Manufacturing method of fluorine plastic sleeve

A manufacturing method, the technology of fluoroplastics, applied in the field of polymer materials, can solve the problems of unsatisfactory temperature resistance, wear resistance, flexibility, comfort, and lifespan decline, etc., to ensure flexibility, comfort and long-term creep resistance Fatigue, overcoming creep and wear resistance, and improving the service life

Inactive Publication Date: 2013-05-15
SHANGHAI CHANGYUAN ELECTRONICS MATERIAL +1
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The patent number is CN200810042889.4 "Abrasion Resistant Fluoroplastic Sleeve". At present, its technology has been promoted in the lining pipe of the automobile gear shifting system, but due to the added wear resistance modifier polyoxymethylene (POM) ),) (polyimide) PI, (polyphenylene sulfide) PPS and other materials are not ideal in temperature resistance, wear resistance, and their composite properties with PTFE materials, which must be matched when the automobile shift system is assembled Lubricant (silicon ester paste) use
[0007] With the development of the cable liner of the automobile shifting system, some defects in the existing wear-resistant fluoroplastic bushing technology have also emerged. The general wear-resistant fluoroplastic In the environment, when the lubricant (silicon ester paste) in the automobile shifting system is lost or the working environment is not added or lacks the lubricant (silicon ester paste), the flexibility, comfort and life of the automobile shifting system will also decrease. drop with it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of fluorine plastic sleeve

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to make the purpose and features of the present invention more comprehensible, the specific implementation manners of the present invention will be further described below in conjunction with the accompanying drawings.

[0022] The fluoroplastic provided by an embodiment of the present invention is prepared from the following materials in the attached parts by weight: 100 parts of polytetrafluoroethylene dispersion resin (PTFE dispersion resin); 3-15 parts of polyamide-imide resin (PAI resin) parts; auxiliary oil 20-25 parts.

[0023] In the embodiment of the present invention, the particle size of the ethylene dispersion resin is 400-650 μm, the apparent density is 400-500 g / l, and the extrusion force RR1600=30-50 MPa.

[0024] Preferably, the ethylene dispersion resin has a particle size of 400 μm, an apparent density of 500 g / l, and an extrusion force of RR1600=30MP.

[0025] In the embodiment of the present invention, the particle size of the polyamide-imi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a fluorine plastic sleeve. The method comprises the following steps: mixing 100 parts of polytetrafluoroethylene dispersion resins, 3 to 15 parts of polyamide-imide resins and 20 to 25 parts of assistant oil by weight; aging the mixed material; taking out the aged material, prefabricating and forming; forming the prefabricated and formed material in a pushing and squeezing manner; volatilizing the sleeve material, formed in a pushing and squeezing manner, to remove the assistant oil; and sintering the sleeve material to obtain the fluorine plastic sleeve. According to the fluorine plastic sleeve produced by utilizing the manufacturing method, the low friction coefficient and the self-lubricating characteristic of fluorine plastic are maintained to a maximum extent; and the defects of the fluorine plastic which is easy to creep and poor in abrasion resistance is overcome. Therefore, the fluorine plastic sleeve has the best balance characteristic of self lubrication and abrasion resistance.

Description

technical field [0001] The invention relates to the technical field of polymer materials, and in particular to a method for manufacturing a fluoroplastic sleeve. Background technique [0002] Fluoroplastics have excellent material properties, such as high and low temperature resistance, corrosion resistance, good electrical insulation, non-adhesive properties, etc., and were first used in high-tech military fields such as aviation and aerospace. As its use becomes more and more extensive, it is also widely used in various parts of the car. Because fluoroplastics have excellent resistance to special environmental conditions, low friction, and self-lubricating properties, a polytetrafluoroethylene (PTFE) sleeve has been used in the cable liner of the automotive gear shift system to make gear shifting easier. Flexible and comfortable, it has gradually replaced the traditional lining pipes of high-density polyethylene (HDPE), polypropylene (PP), polyoxymethylene (POM), polybuty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08L79/08C08K5/01B29D23/00
Inventor 聂云宋冠军许兰杭
Owner SHANGHAI CHANGYUAN ELECTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com