High-strength steel sheet with yield strength of 1100MPa and manufacturing method thereof

A high-strength steel plate and yield strength technology, applied in the field of ultra-high-strength steel plates, can solve the problems of low-temperature impact energy of high-strength steel plates, etc., and achieve the effects of ultra-high strength, good welding performance, and low carbon equivalent

Active Publication Date: 2015-01-21
BAOSHAN IRON & STEEL CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The larger defect density is the source of micro-cracks, which can form micro-cracks under the action of force. The growth of micro-cracks makes the steel plate break rapidly along the grain boundary. Therefore, the low-temperature impact of high-strength steel plates with martensitic structure low power

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength steel sheet with yield strength of 1100MPa and manufacturing method thereof
  • High-strength steel sheet with yield strength of 1100MPa and manufacturing method thereof
  • High-strength steel sheet with yield strength of 1100MPa and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] Smelt in electric furnace or converter according to the chemical composition shown in Table 2, and cast into continuous casting slab or steel ingot, heat the continuous casting slab or steel ingot to 1050°C, start rolling at 1020°C, pass deformation rate is 5-30%, The final rolling temperature is 860°C, and the thickness of the finished steel plate is 8mm. Cool in air after rolling. The quenching heating temperature is 850°C. The tempering temperature is 350°C.

Embodiment 2

[0072] The implementation is the same as in Example 1, wherein the heating temperature is 1080°C, the rolling start temperature is 1060°C, the pass deformation rate is 5-30%, the final rolling temperature is 870°C, and the thickness of the finished steel plate is 10mm. Cool in air after rolling. The quenching heating temperature is 880°C. The tempering temperature is 320°C.

Embodiment 3

[0074] The implementation is the same as in Example 1, wherein the heating temperature is 1110°C, the rolling start temperature is 1100°C, the pass deformation rate is 5-30%, the final rolling temperature is 930°C, and the thickness of the finished steel plate is 12mm. Cool in air after rolling. The quenching heating temperature is 900°C. The tempering temperature is 280°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A high-strength steel sheet with yield strength of 1100MPa and a manufacturing method thereof. The high-strength steel sheet comprises, based on the weight percentage, 0.15-0.25% of C, 0.10-0.50% of Si, 0.60-1.20% of Mn, no more than 0.013% of P, no more than 0.003% of S, 0.20-0.55% of Cr, 0.20-0.70% of Mo, 0.60-2% of Ni, 0-0.07% of Nb, 0-0.07% of V, 0.0006-0.0025% of B, 0.01-0.08% of Al, 0.003-0.06% of Ti, no more than 0.00018% of H, no more than 0.0040% of N, no more than 0.0030% of O, and the balance of Fe and inevitable impurities; and the carbon equivalent CEQ is no more than 0.60%. A quenching and a tempering heat treatment are employed to obtain a tempered martensite tissue. The steel provided by the present invention has yield strength no less than 1100MPa, tensile strength no less than 1250MPa, Charpy ballistic work Akv (-40 DEG C) no less than 50J, and good strength and toughness.

Description

technical field [0001] The invention relates to an ultra-high-strength steel plate with good low-temperature toughness, in particular to a high-strength steel plate with a yield strength of 1100 MPa and a manufacturing method thereof. Background technique [0002] High-strength steel plates are used in coal mine machinery such as coal mine hydraulic supports, construction machinery such as crawler cranes, construction cranes and concrete pump trucks, and large marine floating cranes. Mechanical structures usually serve in heavy loads and complex environments, so high-strength steel plates for mechanical structures require high strength and good low-temperature toughness. At present, the high-strength steel plates involved in the European standard EN10025 and the national standard 16270 have a yield strength of up to 960MPa. At present, ultra-large construction machinery, such as large-tonnage crawler cranes and engineering cranes, all need to use steel plates with a yield s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/54C21D8/02C21D1/18
Inventor 赵四新姜洪生姚连登
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com