Preparation method for different carbon fibers / cobalt hydroxide electrode and solid-liquid composite electrode system

A technology of cobalt hydroxide and solid-liquid recombination, which is applied in the manufacture of hybrid/electric double layer capacitors and electrodes of hybrid capacitors, can solve the problems of low energy density, achieve high electrochemical activity, simple operation, and reduce the internal resistance of electrodes. Effect

Inactive Publication Date: 2013-12-04
JILIN UNIV
View PDF2 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, relative to batteries, its energy density is still low, which will largely limit its use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for different carbon fibers / cobalt hydroxide electrode and solid-liquid composite electrode system
  • Preparation method for different carbon fibers / cobalt hydroxide electrode and solid-liquid composite electrode system
  • Preparation method for different carbon fibers / cobalt hydroxide electrode and solid-liquid composite electrode system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0075] 1) Cut the 2mm thick carbon felt into a rectangle with an area of ​​1cm x 2cm.

[0076] 2) Soak the rectangular sample in a beaker filled with acetone solution, let it stand for 2 hours, and sonicate it in the solution for 10 minutes; rinse the sample with ethanol solution, soak it in a beaker filled with ethanol solution, and let it stand for 2 hours. After 1 hour, ultrasonic in the solution for 10 min; rinse the sample with deionized water, soak it in a beaker filled with deionized water, let it stand for 2 hours, and ultrasonic in the solution for 10 min. After repeated rinsing with deionized water, dry in an oven at 60°C for 18 hours. After cooling down, the mass of the sample was weighed with a microbalance.

[0077] 3) Adjust the voltage of the potentiostat to -0.9V, and use the cathodic deposition method for electrodeposition. Electrodeposition adopts a three-electrode system, the above-mentioned treated carbon felt is the working electrode, the counter electro...

Embodiment 2

[0081] In Step 1) of Example 1, the carbon felt is replaced by carbon cloth, and the rest of the steps are the same as in Example 1. According to electrochemical tests, when the current density is 2A / g, the specific capacitance can reach 1055F / g.

Embodiment 3

[0083] 1) Cut the 2mm thick carbon felt into a rectangle with an area of ​​1cm x 2cm.

[0084] 2) Soak the rectangular sample in a beaker filled with acetone solution, let it stand for 2 hours, and sonicate it in the solution for 10 minutes; rinse the sample with ethanol solution, soak it in a beaker filled with ethanol solution, and let it stand for 2 hours. After 1 hour, ultrasonic in the solution for 10 min; rinse the sample with deionized water, soak it in a beaker filled with deionized water, let it stand for 2 hours, and ultrasonic in the solution for 10 min. After repeated rinsing with deionized water, dry in an oven at 60°C for 18 hours.

[0085] 3) After the dried sample is lowered to room temperature, soak it in a beaker filled with a mixed solution of nitric acid: sulfuric acid = 1:3 (volume ratio), and let it stand for 2 hours. Then, the samples were rinsed repeatedly with deionized water. The samples were soaked in deionized water overnight, soaked for 12 hours, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
current efficiencyaaaaaaaaaa
current efficiencyaaaaaaaaaa
current efficiencyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for different carbon fibers / a cobalt hydroxide electrode and a solid-liquid composite electrode system. By means of pretreatment and modification of different carbon fibers, the carbon fibers serve as a substrate, composite of metal oxide or hydroxide and the carbon fibers are realized by the electrochemical deposition, and a solid electrode is obtained and has high specific capacitance in the alkaline aqueous solution. Redox substances are added into the alkaline aqueous solution, a composite electrode system that the solid electrode and liquid-phase electrolyte supply the pseudocapacitance jointly is obtained. The composite electrode system has ultra-high specific capacitance, is applied in supercapacitors, and has the advantages of ultra-high energy density, high power density and long service life. The specific capacitance of the composite electrode system can be adjusted by changing the concentration and volume of the redox substances, and the energy density and power density of the supercapacitors can be further changed to meet different using requirements.

Description

technical field [0001] The invention relates to a composite electrode system of different carbon fiber materials / cobalt hydroxide electrodes and solid-liquid two-phase pseudocapacitance. Electrochemical deposition method was used to prepare different carbon fiber materials / cobalt hydroxide solid electrodes, which were used in KOH electrolyte. On the basis of the above, different redox substances are added to the KOH solution, and the pseudocapacitance produced by different redox substances can be superimposed and synergistic with the solid electrode pseudocapacitance in this system, thereby obtaining an unprecedented ultrahigh specific capacitance. It specifically involves the pretreatment and modification of different carbon fiber materials, and based on this, the metal oxide or hydroxide is combined with the carbon fiber material substrate by electrochemical deposition. In the KOH electrolyte, by changing the redox substance The concentration and volume of the supercapacito...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01G11/32H01G11/40H01G11/86
CPCY02E60/13
Inventor 郑伟涛王浩翔张恒彬王欣赵翠梅
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com