Steel plate for low-temperature vessel and production method thereof

A low-temperature container and production method technology, applied in the field of steel plates for low-temperature containers, can solve the problems of high cost and poor Z-direction performance, and achieve the effects of high low-temperature impact energy, excellent comprehensive performance, and high Z-direction section shrinkage.

Active Publication Date: 2014-01-29
WUYANG IRON & STEEL +1
View PDF4 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mechanical properties of domestic large-thickness, large-weight steel, such as negative temperature impact energy at 1 / 2 of the plate thickness, especially the Z-direction performance is not good, and the production cost is high, resulting in domestic large-thickness, large single-weight steel plates for low-temperature pressure vessels Can not meet market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel plate for low-temperature vessel and production method thereof
  • Steel plate for low-temperature vessel and production method thereof
  • Steel plate for low-temperature vessel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] This example is: 10mm thick steel plate for low-temperature pressure vessel and its production method. The steel plate is smelted from the following components by weight percentage: C: 0.10%, Si: 0.30%, Mn: 1.47%, Ni: 0.38%, P: 0.008%, S: 0.001%, Al: 0.040%, Nb: 0.019%, and the balance is iron and unavoidable impurities.

[0052] The steps of the steel plate production method of the present embodiment are as follows:

[0053] 1) Smelting: The molten steel containing the above weight percentage components is first smelted in an electric furnace, sent to an LF refining furnace for refining, and 17kg / t of lime is added to the steel, fed to an Al line of 700 meters to remove oxygen in the molten steel, and the white slag is kept for 35 minutes. When the temperature of the molten steel reaches 1640°C, it is transferred to the VD furnace for vacuum degassing treatment. The vacuum degree is not greater than 66.6Pa, and the vacuum holding time is 22 minutes. Before vacuuming, 1...

Embodiment 2

[0061] This example is: 32mm thick steel plate for low temperature pressure vessel and its production method. The steel plate is smelted from the following components by weight percentage: C: 0.11%, Si: 0.28%, Mn: 1.43%, Ni: 0.33%, P: 0.003%, S: 0.001%, Al: 0.035%, Nb: 0.017%, and the balance is iron and unavoidable impurities.

[0062] The steps of the steel plate production method of the present embodiment are as follows:

[0063] 1) Smelting: The molten steel containing the above weight percentage components is first smelted in an electric furnace, sent to an LF refining furnace for refining, and 19kg / t of lime is added to the steel, fed to an Al line of 750 meters to remove oxygen in the molten steel, and the white slag is kept for 45 minutes. When the temperature of the molten steel reaches 1635°C, it is transferred to the VD furnace for vacuum degassing treatment. The vacuum degree is not greater than 66.6Pa, and the vacuum holding time is 21 minutes. Before vacuuming, 1...

Embodiment 3

[0071] This example is: 64mm thick steel plate for low-temperature pressure vessel and its production method. The steel plate is smelted from the following components by weight percentage: C: 0.08%, Si: 0.33%, Mn: 1.46%, Ni: 0.67%, P: 0.009%, S: 0.002%, Al: 0.035%, Nb: 0.03%, and the balance is iron and unavoidable impurities.

[0072] The steps of the steel plate production method of the present embodiment are as follows:

[0073] 1) Smelting: The molten steel containing the above weight percentage components is smelted in an electric furnace first, sent to an LF refining furnace for refining, fed with lime 21kg / t steel, and the Al line is 720 meters to remove oxygen in the molten steel, and the white slag is kept for 40 minutes. When the temperature reaches 1645°C, transfer to a VD furnace for vacuum degassing treatment, the vacuum degree is not greater than 66.6Pa, the vacuum holding time is 22 minutes, and 165kg of CaSi blocks are added before vacuuming;

[0074] 2) Casti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a steel plate for a low-temperature vessel and a production method thereof, belonging to the technical fields of special steel plates and steel plate production methods. The steel plate for a low-temperature vessel is produced by smelting the following components in percentage by weight: no more than 0.12% of C, 0.15-0.50% of Si, 1.2-1.6% of Mn, 0.3-0.8% of Ni, no more than 0.010% of P, no more than 0.005% of S, 0.020-0.045% of Al, no more than 0.040% of Nb and the balance of Fe and inevitable impurities. The invention develops a new steel plate for a low-temperature vessel and a production method thereof. The favorable mechanical property of the steel plate is ensured under the condition of low noble alloy consumption, so that the steel plate has good organization, comprehensive property and weldability, the low-temperature impact toughness of the steel plate in a delivery state and a die welding state is improved, and the requirements of the market for high-quality steel for a low-temperature vessel are met, thus making positive contributions for domestic production of large engineering low-temperature equipment and achieving remarkable economic benefits.

Description

technical field [0001] The invention relates to a steel plate for cryogenic containers and a production method of the steel plate, and belongs to the technical field of special steel plates and steel plate production methods. Background technique [0002] In recent years, with the in-depth development of petrochemical and coal chemical industries, the steel for cryogenic pressure vessels used in the manufacture of various condensation tower equipment in coal chemical, petrochemical and other equipment has developed rapidly. The demand for steel is increasing, and customers have more and more stringent requirements on the impact toughness of the 1 / 2 thickness of the steel plate, and put forward long-term (more than 10 hours) mold welding performance requirements, which have never been done before. The mechanical properties of domestic large-thickness, large-weight steel, such as negative temperature impact energy at 1 / 2 of the plate thickness, especially the Z-direction perfo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/12C22C33/04C21D8/02
Inventor 刘丹刘生张海军高雅张志军王晓书
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More