Method for manufacturing flocked hot-dip galvanized printed board

A manufacturing method and hot-dip galvanizing technology, which are applied to chemical instruments and methods, devices for coating liquid on the surface, lamination devices, etc., can solve the problem of weak velvet feeling, monotonous color, and flocking of hot-dip galvanized sheets. Without problems such as diffuse reflection of light, it can achieve the effect of strong velvet feeling, soft hand feeling and bright colors

Inactive Publication Date: 2014-04-16
WUXI XINDAZHONG STEEL SHEET
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flocking hot-dip galvanized sheet has a weak velvet feel and monotonous color, especially as the surface area of ​​the flocking surface increases, the flocked hot-dip galvanized sheet cannot achieve excellent light diffuse reflection effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The manufacture method of a kind of flocking hot-dip galvanized printing plate of the present invention comprises the following steps:

[0018] (1) Material selection: The material selection is a hot-dip galvanized sheet with a thickness of 0.8mm and a width of 1200mm;

[0019] (2) Surface pretreatment: put the hot-dip galvanized sheet with a thickness of 0.8mm and a width of 1200mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is GR934 passivator produced by Nippon Paint, the single-side coating speed of the board surface treatment agent is: 15m / min, and the single-side coating amount of the board surface treatment agent is: 1.5g / m 2 , the temperature of the surface treatment agent is 25°C when coating;

[0020] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. The tem...

Embodiment 2

[0028] The manufacture method of a kind of flocking hot-dip galvanized printing plate of the present invention comprises the following steps:

[0029] (1) Material selection: The material selection is a hot-dip galvanized sheet with a thickness of 1.6mm and a width of 1800mm;

[0030] (2) Surface pretreatment: Put the hot-dip galvanized sheet with a thickness of 1.6mm and a width of 1800mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is GR934 passivator produced by Nippon Paint, the single-side coating speed of the board surface treatment agent is: 35m / min, and the single-side coating amount of the board surface treatment agent is: 0.8g / m 2 , the temperature of the board surface treatment agent is 35°C when coating;

[0031] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. T...

Embodiment 3

[0039] The manufacture method of a kind of flocking hot-dip galvanized printing plate of the present invention comprises the following steps:

[0040] (1) Material selection: The material selection is a hot-dip galvanized sheet with a thickness of 1.2mm and a width of 1600mm;

[0041](2) Surface pretreatment: put the hot-dip galvanized sheet with a thickness of 1.2mm and a width of 1600mm that is clean and unoiled into the surface treatment machine for surface pretreatment of coating the surface treatment agent , the coated board surface treatment agent is GR934 passivator produced by Nippon Paint, the single-side coating speed of the board surface treatment agent is: 25m / min, and the single-side coating amount of the board surface treatment agent is: 1.2g / m 2 , the temperature of the surface treatment agent is 30°C when coating;

[0042] (3) Drying treatment: the hot-dip galvanized sheet coated with the surface treatment agent enters the oven for drying treatment. The temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for manufacturing a building board which has corrosion resistance and weather resistance, can prevent dew from dripping and has certain thermal insulation performance, in particular to a method for manufacturing a flocked hot-dip galvanized printed board. The method includes the following steps: material selection, board surface pretreatment, drying treatment, printing, spreading of an adhesive and epoxy zinc-rich paint mixture, electrostatic flocking, drying, checking and warehousing; the method is characterized in that dacron flock is adopted in the electrostatic flocking step, and the GR934 passivator is adopted as a board surface treating agent. The board obtained through the method has excellent fire resistance; as is shown in detection, the board passes the National Building Material Fireproofing Grade B-1 Certification and is environmentally friendly and free of pollution; the board also passes the Environmental Certification, can be directly used indoors and has the advantages of being strong in upright-flock sense, bright in color, capable of achieving comfortable touch and good in sound absorption performance, light absorption performance and light diffuse reflection effect.

Description

technical field [0001] The invention relates to a method for manufacturing a building plate with corrosion resistance, weather resistance, dew condensation prevention, and thermal insulation performance, especially a method for manufacturing a flocking hot-dip galvanized printing plate. Background technique [0002] In modern decoration, hot-dip galvanized sheets are used in many cases, such as square hot-dip galvanized gussets for integrated ceilings, and large-area hot-dip galvanized paint panels for wall decoration. The flocking hot-dip galvanized sheet can provide more luxurious decorative effects than existing products. The fleece itself has a certain water absorption capacity. When the ambient humidity is too high, it can keep the condensation water on the surface of the sheet to prevent water droplets from dripping . However, the flocking hot-dip galvanized sheet has a weak velvet feel and monotonous color, especially as the surface area of ​​the flocking surface exp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B05D5/00B05D3/02B32B37/24B32B37/12B32B38/14
Inventor 周明华
Owner WUXI XINDAZHONG STEEL SHEET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap