Polyphenylene sulfide fibers and nonwoven fabric

A technology of polyphenylene sulfide fiber and polyphenylene sulfide, applied in fiber treatment, fiber chemical characteristics, textiles, etc., can solve the problems of poor thermal adhesion and no proposal, and achieve excellent thermal adhesion and mechanical strength excellent effect

Active Publication Date: 2014-02-05
TORAY IND INC
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, all solutions suffer from poor thermal adhesion
[0005] As mentioned above, regarding PPS fibers or PPS non-woven fabrics that simultaneously achieve heat resistance and thermal adhesiveness, there is currently no proposal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenylene sulfide fibers and nonwoven fabric
  • Polyphenylene sulfide fibers and nonwoven fabric
  • Polyphenylene sulfide fibers and nonwoven fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0105] (PPS resin)

[0106] 100 mol% linear polyphenylene sulfide resin (manufactured by Toray Co., Ltd., product number: E2280, MFR: 160 g / 10 minutes) in which trichlorobenzene was intentionally not copolymerized was dried in a nitrogen atmosphere at a temperature of 160° C. for 10 minutes. hours to use.

[0107] (spinning and non-woven reticulation)

[0108] Melt the above PPS resin with an extruder, and at a spinning temperature of 320°C, It was spun at a single-hole discharge rate of 1.38 g / min in a rectangular spinning nozzle. The distance from the rectangular spinning nozzle to the rectangular injector was set at 55 cm, and the spun filaments were cooled and solidified in an atmosphere at a room temperature of 20°C. The cooled and solidified filaments are passed through a rectangular injector, and compressed air is sprayed from the injector, and the compressed air is heated to a temperature of 230°C with an air heater and the pressure of the injector is 0.15MPa, to d...

Embodiment 2

[0114] (PPS resin · spinning · nonwoven reticulation)

[0115] A nonwoven web was formed by spinning in the same manner as in Example 1, except that the same PPS resin as that used in Example 1 was used, and the temperature of the compressed air was set to 200°C.

[0116] The average single fiber fineness of the obtained long fiber is 2.8dtex, the crystallinity is 17.3%, the sum of rigid amorphous and crystallinity is 37.3%, and the boiling water shrinkage is 7.0%. In addition, the spinning speed was 4,991 m / min, and there were no yarn interruptions in one hour of spinning, and the spinnability was good.

[0117] (Temporary Bonding · Thermal Bonding)

[0118] Next, the above-mentioned nonwoven web was temporarily bonded and thermally bonded in the same manner as in Example 1 to obtain the long-fiber nonwoven fabric of Example 2.

[0119] When the obtained nonwoven fabric was thermally bonded using an embossing roll, it did not have a large width shrinkage caused by thermal s...

Embodiment 3

[0121] (PPS resin · spinning · nonwoven reticulation)

[0122] The same PPS resin as the resin used in Example 1 was used, except that the temperature of the compressed air was 140° C., and spinning was carried out in the same manner as in Example 1 to form a nonwoven web.

[0123] The average single fiber fineness of the obtained long fiber is 2.9dtex, the crystallinity is 15.1%, the sum of rigid amorphous and crystallinity is 31.3%, and the boiling water shrinkage is 17.5%. In addition, the spinning speed was 4,824 m / min, and there were 0 interruptions in spinning for 1 hour, and the spinnability was good.

[0124] (Temporary Bonding · Thermal Bonding)

[0125] Next, the above-mentioned nonwoven web was temporarily bonded and thermally bonded in the same manner as in Example 1 to obtain the long-fiber nonwoven fabric of Example 3.

[0126] The obtained nonwoven fabric did not suffer from large width shrinkage due to heat shrinkage even when heat-compression bonding was perfo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystallinityaaaaaaaaaa
shrinkageaaaaaaaaaa
crystallinityaaaaaaaaaa
Login to View More

Abstract

Provided are: polyphenylene sulfide fibers which are mainly composed of a PPS resin and has excellent heat resistance and thermal bondability at the same time; and a nonwoven fabric which is configured of the fibers. The polyphenylene sulfide fibers are characterized by being mainly composed of a polyphenylene sulfide and having a sum of the crystallinity and the rigid amorphia of 30-90% (inclusive). The crystallinity is preferably 5% or more but less than 25%. A nonwoven fabric is configured using the polyphenylene sulfide fibers. The nonwoven fabric is preferably integrated by thermal bonding or mechanical interlacing.

Description

technical field [0001] The present invention relates to fibers made of a resin mainly composed of polyphenylene sulfide (hereinafter sometimes abbreviated as "PPS") and a nonwoven fabric made of the fibers. Background technique [0002] PPS resin has excellent heat resistance, flame retardancy, and chemical resistance, and is suitable for engineering plastics, films, fibers, and non-woven fabrics. In particular, nonwoven fabrics are expected to be used in industrial applications such as heat-resistant filters, electrical insulating materials, and battery separators by making use of the above-mentioned characteristics. [0003] On the other hand, when the PPS resin is molded into fibers to form a nonwoven fabric, the dimensional stability against heat is poor, and the heat shrinkage of the fiber or the nonwoven fabric is large, which is a problem. [0004] As a method of improving the dimensional stability of PPS nonwoven fabrics, for example, long-fiber nonwoven fabrics hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/76D04H3/009D04H3/08D04H3/14
CPCD01D5/08D01F6/765D04H1/54D01D5/04D04H1/44D04H1/4326D01D5/253Y10T442/60Y10T442/69D01F6/76D04H3/009D04H3/10D04H3/14
Inventor 中野洋平矢挂善和伊藤正士
Owner TORAY IND INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com