Waterproof temperature-resistant modified nylon material for automobile plastic members
A technology for modifying nylon and plastic parts, which is applied in the field of waterproof and temperature-resistant modified nylon materials for automotive plastic parts and its preparation. The effect of light weight and improved performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment
[0012] The material in this embodiment is made of the following raw materials in parts by weight: nylon 12 100, chopped glass fiber 14, stearic acid amide 6, ammonium polyphosphate 6, bentonite 14, trimethylsilylmethyl phosphonate 18, cyanide Melamine uric acid 45, antimony trioxide 12, polystyrene 25, montmorillonite 10, ricinoleic acid 6, additive 15.
[0013] The auxiliary agent is made of the following raw materials in parts by weight: clay 300, silicon carbide 9, jade powder 6, antioxidant 565 0.2, trimethylolethane 8, polyisobutylene 4, N-(β-aminoethyl base)-γ-aminopropyltrimethyl(ethyl)oxysilane 3, nonylphenol 2, isophorone diisocyanate 2, hydroxyethyl methacrylate 8, aluminum hydroxide 8, clove oil 1, stearic acid Calcium 2; the preparation method is to put the clay into a calciner and calcinate at 740°C for 4 hours, cool it, soak it in 12% hydrochloric acid solution for 2 hours, filter it out, wash it with water and dry it, and crush it into a 400-mesh powder. Mix wi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com