Novel strongly acid-resistant archaistic glazed tile
A glazed tile, a new type of technology, applied in the field of building materials, can solve the problems of high material toxicity, unfavorable health and environmental protection, ecological balance damage, etc., and achieve the effect of light weight
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0013] Preparation:
[0014] Coal ash 10kg, polytetrafluoroethylene 100kg, quartz powder 15kg, water glass 35kg, alum 10kg, iron oxide pigment 8kg, triethanolamine 3kg.
[0015] Production of antique glazed tiles:
[0016] (1) Weigh the material according to the proportion, crush the fineness to 200 mesh, mix in the mixer, control the mixing temperature at 15-19°C, mix in two times, each mixing time is 3-5 minutes;
[0017] (2) After the mixture is sieved through a 40-mesh sieve, it is then put into a mold, and cold pressed for 5 to 8 minutes under a pressure of 50 MPa. The parison is gently taken out from the mold, sintered in a sintering furnace, and uniform within 6 hours. Raise the temperature to 330°C, rise to 370°C in 8.3 hours, keep the temperature for 3 hours, then cool down, uniformly cool down to 310°C within 2 hours, maintain the temperature for 1 hour, and then cool down to room temperature uniformly within 1.5 hours, after cutting and trimming get the product. ...
Embodiment 2
[0038] Preparation:
[0039] Coal ash 11kg, polytetrafluoroethylene 100kg, quartz powder 18kg, water glass 38kg, alum 11kg, iron oxide pigment 10, triethanolamine 4.5kg.
[0040] Production of antique glazed tiles:
[0041] (1) Weigh the material according to the proportion, crush the fineness to 200 mesh, mix in the mixer, control the mixing temperature at 15-19°C, mix in two times, each mixing time is 3-5 minutes;
[0042] (2) After the mixture is sieved through a 40-mesh sieve, it is then put into a mold, and cold pressed for 5 to 8 minutes under a pressure of 50 MPa. The parison is gently taken out from the mold, sintered in a sintering furnace, and uniform within 6 hours. Raise the temperature to 330°C, rise to 370°C in 8.3 hours, keep the temperature for 3 hours, then cool down, uniformly cool down to 310°C within 2 hours, maintain the temperature for 1 hour, and then cool down to room temperature uniformly within 1.5 hours, after cutting and trimming get the product. ...
Embodiment 3
[0046] Preparation:
[0047] Coal ash 12kg, polytetrafluoroethylene 100kg, quartz powder 20kg, water glass 40kg, alum 12kg, iron oxide pigment 12kg, triethanolamine 5.5kg.
[0048] Production of antique glazed tiles:
[0049] (1) Weigh the material according to the proportion, crush the fineness to 200 mesh, mix in the mixer, control the mixing temperature at 15-19°C, mix in two times, each mixing time is 3-5 minutes;
[0050] (2) After the mixture is sieved through a 40-mesh sieve, it is then put into a mold, and cold pressed for 5 to 8 minutes under a pressure of 50 MPa. The parison is gently taken out from the mold, sintered in a sintering furnace, and uniform within 6 hours. Raise the temperature to 330°C, rise to 370°C in 8.3 hours, keep the temperature for 3 hours, then cool down, uniformly cool down to 310°C within 2 hours, maintain the temperature for 1 hour, and then cool down to room temperature uniformly within 1.5 hours, after cutting and trimming get the product...
PUM
Property | Measurement | Unit |
---|---|---|
Fineness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap