60mm steel plate with excellent performance in thickness direction for ocean platform and production method thereof

An ocean platform, technology in the thickness direction, applied in the manufacture of converters, etc., can solve the problems of long time, high cost, complicated process, etc., and achieve the effect of fine grain, excellent performance, and reduced segregation

Inactive Publication Date: 2013-12-18
JIGANG GRP
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, the patent application with the application number 201310154636.7 discloses a 355MPa grade easy-to-weld steel plate for offshore platforms and its production process. The chemical composition of the steel plate with a thickness specification of (40-60 mm) contains vanadium, and the price of vanadium alloys is relatively high. Expensive, high cost, no cost advantage
[0006] In the existing converter smelting process, the double slag method is used for dephosphorization, the process is complicated, the time is long, and the content of components is not easy to control during the operation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The steel plate for offshore platforms with excellent performance in the thickness direction of 60 mm includes the following chemical composition in mass percentage: C 0.13%, Si 0.25%, Mn 1.41%, P 0.015%, S 0.004%, Nb 0.058%, Ti 0.017%, Als 0.035%, the balance is Fe and unavoidable impurities.

[0025] The production method of the steel plate for the offshore platform comprises the following steps:

[0026] (1) KR pretreatment: After KR pretreatment, the mass percentage of S in the molten iron entering the converter is 0.006%;

[0027] (2) Converter smelting: In the process of converter smelting, the single slag method is used to dephosphorize, and then the slag is blocked to tap the steel;

[0028] (3) LF refining: Bottom-blown argon stirring during the LF refining process, white slag operation, LF refining time 12 minutes, adding FeTi out of the station;

[0029] (4) RH refining: During the RH refining process, keep the vacuum below 2mbar for 15 minutes;

[0030] (...

Embodiment 2

[0042] The steel plate for offshore platforms with excellent performance in the thickness direction of 60 mm includes the following chemical composition in mass percentage: C 0.11%, Si 0.32%, Mn 1.47%, P 0.012%, S 0.003%, Nb 0.052%, Ti 0.015%, Als 0.037%, the balance is Fe and unavoidable impurities.

[0043] The production method of the steel plate for the offshore platform comprises the following steps:

[0044] (1) KR pretreatment: After KR pretreatment, the mass percentage of S in the molten iron entering the converter is 0.004%;

[0045] (2) Converter smelting: In the process of converter smelting, the single slag method is used to dephosphorize, and then the slag is blocked to tap the steel;

[0046] (3) LF refining: Bottom-blown argon stirring during the LF refining process, white slag operation, LF refining time 13 minutes, adding FeTi out of the station;

[0047] (4) RH refining: During the RH refining process, keep the vacuum below 2mbar for 12 minutes;

[0048] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of structural steels for ship and ocean engineering, and particularly relates to a 60mm steel plate with excellent performance in a thickness direction for an ocean platform and a production method thereof. The 60mm steel plate with excellent performance in the thickness direction for the ocean platform comprises the following chemical components by mass percent: 0.09-0.14% of C, 0.20-0.50% of Si, 1.10-1.50% of Mn, less than or equal to 0.015% of P, less than or equal to 0.005% of S, 0.030-0.060% of Nb, 0.010-0.020% of Ti, 0.015-0.050% of Als, the balance of Fe, and inevitable impurities. The steel plate has excellent performances in the thickness direction, steelmaking production adopts a single slag process, and the production method is simple and feasible.

Description

technical field [0001] The invention belongs to the technical field of structural steel for ships and ocean engineering, and in particular relates to a steel plate for an ocean platform with excellent performance in the thickness direction of 60 mm and a production method thereof. Background technique [0002] With the continuous development of the global economy, the demand for energy at home and abroad continues to grow, especially the demand for oil and natural gas, which has increased dramatically. While the supply of land resources is decreasing day by day, countries all over the world pay great attention to the development and utilization of marine energy, and the construction of ocean platforms has been paid more and more attention. Performance requirements are getting higher and higher. [0003] 60mm thick steel plates for offshore platforms are mostly used in key parts such as jackets of jack-up offshore platforms. They are used in underwater service for a long tim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/14C22C33/04C21C1/02C21C5/28C21C7/072C21D8/02
Inventor 李旺生孙风晓徐洪庆王焕洋李敏王勇朱延山
Owner JIGANG GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com