Bowlder-imitated artificial stone plate and manufacturing method thereof

A technology of artificial slate and production method, applied in the field of imitation jade artificial slate and its production, can solve the problems of dirt infiltration into the plate, the artificial plate has pores, and the smoothness is not enough, and achieves bright colors, all thicknesses, and light transmission. strong effect

Inactive Publication Date: 2014-04-16
ZHOUSHAN OUPOSHI ENVIRONMENTAL PROTECTION TECH DEV
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its disadvantage is that the formula is unreasonable, the surface of the produced wood-based panel will have fine holes, and the smoothness is not enough
Therefore, dirt will penetrate into the board during use, which is prone to bacterial growth and is not easy to clean

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1, the imitation jade artificial stone slab of this embodiment, the formula of the imitation jade artificial stone slab is composed of: 28% of o-phthalic series unsaturated polyester resin, 71.64% of aluminum hydroxide, 0.03% of cobalt naphthenate, over 0.03% methyl ethyl ketone oxide, 0.3% pigment paste made by grinding saturated polyester resin and pigment powder with a particle size of less than 30 um, the above are mass percentages.

[0029] The manufacture method of imitation jade artificial stone slab of the present embodiment, the steps of described manufacture method are as follows:

[0030] 1. Prepare the materials according to the above formula;

[0031] 2. Wax the inner wall of the mold first, and set aside;

[0032] 3. Add cobalt naphthenate to the unsaturated polyester resin and stir evenly with a hand drill;

[0033] 4. Then add aluminum hydroxide and pigment paste, and then stir evenly;

[0034] 5. Add methyl ethyl ketone peroxide again, and...

Embodiment 2

[0038] Embodiment 2, the imitation jade artificial stone slab of this embodiment, the formula of the imitation jade artificial stone slab is composed of: 29% of unsaturated polyester resin of o-phthalic series, 70.64% of aluminum hydroxide, 0.03% of cobalt naphthenate, super 0.03% methyl ethyl ketone oxide, 0.3% pigment paste made by grinding saturated polyester resin and pigment powder with a particle size of less than 30 um, the above are mass percentages.

[0039] The manufacture method of imitation jade artificial stone slab of the present embodiment, the steps of described manufacture method are as follows:

[0040] 1. Prepare the materials according to the above formula;

[0041] 2. Wax the inner wall of the mold first, and set aside;

[0042] 3. Add cobalt naphthenate to the unsaturated polyester resin and stir evenly with a hand drill;

[0043] 4. Then add aluminum hydroxide and pigment paste, and then stir evenly;

[0044] 5. Add methyl ethyl ketone peroxide again,...

Embodiment 3

[0048]Embodiment three, the imitation jade artificial stone slab of this embodiment, the formula of the imitation jade artificial stone slab is composed of: 30% of unsaturated polyester resin of o-phthalic series, 69.86% of aluminum hydroxide, 0.02% of cobalt naphthenate, super 0.02% methyl ethyl ketone oxide, 0.1% pigment paste made by grinding saturated polyester resin and pigment powder with a particle size of less than 30um, the above are mass percentages.

[0049] The manufacture method of imitation jade artificial stone slab of the present embodiment, the steps of described manufacture method are as follows:

[0050] 1. Prepare the materials according to the above formula;

[0051] 2. Wax the inner wall of the mold first, and set aside;

[0052] 3. Add cobalt naphthenate to the unsaturated polyester resin and stir evenly with a hand drill;

[0053] 4. Then add aluminum hydroxide and pigment paste, and then stir evenly;

[0054] 5. Add methyl ethyl ketone peroxide agai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bowlder-imitated artificial stone plate and a manufacturing method thereof. The artificial stone plate comprises the following components in percentage by mass: 28-30% of unsaturated polyester resin, 40-65% of aluminum hydroxide, 5-30% of shells crushed into objects with diameters of 1-5 cm, 0.02-0.04% of cobalt naphthenate, 0.03-0.05% of methyl ethyl ketone peroxide and 1-2% of pigment paste. The bowlder-imitated artificial stone plate disclosed by the invention has the advantages that: the bowlder-imitated artificial stone plate is environmental-friendly, non-toxic and non-radiative; products are diversiform in color, bright in color and translucent; and the bowlder-imitated artificial stone plate can be produced according to various needs of customers, so that the stone plate is agile and changeable and convenient to decorate and collocate, thereby creating colorful life spaces. Compared with ceramic tiles, the product is light in weight and can be arbitrarily cut and processed; and the bowlder-imitated artificial stone plate has various thicknesses, so that the applicable range of the stone plate is wider than that of ceramic tiles in decoration. The production method disclosed by the invention is simple in process and safe and convenient in production, and a produced artificial stone plate has a smooth and non-porous surface, and a situation that dirt infiltrates into the plate does not occur in the process of application, so that the application of the artificial stone plate is cleaner and more sanitary.

Description

technical field [0001] The invention relates to the technical field of a jade-like artificial stone slab and a manufacturing method thereof. Background technique [0002] There are two main types of natural stone: marble and granite. Generally speaking, those with texture are called "marble"; those with spots are called "granite". In a narrow sense, marble refers to the stone produced in Dali, Yunnan. In fact, there are not many stones from Dali in all parts of the country. The two can also be distinguished from geological concepts. Granite is igneous rock, also called acid crystalline plutonic rock. It is the most widely distributed rock in igneous rock. It is composed of feldspar, quartz and mica, and the rock is hard and dense. Its composition is mainly silicon dioxide, accounting for about 65% to 75%. The so-called igneous rock is the rock formed by the condensation and crystallization of underground magma or lava from volcanoes. The content of silica in igneous ro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/18B28B1/087
Inventor 李铮标
Owner ZHOUSHAN OUPOSHI ENVIRONMENTAL PROTECTION TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com