Iron and nitrogen doped carbon black catalyst and preparation method thereof

A catalyst and co-doping technology, used in chemical instruments and methods, physical/chemical process catalysts, chemical/physical processes, etc., can solve the problems of complex preparation methods and high equipment requirements, and achieve broad application prospects and high oxygen reduction activity. , the effect of promoting the commercialization process

Active Publication Date: 2013-03-20
CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
View PDF4 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention solves the technical problem that the preparation method of the carbon-supported oxygen reduction catalyst is complex and requires high equipment in the prior art, and provides an iron-nitrogen co-doped with a simple preparation method and high oxygen reduction activity Carbon black catalyst and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron and nitrogen doped carbon black catalyst and preparation method thereof
  • Iron and nitrogen doped carbon black catalyst and preparation method thereof
  • Iron and nitrogen doped carbon black catalyst and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Put 0.1g of Black Pearl 2000 (hereinafter referred to as BP 2000) and 0.5g of melamine into a high-speed shimmy ball mill (Nanjing Yifan, model GM-3B), and high-speed ball mill for 4 hours. After the temperature of the ball mill tank dropped to room temperature, the obtained mixed powder containing carbon, nitrogen and iron was placed in a single-temperature zone slide rail furnace, and heated at 1.01×10 5 pa, high temperature treatment at 900°C for 1 hour to obtain iron and nitrogen co-doped carbon black catalyst. After the temperature drops to room temperature, take it out and set aside. Measured by ICP: the ratio of carbon, nitrogen and iron atoms is 10:1:0.5.

[0040]Add 5 mg of the above-prepared iron-nitrogen co-doped carbon black catalyst to 100 μL of Nafion solution with a mass concentration of 5%, and ultrasonically disperse for 30 min to obtain a solution; 10 μL of the solution is drip-coated on a rotating disk electrode, and dried at room temperature Finall...

Embodiment 2

[0044] Put 0.1g of BP 2000 and 1g of melamine into a high-speed pendulum-type ball mill (Nanjing Yifan, model GM-3B), and perform high-speed ball milling for 4 hours. After the temperature of the ball mill tank dropped to room temperature, the obtained mixed powder containing carbon, nitrogen and iron was placed in a single-temperature zone slide rail furnace, and heated at 1.01×10 5 pa, high temperature treatment at 900°C for 1 hour to obtain iron and nitrogen co-doped carbon black catalyst. After the temperature drops to room temperature, take it out and set aside. Measured by ICP: The ratio of carbon, nitrogen and iron atoms is 10:3:1.

[0045] Add 5 mg of the above-prepared iron-nitrogen co-doped carbon black catalyst to 100 μL of Nafion solution with a mass concentration of 5%, and ultrasonically disperse for 30 min to obtain a solution; 10 μL of the solution is drip-coated on a rotating disk electrode, and dried at room temperature Finally, the thin film electrode is o...

Embodiment 3

[0049] Put 0.1g of BP 2000 and 2g of melamine into a high-speed pendulum-type ball mill (Nanjing Yifan, model GM-3B), and perform high-speed ball milling for 7 hours. After the temperature of the ball mill tank dropped to room temperature, the obtained mixed powder containing carbon, nitrogen and iron was placed in a single-temperature zone slide rail furnace, and heated at 1.01×10 5 pa, high temperature treatment at 900°C for 5 hours to obtain iron and nitrogen co-doped carbon black catalyst. After the temperature drops to room temperature, take it out and set aside. Measured by ICP: The ratio of carbon, nitrogen and iron atoms is 10:5:1.

[0050] Add 5 mg of the above-prepared iron-nitrogen co-doped carbon black catalyst to 100 μL of Nafion solution with a mass concentration of 5%, and ultrasonically disperse for 30 min to obtain a solution; 10 μL of the solution is drip-coated on a glassy carbon electrode, and after drying at room temperature , to obtain a thin-film elect...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an iron and nitrogen doped carbon black catalyst and a preparation method of the iron and nitrogen doped carbon black catalyst, and solves the technical problems that the preparation method of an oxygen reduction catalyst with carbon as the carrier is complex, and requirements for devices are high. The catalyst of the invention is prepared in the following processes: carbon blacks are mixed with melamine evenly through ball milling technique; and the mixed material is doped with iron atoms due to the use of ball milling technique, the iron atoms and nitrogen atoms are enabled to be doped into a stratified structure of the carbon blacks after a high-temperature treatment, and the iron and nitrogen doped carbon black catalyst is formed. The catalyst is very high in oxygen reduction activity, much higher than platinum base catalysts in oxygen reduction initial potential and half wave potential, and higher than the prior oxygen reduction catalyst with the carbon as the carrier in oxygen reduction activity. The preparation method of the iron and nitrogen doped carbon black catalyst is simple, practical, and low in cost. Therefore, the oxygen reduction catalyst is suitable for being used to prepare fuel cells.

Description

technical field [0001] The invention relates to the technical field of fuel cells, in particular to an iron and nitrogen co-doped carbon black catalyst and a preparation method thereof. Background technique [0002] Fuel cells, such as proton exchange membrane fuel cells and direct methanol fuel cells, are widely used in electric vehicle power sources, mobile power sources, and micro power sources due to their advantages such as environmental friendliness, quick start, no electrolyte loss, long life, high power density and energy density. and small power generation devices have shown broad application prospects. For fuel cells, the oxygen reduction reaction at the cathode is the rate-determining step of the electrocatalytic reaction of the fuel cell. To increase the speed of the cathode oxygen reduction reaction, an oxygen reduction catalyst must be used. At present, carbon-supported platinum and platinum alloy catalysts are the most widely used fuel cell oxygen reduction ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J27/24H01M4/90H01M4/88
CPCY02E60/50
Inventor 徐维林孙秀娟刘京
Owner CHANGZHOU INST OF ENERGY STORAGE MATERIALS &DEVICES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com