High-temperature-resistant weatherproof fireproof chlorinated polyvinyl chloride (CPVC) corrugated board with low heat conductivity, and preparation method of chlorinated polyvinyl chloride (CPVC) corrugated board

A technology of chlorinated polyvinyl chloride and low thermal conductivity, which is applied in the field of corrugated board, can solve the problems of uneven stress distribution, high processing difficulty, and high molding difficulty, and achieve the effects of enhanced fluidity, reduced processing difficulty, and easy molding

Active Publication Date: 2015-05-13
山东高信化学股份有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high viscosity and poor fluidity of the traditional CPVC melt, the processing difficulty is too high, that is, the forming difficulty is high, so that when CPVC is made into corrugated boards, there will be obvious quality defects on the raised corrugations: thickness Uneven, uneven stress distribution, brittle, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant weatherproof fireproof chlorinated polyvinyl chloride (CPVC) corrugated board with low heat conductivity, and preparation method of chlorinated polyvinyl chloride (CPVC) corrugated board
  • High-temperature-resistant weatherproof fireproof chlorinated polyvinyl chloride (CPVC) corrugated board with low heat conductivity, and preparation method of chlorinated polyvinyl chloride (CPVC) corrugated board
  • High-temperature-resistant weatherproof fireproof chlorinated polyvinyl chloride (CPVC) corrugated board with low heat conductivity, and preparation method of chlorinated polyvinyl chloride (CPVC) corrugated board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A chlorinated polyvinyl chloride corrugated board with high temperature resistance, weather resistance, fire prevention and low thermal conductivity, which is prepared from the following raw materials in parts by weight:

[0030]

[0031] Wherein, the anti-impact additive is a mixture of ACM and CPE; the processing aid is ACR; the filler is calcium carbonate; the lubricant is calcium stearate.

[0032] The preparation method is as follows:

[0033] (1) Thermally mix the raw materials, add the raw materials to a 1000r / min high-speed mixer and mix for 10 minutes or until the temperature reaches 115°C, then put the mixed materials into a 500r / min cold mixer with a cold water jacket, Fully cool down to 60°C;

[0034] (2) Release the mixed materials to the trough, spread them out and place them at room temperature for 20 hours;

[0035] (3) Put the placed material into the upper hopper of the extruder through the screw conveyor and enter the extrusion process. The barre...

Embodiment 2

[0039] A chlorinated polyvinyl chloride corrugated board with high temperature resistance, weather resistance, fire prevention and low thermal conductivity, which is prepared from the following raw materials in parts by weight:

[0040]

[0041] Wherein, ACM is used as the anti-impact additive; ACR is used as the processing aid; calcium carbonate is used as the filler; OPE is used as the lubricant.

[0042] The preparation method is as follows:

[0043] (1) Thermally mix the raw materials, add the raw materials to a 1100r / min high-speed mixer and mix for 10 minutes, or mix until the temperature reaches 115°C, and then put the mixed materials into a 600r / min cold mixer with a cold water jacket , fully cool down to 65°C;

[0044] (2) Release the mixed materials to the trough, spread them out and place them at room temperature for 24 hours;

[0045] (3) Put the placed material into the upper hopper of the extruder through the screw conveyor and enter the extrusion process. T...

Embodiment 3

[0049] A chlorinated polyvinyl chloride corrugated board with high temperature resistance, weather resistance, fire prevention and low thermal conductivity is prepared from the following raw materials in parts by weight:

[0050]

[0051]Wherein, the anti-impact additive is CPE; the processing aid is ACR; the filler is calcium carbonate; and the lubricant is glyceryl stearate.

[0052] The preparation method is as follows:

[0053] (1) Thermally mix the raw materials, add the raw materials to a 1200r / min high-speed mixer and mix for 10 minutes, or mix until the temperature reaches 115°C, and then put the heated material into a 700r / min cold mixer with a cold water jacket , fully cool down to 65°C;

[0054] (2) Release the mixed materials to the trough, spread them out and place them at room temperature for 28 hours;

[0055] (3) Put the placed material into the upper hopper of the extruder through the screw conveyor and enter the extrusion process. The barrel of the extru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Vicat softening pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
Vicat softening pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature-resistant weatherproof fireproof chlorinated polyvinyl chloride (CPVC) corrugated board with low heat conductivity, and a preparation method of the chlorinated polyvinyl chloride (CPVC) corrugated board. The corrugated board is prepared from the following raw materials by weight: 10-60 parts of CPVC resin, 30-70 parts of PVC (polyvinyl chloride) resin, 1-8 parts of composite lead salt stabilizer, 1-4 parts of processing aids, 8-12 parts of anti-impact aids, 25-75 parts of filler, 1.5-4.5 parts of lubricant, and a reasonable amount of colorant. The corrugated board has the advantages of high mechanical strength, excellent weatherability, high aging resistance and chemical stability and the like, and the formed raised corrugated board has higher thickness uniformity and uniform stress distribution, thereby being not easy to break due to stress concentration.

Description

technical field [0001] The invention relates to a corrugated board, in particular to a chlorinated polyvinyl chloride corrugated board with high temperature resistance, weather resistance, fire prevention and low thermal conductivity and a preparation method thereof. Background technique [0002] At present, most of the materials of color steel corrugated boards are steel, which will corrode and rust after a period of use, and color steel tiles are easily corroded by acidic substances. In hot weather, when the sun is exposed to the sun, the heat conduction and heat absorption are fast, so the heat insulation effect is poor; the noise is also louder when it rains. [0003] Due to the high hardness and mechanical properties of PVC boards, there are also many PVC corrugated boards. However, the hardness and mechanical properties of PVC board will decrease with the increase of temperature. Its thermal deformation temperature is low, it is easy to bend and deform when exposed to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L27/24C08L23/28C08L33/04C08L23/06C08L51/00C08L23/30C08K13/02C08K3/26C08K5/098C08K5/103B29C47/00
Inventor 肖斌王曙光金胜波刘春山任可敬庄奇大凌玉英杜方爱田瑞霞
Owner 山东高信化学股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products