. , and then add dispersant, thickener, defoamer to prepare the film-making liquid, coat the film on the porous support, and then sinter and cool under the protection of nitrogen to obtain the magnetic induction charged ceramic ultrafiltration membrane

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1) Dissolve 10 parts by weight of alumina colloidal particles in a solvent to form a uniformly dispersed and stable sol

[0033] 2) Add 1 part by weight of copper metal fiber and 1 part by weight of polyethyleneimine to the sol solution obtained in step 1), stir and disperse evenly, and then add 2 parts by weight of hydroxyethyl cellulose and 1 part by weight of Silicone defoaming agent, increase the viscosity of the sol solution, make the metal fiber not easy to settle in the sol solution, disperse evenly, and form a film-making solution;

[0034] 3) Coat the film-making liquid obtained in step 2) on a flat porous ceramic support, air-dry for 3 hours under natural conditions, and then coat the film again, repeating 2 times, and then sinter and dry the air-dried film under the protection of nitrogen. The temperature was lowered and cooled, the sintering temperature was 500° C., and the sintering time was 2 hours to obtain a magnetic induction charged ceramic ultrafiltra...

Embodiment 2

[0036] 1) Dissolve 10 parts by weight of titanium oxide colloidal particles in a solvent to form a uniformly dispersed and stable sol

[0037] 2) Add 2 parts by weight of aluminum metal fiber and 1 part by weight of citrate to the sol solution obtained in step 1), stir and disperse evenly, then add 2 parts by weight of polyvinyl alcohol and 1 part by weight of silicone defoaming while stirring agent to increase the viscosity of the sol solution, so that the metal fibers are not easy to settle in the sol solution, disperse evenly, and form a film-making solution;

[0038] 3) Coat the film-making solution obtained in step 2) on a flat porous metal support, air-dry for 3 hours under natural conditions, and then coat the film again, repeating 3 times, and then sinter and dry the air-dried film under the protection of nitrogen. The temperature was lowered and cooled, the sintering temperature was 600° C., and the sintering time was 4 hours to obtain a magnetic induction charged cer...

Embodiment 3

[0040] 1) Dissolve 15 parts by weight of zirconia colloidal particles in a solvent to form a uniformly dispersed and stable sol

[0041] 2) Add 3 parts by weight of copper metal fiber and 2 parts by weight of glycerol to the sol solution obtained in step 1), stir and disperse evenly, and then add 2 parts by weight of polyethylene glycol and 1 part by weight of silicone disinfectant while stirring. Foaming agent to increase the viscosity of the sol solution, so that the metal fibers are not easy to settle in the sol solution, disperse evenly, and form a film-making solution;

[0042] 3) Coat the membrane-forming solution obtained in step 2) on the tubular porous ceramic support, air-dry for 5 hours under natural conditions, and coat the membrane again, repeating 4 times, and then sinter and dry the air-dried membrane under the protection of nitrogen. The temperature was lowered and cooled, the sintering temperature was 800° C., and the sintering time was 4 hours to obtain a mag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a magnetic-induction charged ceramic ultra-filtration membrane and a preparation method of the magnetic-induction charged ceramic ultra-filtration membrane. A metal fiber is added into a colloid particle solution and stirred up and dispersed, a dispersant, a thickening agent and a defoamer are added into the mixture solution to prepare a membrane formation solution, a porous support is coated with the membrane formation solution, the membrane is cast and cooled under the protection of nitrogen, so as to prepare the magnetic-induction charged ceramic ultra-filtration membrane. The retaining effect of the ultra-filtration membrane on charged ions varies with the external magnetic field, and the retaining effect can be adjusted at any moment according to the actual situation, and the retaining effect of the charged ions is larger than 98%. The ultra-filtration membrane has advantages of resistance to pollution and corrosion, high strength, long service life, and wide application value.

Description

Technical field [0001] The present invention involves a membrane separation field, which specifically involves a magnetic induction lotus ceramic ultrafiltration film and its preparation method. Background technique [0002] The principle of ultrafiltration technology is a new membrane separation technology that uses asymmetric microporous structures and semi -transparent membrane medium at normal temperature, use asymmetric microporous structure and semi -transparent membrane medium, and uses asymmetric microporous structures and semi -transparent membrane medium.Ultrafilled membrane technology is separated by the driving force of static pressure difference and depending on the quality of the relative molecular quality.The ultrafiltration process is easy to operate and the equipment is simpler. The 0.01 ~ 0.1um pores unique to the ultra -filter membrane can effectively remove bacteria. Most viruses, colloids, and mud can be achieved.It has been widely used for separation, concen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01D71/02B01D69/02B01D67/00
Inventor 陈庆李兴文
Owner 钱陈
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com