Anti-blue-ray resin lens with refraction index of 1.56 and preparation method thereof

A resin lens and refractive index technology, applied in the field of optical lenses, can solve problems such as aggravating chromatic aberration and visual blurring, increasing the distance of light chromatic aberration, strengthening blood supply to the eyes, etc., achieving excellent adhesion, reducing tingling and soreness, The effect of preventing cataract and macular degeneration

Inactive Publication Date: 2014-03-26
江苏硕延光学眼镜有限公司
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

(2) After the blue light enters the fundus and is focused, the focal point does not fall on the retina, but falls between the retina and the lens, which increases the chromatic aberration distance of the light focusing in the eye, and the distance between the focal points in the eye It is the main cause of blurred vision, so the injection of blue light will exacerbate chromatic aberration and visual blurring, and then the eye muscles will be overly tense, the blood supply to the eyes will be overly tense, and the blood supply to the eyes will be strengthened, which will aggravate fatigue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-blue-ray resin lens with refraction index of 1.56 and preparation method thereof
  • Anti-blue-ray resin lens with refraction index of 1.56 and preparation method thereof
  • Anti-blue-ray resin lens with refraction index of 1.56 and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The anti-blue light resin lens described in the present embodiment, its resin substrate is made of 950 parts by weight of polybisallyl diglycol dicarbonate CR-39, 50 parts by weight of allyl diethylene glycol carbonate and bisphenol A carbonate KOC-55, 29 parts by weight of diisopropyl peroxydicarbonate IPP, 5 parts by weight of UV-329 and 3 parts by weight of UV-366 are made; its preparation process includes batching, filling, primary curing, substrate treatment, Secondary curing and substrate cleaning processes:

[0026] 1. Ingredients

[0027] 1.1 Weighing of raw materials: Polydiallyl diglycol dicarbonate CR-39: 950 parts by weight, allyl diethylene glycol carbonate and bisphenol A carbonate KOC-55: 50 parts by weight, peroxydicarbonate dicarbonate Isopropyl ester IPP: 29 parts by weight, UV-329: 5 parts by weight, UV-366: 3 parts by weight; the UV-329 refers to the ultraviolet absorber UV-329, and the UV-366 refers to the ultraviolet absorber UV -366;

[0028] 1...

Embodiment 2

[0059] The anti-blue light resin lens described in the present embodiment, its resin substrate is made of 950 parts by weight of polybisallyl diglycol dicarbonate CR-39, 50 parts by weight of allyl diethylene glycol carbonate and bisphenol A carbonate KOC-55, 29 parts by weight of diisopropyl peroxydicarbonate IPP, 3 parts by weight of hydroxyethyliminodiacetic acid, 22 parts by weight of trimethylolpropane tripacrylate, 5 parts by weight of UV-329 and 3 parts by weight It is made of UV-366 in parts by weight; its preparation process includes steps such as batching, filling, primary curing, substrate treatment, secondary curing and substrate cleaning:

[0060] 1. Ingredients

[0061] 1.1 Weighing of raw materials: Polydiallyl diglycol dicarbonate CR-39: 950 parts by weight, allyl diethylene glycol carbonate and bisphenol A carbonate KOC-55: 50 parts by weight, peroxydicarbonate dicarbonate Isopropyl ester IPP: 29 parts by weight, hydroxyethyliminodiacetic acid: 3 parts by wei...

Embodiment 3

[0093]Compared with Example 1, the difference is only in the third SiO 2 A waterproof film layer is deposited on the film layer, and the water vapor transmission rate is lower than 3×10 under the conditions of 25°C and 90% R.H. -4 gm -3 the day -1 ; wherein the waterproof film layer is prepared by PECVD method, wherein the deposition temperature is 100 ~ 120 ° C, with 0.50Wcm -2 The power is applied to the plasma, the working pressure is 200-250Pa, the flow rate of silane is 100sccm, the flow rate of methane is 20sccm, the flow rate of ammonia is 300sccm, the flow rate of nitrogen is 2000sccm, the flow rate of hydrogen is 5000sccm, and the thickness of the waterproof film layer is 1.5~3.5μm. The waterproof film layer has extremely excellent waterproof performance, which can ensure that the resin lens of the present invention maintains a blue light filtering rate of 44-48% within 3-5 years.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an anti-blue-ray resin lens with the refraction index of 1.56. The anti-blue-ray resin lens with the refraction index of 1.56 comprises a resin substrate with the refraction index of 1.56; the resin substrate is dip-coated with a hardened film; a first SiO2 film, a ZrO2 film, a second SiO2 film, a Ti2O3 film, an In2O3 film and a third SiO2 film are deposited on the surface of the hardened film in sequence. According to the resin lens disclosed by the invention, the effect of filtering blue rays with the wavelength of 400 to 500 nm can reach 40 to 50 percent; blue ray radiation can be filtered effectively; sharp pain, soreness and swelling of eyes can be reduced; eye dryness and eye fatigue can be reduced; cataract and macular degeneration can be prevented.

Description

technical field [0001] The invention relates to the technical field of optical lenses, more specifically, the invention relates to a method for preparing and coating a high-refractive index resin lens, and the prepared resin lens has excellent anti-blue light performance. Background technique [0002] The damage of ultraviolet rays to the eyes and the body is known to the world, and a variety of anti-ultraviolet spectacle lenses have also been developed in the prior art and have been widely used. In comparison, blue light damage has only been known to the world in recent years. According to data from the Ophthalmology Branch of the Chinese Medical Association, among the 420 million Internet users in China, 63.5% of them suffer from vision loss, cataracts, and blindness due to blue light radiation. The World Health Organization (WHO) announced that from 2006 to 2008, more than 30,000 people around the world were blinded by blue light radiation every year. [0003] Blue ligh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G02C7/10G02B1/10B32B9/04B32B27/06G02B1/14
Inventor 赵勤
Owner 江苏硕延光学眼镜有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com