Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Manufacturing method of whisker enhancement type fiberglass full thread roof bolt

A technology of glass fiber and manufacturing method, which is applied in the manufacturing field of whisker-reinforced glass fiber full-thread bolt, can solve the problems of poor surface finish, poor chemical stability, poor fatigue resistance, etc., and achieves improved appearance quality and extended service life , the effect of improving mechanical strength

Active Publication Date: 2012-11-14
HUAIBEI YUXIN NEW MATERIAL
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a whisker-reinforced glass fiber fully threaded anchor rod manufacturing method, which can solve the problem of poor surface finish of traditional glass fiber fully threaded anchor rods, serious equipment wear, poor toughness, poor fatigue resistance, chemical Disadvantages of poor stability, poor heat and humidity resistance and easy water absorption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 of the present invention: a method for manufacturing a whisker-reinforced glass fiber fully threaded anchor rod, the process includes the following steps:

[0035] Step a, yarn supply, the fiber yarn is divided into two parts, the inner yarn and the outer yarn, through the partition, and sent to the full-thread anchor forming device;

[0036] Step b, soaking liquid, adding potassium titanate whiskers to the resin and stirring evenly, the content of potassium titanate whiskers is 3% of the resin, and then immersing the fiber yarn of the inner yarn part into the resin with potassium titanate whiskers In the process, the fiber yarn of the inner yarn part is impregnated with the resin with potassium titanate whiskers;

[0037] Step c, heat forming, the fiber yarn of the outer yarn part and the fiber yarn of the inner yarn part impregnated with the resin with potassium titanate whiskers are pultruded and wound in the full-thread anchor forming device, and the fi...

Embodiment 2

[0042] Embodiment 2 of the present invention: a method for manufacturing a whisker-reinforced glass fiber fully threaded anchor rod, the process includes the following steps:

[0043] Step a, yarn supply, the fiber yarn is divided into two parts, the inner yarn and the outer yarn, through the partition, and sent to the full-thread anchor forming device;

[0044] Step b, immersion, adding zinc oxide whiskers to the resin and stirring evenly, the content of zinc oxide whiskers is 8% of the resin, then immersing the fiber yarn of the inner yarn part in the resin with zinc oxide whiskers, so that The fiber yarn of the inner yarn part is impregnated with resin with zinc oxide whiskers;

[0045] Step c, heat forming, the fiber yarn of the outer yarn part and the fiber yarn of the inner yarn part impregnated with the resin with zinc oxide whiskers are pultruded and wound in the fully threaded anchor forming device, and the fiber yarn is passed through the forming wire The thread sha...

Embodiment 3

[0050] Embodiment 3 of the present invention: a method for manufacturing a whisker-reinforced glass fiber fully threaded anchor rod, the process includes the following steps:

[0051] Step a, yarn supply, the fiber yarn is divided into two parts, the inner yarn and the outer yarn, through the partition, and sent to the full-thread anchor forming device;

[0052] Step b, soaking liquid, adding calcium sulfate whiskers in the resin and stirring evenly, the content of calcium sulfate whiskers is 15% of the resin, then immersing the fiber yarn of the inner yarn part in the resin with calcium sulfate whiskers, so that The fiber yarn of the inner yarn part is impregnated with resin with calcium sulfate whiskers;

[0053] Step c, heat forming, the fiber yarn of the outer yarn part and the fiber yarn of the inner yarn part filled with resin with calcium sulfate whiskers are pultruded and wound in the full-thread anchor forming device, and the fiber yarn is passed through the forming w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a whisker enhancement type fiberglass full thread roof bolt, wherein the technical process comprises the following steps: yarn supplying, resin pickup, hot briquetting, heat preservation, step cooling, dragging and cutting. The manufacturing method can overcome the defects that the traditional fiberglass full thread roof bolt has poor surface finishment, serious abrasion for equipment, poor toughness, poor fatigue resistance, poor chemical resistance, poor humidity resistance and is easy to absorb water.

Description

technical field [0001] The invention relates to a method for manufacturing a whisker-reinforced glass fiber fully threaded anchor rod. Background technique [0002] Fiber-reinforced plastic bolts have the advantages of high specific strength, good safety, corrosion resistance, strong designability, and convenient construction, and are mostly used for coal mine roadway support. With the development of science and technology, bolts are not only used in mines, but also in engineering technology, which can actively reinforce slopes, tunnels and dams. It is used more and more widely. [0003] However, due to the poor surface finish of the fiber reinforced plastic anchors currently on the market, there are many burrs on the surface of the anchors. If you do not wear gloves, it is easy to scratch your hands. wear and tear. Due to the immature formula of fiber-reinforced plastic bolts, the produced bolts have the disadvantages of poor toughness, poor fatigue resistance, poor chem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C53/58B29C53/84B29C70/52B29C70/54
Inventor 崔志军孙佰川耿琛松
Owner HUAIBEI YUXIN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com