Biodegradable medical hydrogel and preparation method and application thereof

A biodegradable and hydrogel technology, which is applied in medical science, absorbent pads, surgery, etc., can solve the problems that cannot meet the requirements of gelation speed and degradation time, and achieve controllable performance, simple operation, and long degradation time. Effect

Inactive Publication Date: 2013-02-06
SAIKE SAISI BIOTECH CO LTD
View PDF19 Cites 58 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, hydrogel products with a single nucleophilic or electrophilic component cannot meet the requirements of different physical properties such as gelation speed and degradation time, and it is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable medical hydrogel and preparation method and application thereof
  • Biodegradable medical hydrogel and preparation method and application thereof
  • Biodegradable medical hydrogel and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0087] 2. Preparation and use of medical hydrogel

[0088] Method 1: a method for preparing the above-mentioned medical hydrogel by in-situ cross-linking forming hydrogel, which is realized by changing the pH value of the corresponding buffer solution.

[0089] The specific method is to dissolve the first component containing nucleophilic functional groups in buffer A with a pH of 7.5-12.5 (preferably 9.5-10.2) to obtain solution A, and dissolve the second component containing electrophilic functional groups in pH The solution B is obtained in the buffer B of 2.0-6.5 (preferably 3.9-6.0), and then the solution A and the solution B are mixed, and the first component and the second component undergo a cross-linking reaction to form a hydrogel.

[0090] Method 2: Another method for preparing the above-mentioned medical hydrogel by in-situ cross-linking forming hydrogel is to mix the first component containing the nucleophilic functional group and the second component containing t...

Embodiment 1

[0137] Embodiment 1, prepare hydrogel with single nucleophilic component and double nucleophilic component

[0138] In order to compare the properties of hydrogels prepared with a single nucleophilic (or electrophilic) component and a double nucleophilic (or electrophilic) component, this example uses a nucleophilic component (first component) hyperbranched polymer Ethyleneimine (PEI-1800, molecular weight 1800, structural repeating unit see Figure 7B , with a primary amino group content of 35%, purchased from Aladdin Reagent Company) and Tri-lysine (Tri-lys, purchased from Shanghai Gil Biochemical Reagent Company) as examples, compare the two alone with the electrophilic component (the second group points) Four-arm N-hydroxysuccinimide propionate-based polyethylene glycol (4-arm-PEG-SPA, molecular weight 10000), four-arm N-hydroxysuccinimide-succinate-based polyethylene glycol Diol (4-arm-PEG-SS, molecular weight 10000), four-arm N-hydroxysuccinimide glutarate-based polyethy...

Embodiment 2

[0149] Embodiment 2, changing the proportion of nucleophilic components to prepare hydrogel

[0150] The first component whose end group is a nucleophilic functional group is hyperbranched polyethyleneimine 1800 (PEI-1800, structural repeating unit see Figure 7B , molecular weight 1800, primary amino group content 35%, purchased from Aladdin Reagent Company), and / or four-arm mercapto polyethylene glycol (4-arm-PEG-SH, molecular weight 10000), and / or trilysine acid (Tri-lys, Shanghai Gil Biochemical Reagent Co.), and / or trilysine hydrochloride (Tri-lys-HCl), and / or two-arm aminopolyethylene glycol (2-arm-PEG-NH 2, with a molecular weight of 10000), the second component whose end group is an electrophilic functional group is four-arm N-hydroxysuccinimide glutarate-based polyethylene glycol (4-arm-PEG-SG, molecular weight 10000), The ratio of the nucleophilic components was changed (see Table 2 for the formula) to prepare the hydrogel and test its performance. The preparation me...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
breaking strengthaaaaaaaaaa
breaking strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a biodegradable medical hydrogel and a preparation method and application of the hydrogel, and particularly discloses a biodegradable medical hydrogel which is formed by in-situ crosslinking and shaping. The gelation time of the hydrogel is less than 20s, the swelling rate is 0-600%, the fracture strength is not less than 50mmHg, the time of beginning degradation is 3-40d and the degradation time is 7-180d. The raw materials for preparing the hydrogel comprise a first compound component containing a nucleophilic functional group and a second compound component containing an electrophilic functional group, and the two components are physically mixed by a mixing tool and subjected to covalent crosslinking to form the hydrogel. The physical property and biodegradability of the hydrogel can be adjusted by changing the ratio of compound components of the first component or the second component; and the hydrogel is controllable in performance and simple to operate, and can be used for organism environments of different parts.

Description

Technical field [0001] The invention belongs to the field of biodegradable polymer materials, and in particular relates to an in-situ cross-linked biodegradable medical hydrogel and its preparation method and application. Background technique [0002] As a biocompatible material, hydrogel is mainly used in medicine to prevent adhesion after surgery, as a hemostatic agent, to fill defective tissue, to prevent tissue fluid leakage, and to sustain the release of drugs. There are many types of hydrogels, such as thermosensitive gels, which mainly generate gels at body temperature and turn into fluids at a certain temperature below body temperature; photosensitive gels, which mainly generate gels under short-term exposure to visible light or ultraviolet light. Cross-linking polymerizes to form a gel. [0003] Most of the hydrogels commonly used in medicine are acrylamide products, but these products often contain monomer residues, and it is very difficult to remove the residual ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/00C08L79/02C08K5/20C08J3/24C08J3/075A61L31/04A61L31/06A61L31/14A61L15/42A61L15/20A61L15/24A61L15/26
Inventor 董芳芳赵成如侯昭升邓凤娟李然李烨白云峰孔凡照李学刚
Owner SAIKE SAISI BIOTECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com