Polyolefin resin composition with lusterless characteristic

A technology of polyolefin resin and polypropylene resin, which is applied in the field of film materials, can solve the problems of lack of matte effect and complicated production and processing of films, and achieve the effects of excellent matte characteristics, simple production and excellent molding performance

Inactive Publication Date: 2014-01-22
大韩道恩高分子材料(上海)有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the current problems of lack of matte effect and complicated production and processing of films, a solution is now provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyolefin resin composition with lusterless characteristic

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0037] 45-55 parts by weight of homopolypropylene with a melt index of 3-4g / 10min, 45-55 parts by weight of high-density polyethylene with a melt index of 0.09-0.15g / 10min, 0.1 part by weight of peroxide, and 0.2-0.25 parts by weight of oxidation inhibitor % parts by weight. It is produced by mixing and extruding with a twin-screw extruder.

example 2

[0039] A composite resin composition was produced in the same manner as in Example 1, using 45 to 55 parts by weight of random copolymer of ethylene / 1-butene and 45 to 55 weight percent of high-density polyethylene (HDPE). The results are shown in Table 1.

example 3

[0041] Using 50-80 parts by weight of random copolymer of ethylene / 1-butene and 20-50 parts by weight of high-density polyethylene, the same method as Example 1 was used to prepare a composite resin composition. The results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyolefin resin composition with a lusterless characteristic. The composition comprises, by weight, 20 to 80% of a polypropylene random copolymer resin of homo-polypropylene or ethylene / 1-butylene and 80 to 20% of a high density polyethylene resin. The polyolefin resin composition has the advantages of a low price and excellent performance; a film prepared from the polyolefin resin composition has excellent mechanical properties, heat resistance, resistance to chemical reagents and superior formability, can be used for food packaging and commodity packaging and as coating materials for other materials and is a lusterless biaxial drawing polypropylene film with the advantages of the lusterless characteristic, simple manufacturing and excellent processability.

Description

technical field [0001] The invention relates to the technical field of film materials, in particular to a polyolefin resin composition with matt properties. Background technique [0002] The packaging industry has relatively high requirements for transparent plastic films, such as biaxially oriented polypropylene films. The surface of the film in the present invention is not generally high-gloss but dull, so it has a unique texture. [0003] Recently, films with low surface gloss and soft touch are widely used as high value-added products, and are produced by casting. [0004] The conventional production methods of polyolefin film include blow molding and casting molding. Films produced by blow molding with a T-die or circular die have excellent impact strength and tear strength, and are relatively inexpensive in terms of equipment investment, so they are often used. However, because the material will be stretched by blow molding, the melt strength of the resin must reach...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L23/08C08L23/14C08K5/14
CPCC08L23/12C08L23/06C08L23/0815C08L2203/16C08L2207/062
Inventor 河贤洙于晓宁赵德慧
Owner 大韩道恩高分子材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com