Waterborne sealing agent for zinc-based micro coating and preparation method of waterborne sealing agent

A water-based sealing agent and micro-coating technology, applied in the coating process of metal materials, etc., can solve problems such as poor high temperature resistance, safety hazards, and strong odor, and achieve improved acid and alkali resistance and high temperature resistance, good adhesion, Good anti-corrosion effect

Inactive Publication Date: 2013-11-20
JIANGSU BOYE COATING ENG CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since organic coatings and zinc-based micro-coatings cannot be combined by chemical bonds, the binding force of the treated coating system needs to be improved.
Secondly, due to the poor high temperature resistance of general organic resins, it is not suitable for use in high temperature applications, so the high temperature resistance of the final zinc-based micro-coating also needs to be improved
Furthermore, because the thickness of the organic coating is thicker, the thickness of the final zinc-based micro-coating is also thicker, which is not suitable for surface treatment of small standard parts such as screws and nuts. The strength, high temperature resistance, and coating thickness need to be improved, and the smell is strong, and there are certain safety hazards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne sealing agent for zinc-based micro coating and preparation method of waterborne sealing agent
  • Waterborne sealing agent for zinc-based micro coating and preparation method of waterborne sealing agent
  • Waterborne sealing agent for zinc-based micro coating and preparation method of waterborne sealing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] The water-based sealing agent for zinc-based micro-coating of the present invention, its raw material is composed of components with the following mass percentages: 2% to 10% of silane coupling agent, 1% to 5% of titanate coupling agent , 20%~40% silicate, 3%~5% organic solvent, 0.1%~0.5% C13 carbonyl isomer alcohol ethoxylate surfactant, 10~30% fluorocarbon polymer powder or Fluorocarbon polymer emulsion and the balance of deionized water, the particle size of the fluorocarbon polymer micropowder is 10-20 microns, and the above raw materials can be purchased in the market.

[0015] The organic solvent of the present invention is an alcohol organic solvent, and the alcohol organic solvent adopts one or both of ethanol, butanol, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol or tripropylene glycol. More than one mixed alcohol, the mass percentage is not limited when mixing, and the storage stability of the water-based sealing...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterborne sealing agent for a zinc-based micro coating and a preparation method of the waterborne sealing agent. The raw materials of the waterborne sealing agent are composed of the following components in percentage by mass: 2-10% of silane coupling agent, 1-5% of titanate coupling agent, 20-40% of silicate, 3-5% of organic solvent, 0.1-0.5% of C13 carbonyl isomeric alcohol ethoxylate surfactant, 10-30% of fluorocarbon polymer micropowder or fluorocarbon polymer emulsion and the balance of deionized water. The waterborne sealing agent has the characteristics of environment friendliness, safety and capability of improving the adhesive force, hardness, acid and alkaline resistance and high temperature resistance of the zinc-based micro coating and reducing the friction and torque coefficients.

Description

technical field [0001] The invention relates to a water-based sealing agent for zinc-based micro-coatings and a preparation method thereof, belonging to the technical field of post-treatment of metal zinc-based micro-coatings. Background technique [0002] Traditional metals, especially steel, cast iron and their alloys, zinc-based micro-coating treatment processes include electro-galvanizing, Dacromet, and Jiaomet, among which Dacromet and Jiaomet are the main zinc-based micro-coating treatments. host. Dacromet and Jiaomet are the process of forming a flake zinc-based coating on the metal surface by physical and chemical methods. The formed coating is called Dacromet and Jiaomet, also known as zinc-based micro-coating. The purpose is mainly to provide protection for the base metal and prevent the metal from being corroded to a large extent; it can significantly improve the neutral salt spray resistance of the metal. However, the coating is not scratch-resistant, has low h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/83
CPCC23C2222/20
Inventor 蔡继斌张建国
Owner JIANGSU BOYE COATING ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com