Paste solder for hard soldering of SiCp/Al composite material and preparation method and use method thereof

A technology of paste solder and alloy solder, which is applied in the direction of manufacturing tools, welding equipment, metal processing equipment, etc., can solve the problem that strip-shaped or foil-shaped solder is unfavorable to the automation of the brazing process and is not suitable for irregular welding , small or geometrically complex parts, etc., to achieve the effect of facilitating automation, increasing the number of surface atoms, and increasing the specific surface area

Inactive Publication Date: 2014-12-03
HENAN POLYTECHNIC UNIV +2
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem that the existing strip-shaped or foil-shaped solder is not conducive to the automation of the brazing process, and is not suitable for welding irregular, small or geometrically complex parts, and provides a paste Brazing filler metal and its preparation method and use method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paste solder for hard soldering of SiCp/Al composite material and preparation method and use method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Specific embodiment one: present embodiment is a kind of paste solder used for brazing of SiCp / Al composite material by mass percentage by 30%~35% alloy solder powder, 35%~40% flux and 25% to 35% binder is mixed.

[0020] The alloy solder powder described in this embodiment is composed of 21% to 25% of Cu, 4% to 6% of Si, 1% to 2% of Mg, 0.3% to 0.7% of Ni and 66% to 74% by mass percentage. % Al prepared.

[0021] The flux described in this embodiment is KF-AlF 3 Eutectic aluminum flux is added K 2 SiF 6 Mixed as a surfactant, wherein the KF-AlF 3 Eutectic aluminum flux with K 2 SiF 6 The mass ratio is 1:(0.074~0.131).

[0022] The binder described in this embodiment is prepared by mixing 85% to 90% of white oil, 6% to 10% of rosin resin, 2% to 5% of glycerin and 0.5% to 1.5% of hydrogenated castor oil according to the mass percentage. become.

[0023] The brazing alloy powder in this embodiment has a particle size of 5 μm to 25 μm.

[0024] The viscosity of t...

specific Embodiment approach 2

[0030] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the white oil has a flash point of 180° C. to 190° C. and a viscosity of 3.5 cp to 5 cp. Others are the same as the first embodiment.

specific Embodiment approach 3

[0031] Specific embodiment three: the present embodiment is a kind of preparation method for the paste solder of SiCp / Al composite material brazing, specifically is finished according to the following steps:

[0032] 1. Preparation of alloy solder powder: ① Preparation of materials: Firstly, cut or crush the raw materials containing Cu, Si, Mg, Ni and Al to a particle size of 5mm-20mm, and then put them into alcohol for ultrasonication Clean for 15min to 25min, and then prepare materials according to the mass percentage of 21% to 25% of Cu, 4% to 6% of Si, 1% to 2% of Mg, 0.3% to 0.7% of Ni and 66% to 74% of Al ; ② Nitrogen atomization: put the materials prepared in step ① into an intermediate frequency induction furnace for melting, and smelt them in a vacuum of 0.5×10 -3 Pa~1.5×10 -3 Pa and heating rate of 40°C / min~60°C / min are melted into molten metal, and then the molten metal is passed through the annular nozzle. mm, and the annular seam gap of the annular seam nozzle i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
flash pointaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a paste solder for the hard soldering of a SiCp / Al composite material and a preparation method and use method thereof, and relates to a solder for the hard soldering of the SiCp / Al composite material and a preparation method and use method thereof. The paste solder for the hard soldering of the SiCp / Al composite material aims at the problem that the traditional strip-shaped solder or foil-shaped solder is adverse to the automation in a hard soldering process and is not suitable to weld an irregular, small-sized or geometrical complicated part. The paste solder for the hard soldering of the SiCp / Al composite material is prepared by mixing solder alloy powder, a soldering flux and an adhesive. The preparation method comprises the following steps of: 1, preparing the solder alloy powder; 2, preparing the soldering flux; 3, preparing the adhesive; and 4, mixing to prepare the hard soldering of the paste solder for the SiCp / Al composite material. The use method comprises the following steps of: adopting coating type cloth or needle tube type cloth; and then carrying out vacuum heating treatment so as to complete welding. The preparation method disclosed by the invention is mainly used for preparing the paste solder for the hard soldering of the SiCp / Al composite material.

Description

technical field [0001] The invention relates to a brazing filler metal for SiCp / Al composite material brazing, a preparation method and a use method thereof. Background technique [0002] SiCp / Al composite material has the advantages of high specific strength, high specific modulus, high temperature resistance, corrosion resistance, wear resistance, good electrical and thermal conductivity, and small linear expansion coefficient. It has broad application prospects in fields such as chemical industry and chemical industry, but its poor weldability has become a "bottleneck" technical problem for popularization and application. Brazing is one of the ideal effective connection methods. However, the brazing filler metals currently used for brazing SiC particle-reinforced aluminum matrix composites are mostly in the form of strips and foils, which are not conducive to the automation of the brazing process, especially not suitable for irregular and small Or use on parts with comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/28B23K35/363B23K1/008B23K1/19B23K1/20
Inventor 牛济泰王鹏杨顺成徐冬霞李强
Owner HENAN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com