Preparation method and application of internal-external dual cross-linked core-shell structured acrylic acid emulsion

A technology of acrylic emulsion and core-shell structure, applied in the field of polymer material synthesis, can solve the problems of difficulty in solving hardness and minimum film-forming temperature, development and application limitations, loss of water-based paint, etc., to achieve VOC emission and improve densification the effect of lowering the glass transition temperature

Inactive Publication Date: 2014-07-16
SOUTH CHINA UNIV OF TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, there are also disadvantages such as poor film-forming property, solvent resistance, hot stickiness and cold brittleness.
Although there are many modification measures, such as silicone self-crosslinking modified acrylic emulsion, design of core-shell structure and preparation of acrylic microemulsion, it is difficult to solve the contradiction between hardness and minimum film-forming temperature. Adding too much film-forming aid will greatly increase the content of volatile organic compounds, making it lose the meaning of water-based paint, so the development and application of acrylic emulsion are limited to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of internal-external dual cross-linked core-shell structured acrylic acid emulsion
  • Preparation method and application of internal-external dual cross-linked core-shell structured acrylic acid emulsion
  • Preparation method and application of internal-external dual cross-linked core-shell structured acrylic acid emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Preparation of seed monomer: Mix 4 parts by mass of butyl acrylate, 2 parts by mass of methyl methacrylate, 0.1 part by mass of methacrylic acid, and 0.18 parts by mass of trimethylolpropane trimethacrylate to obtain a seed monomer body;

[0037] (2) Preparation of seed emulsion: Take 1.28 parts by mass of compound emulsifier, 0.06 parts by mass of potassium persulfate, dissolve in 60 parts by mass of deionized water, stir well and add to Put the funnel in a four-necked flask and place it in a constant temperature water bath, heat it to 80°C at a speed of 300 rpm, then reduce the speed to 200rmp, and pass the seed monomer through a constant pressure dropping funnel within 10 minutes Add it dropwise into a four-necked flask, and keep it warm for 15 minutes until there is no obvious reflux on the bottle wall to obtain a seed emulsion; the composite emulsifier is composed of 0.96 parts by mass of DSB and 0.32 parts by mass of OP-10;

[0038](3) Preparation of core lay...

Embodiment 2

[0041] (1) Preparation of seed monomers: Mix 8 parts by mass of butyl acrylate, 5.6 parts by mass of methyl methacrylate, 0.5 parts by mass of methacrylic acid, and 0.75 parts by mass of ethylene glycol dimethacrylate to obtain seed monomers;

[0042] (2) Preparation of seed emulsion: Take 1.7 parts by mass of compound emulsifier, 0.16 parts by mass of ammonium persulfate, dissolve in 80 parts by mass of deionized water, stir well and add to funnel in a four-necked flask, and placed in a constant temperature water bath, heated to 85 °C at a speed of 400 rpm, then reduced to 160 rpm, and the seed monomer was passed through a constant pressure dropping funnel in the Drop it into a four-neck flask within 15 minutes, and keep it warm for 20 minutes until there is no obvious reflux on the bottle wall to obtain a seed emulsion; the composite emulsifier consists of 0.85 parts by mass of DSB and 0.85 parts by mass of OP-10;

[0043] (3) Preparation of core layer emulsion: Take 72 part...

Embodiment 3

[0046] (1) Preparation of seed monomers: 6.15 parts by mass of butyl acrylate, 2.76 parts by mass of methyl methacrylate, 0.24 parts by mass of methacrylic acid, and 0.4 parts by mass of dipentaerythritol acrylate were uniformly mixed to obtain seed monomers;

[0047] (2) Preparation of seed emulsion: Take 1.5 parts by mass of compound emulsifier, 0.09 parts by mass of ammonium persulfate, dissolve in 80 parts by mass of deionized water, stir well and add to funnel in a four-necked flask, and placed in a constant temperature water bath, heated to 75°C at a speed of 400 rpm, then reduced to 220 rpm, and the seed monomer passed through a constant pressure dropping funnel in Drop it into a four-neck flask within 12 minutes, and keep it warm for 15 minutes until the bottle wall has no obvious reflux to obtain a seed emulsion; the composite emulsifier consists of 0.375 parts by mass of DSB and 1.125 parts by mass of OP-10;

[0048] (3) Preparation of core layer emulsion: Take 55.35...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method and application of an internally and externally cross-linked core-shell structure acrylic emulsion. The present invention adopts a multi-step seed emulsion pre-emulsification polymerization method to prepare an acrylic emulsion, which mainly includes preparing a seed monomer, seed emulsion polymerization, and core layer emulsion. There are four steps of polymerization and shell emulsion polymerization. After the polymerization is completed, the pH value of the emulsion is adjusted, and adipic acid dihydrazide is added to obtain an acrylic emulsion with an internal and external double cross-linked core-shell structure. The polymerization stability and the minimum film-forming temperature of the core-shell structure acrylic emulsion prepared by the present invention are greatly improved, and are applied in the field of water-based wood lacquer, while improving the cross-linking degree, density and hardness of the paint film, reducing the Water absorption and glass transition temperature of paint film.

Description

Technical field [0001] The present invention is a high -molecular material synthesis field, which involves emulsion aggregation technology, and specifically involves the preparation method and application of an internal and external dual cross -linking nuclear shell structure acrylic emulsion. Background technique [0002] Acrylic emulsion is a common name for the common cluster of various acrylic monomers. It is widely used in various industries, which is especially important in the wood paint industry. [0003] Wood paint not only has decorative beautification, but also has a protective effect on wood and can extend the service life of the wood. However, most of the wood paint sold in the Chinese market is still solvent.Seriously harm the health of production and construction personnel, and pollute the atmosphere.With the increasing awareness of people's environmental protection, the scope of the use of solvent -shaped coatings has become increasingly restricted, and water -bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/18C08F220/14C08F220/06C08F220/28C08F222/14C08F220/58C08F2/30C08F2/26C08F4/30C08K5/25C09D133/08
Inventor 黄洪张静谢德龙司徒粤
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com