A preparation method of construction waste recycled artificial landscape stone
A construction waste and landscape stone technology is applied in the field of construction waste recycling artificial landscape stone preparation to achieve the effects of advanced technology, mature technology and saving construction resources
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0021] A method for preparing artificial landscape stone regenerated from construction waste, characterized in that it comprises the following steps:
[0022] (1) Use channel steel or angle steel to make the bracket of the landscape stone, then use steel bars to make a skeleton according to the shape of the landscape stone and weld it to the outside of the bracket, and cover the skeleton with a layer of steel wire mesh substrate to form the keel of the landscape stone;
[0023] (2) After brushing the mold box with a layer of release agent, fix the processed landscape stone keel into the mold box;
[0024] (3) After adding water to the mixer, add recycled construction waste fine aggregate, recycled construction waste coarse aggregate, construction waste dust, Portland cement, artificial sand, and granite stones into the mixer and stir for 3-5 minutes, then pour into the mold;
[0025] (4) Put the poured mold box into the curing room for 10-20 days of initial curing at room temp...
Embodiment 1
[0032] Portland cement 25%, construction waste recycled fine aggregate 10%, construction waste recycled coarse aggregate 15%, construction waste dust 10%, artificial sand 15%, granite stone 20%, water 5%, unsaturated resin 5% Potassium octanoate accelerator or (cobalt naphthenate accelerator, cobalt isooctanoate accelerator, zinc isooctanoate accelerator, N,N-dimethylaniline accelerator, N,N-diethylaniline accelerator, vanadium phosphate accelerator agent). 0.5%, 0.3% blocked isocyanate curing agent or (m-phenylenediamine curing agent, m-xylylenediamine curing agent, diaminodiphenylmethane curing agent, diaminodiphenylsulfone curing agent), copper foil, other The prepared construction waste regenerated artificial landscape stone has a hardness of 98.5%.
Embodiment 2
[0034] Portland cement 20%, construction waste recycled fine aggregate 15%, construction waste recycled coarse aggregate 25%, construction waste dust 15%, artificial sand 10%, granite stone 10%, water 5%, unsaturated resin 5% Potassium octanoate accelerator or (cobalt naphthenate accelerator, cobalt isooctanoate accelerator, zinc isooctanoate accelerator, N,N-dimethylaniline accelerator, N,N-diethylaniline accelerator, vanadium phosphate accelerator agent). ) 0.5%, blocked isocyanate curing agent 0.3% or (m-phenylenediamine curing agent, m-xylylenediamine curing agent, diaminodiphenylmethane curing agent, diaminodiphenylsulfone curing agent), granite flakes ( 1-3mm in diameter and 0.1-0.5mm in thickness (the dosage is determined according to the overall volume of the actual marble), and the hardness of the artificial landscape stone regenerated from construction waste prepared by it is 98.8%.
PUM
Property | Measurement | Unit |
---|---|---|
hardness | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com