Environmental-friendly termite-resistant cable sheath insulating material and method for preparing same
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of cable sheathing and insulating materials, applied in the direction of insulated conductors, insulated cables, rubber insulators, etc., can solve compatibility, low temperature resistance, compression set resistance, heat aging performance reduction, low tear resistance, water resistance low shrinkage, excellent physical properties, and good compactness
Inactive Publication Date: 2013-03-27
安徽文峰电子科技集团有限公司
View PDF3 Cites 15 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
With the increase of chlorine content, the compatibility of plasticizer, low temperature resistance, compression set resistance, thermal aging performance, etc. decrease, and the water resistance is poor. When the temperature is relatively low, the material itself is relatively hard, low in elasticity and brittle. Large, low tear resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] An environmentally friendly and termite-proof cable sheath insulation material, which is composed of the following raw materials in parts by weight (kg):
[0019] The preparation method of the modified calcium carbonate is as follows: mix quicklime and boiled water at a mass ratio of 1:10, digest for 5 hours, filter and remove slag through a 180 μm resonance sieve, and then further remove slag through a hydrocyclone to obtain Ca(OH) 2 Suspension, in Ca(O...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
elongation at break
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an environmentally-friendly termite-resistant cable sheath insulating material and a preparation method thereof. The material is prepared from the following raw materials in parts by weight: 90-97 parts of chloroprene rubber (CR) 121, 15-21 parts of chlorinated polyethylene, 15-22 parts of semi-reinforcing purpose furnace black N774, 2-3 parts of magnesium oxide, 2-5 parts of glass powder, 30-35 parts of barite powder, 1-2 of anti-aging agent MB, 1-2 of N-(beta-aminoethyl)-gamma-3-aminopropyltrimethoxysilane, 0.9-1.4 of poly(1, 2-propylene glycol adipate, 5-77 parts of dioctyl maleate, 1-2 parts of accelerator DM, 0.8-1 part of dibasic lead phosphite, 12-18.4 parts of hydrotalcite, 1-3 parts of 4, 4'-oxybis(benzenesulfonyl hydrazide), 2-4 parts of antioxidant DSTP, 4-6 parts of glass powder, 0.8-1 part of zinc oxide, 2-3 parts of modified calcium carbonate, 5-6 parts of antimony oxide, 3-5 parts of ethylene thiourea and 0.8-1 part of modified bentonite. The produced environmentally-friendly termite-resistant cable sheath insulating material has excellent physical performance, stable dimensions and low shrinkage factor, and the tensile strength, tear resistance and elastic force performance of a product are all greatly improved.
Description
technical field [0001] The invention mainly relates to a rubber sheath material and a preparation method thereof, in particular to an environment-friendly termite-proof cable sheath insulation material and a preparation method thereof. Background technique [0002] At present, the main materials commonly used in China as cable sheaths are neoprene, chlorosulfonated polyethylene rubber, etc., and the structural components of each material are different and their properties are also different. Chlorinated polyethylene compound is a kind of saturated chlorine-containing rubber, which partially retains the properties of polyethylene, and its elasticity and thermal stability decrease, and the substance becomes a semi-rigid material and loses its elasticity. With the increase of chlorine content, the compatibility of plasticizer, low temperature resistance, compression set resistance, thermal aging performance, etc. decrease, and the water resistance is poor. When the temperature ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.