Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Environment-friendly solar cell back film

A solar cell, environmentally friendly technology, applied in circuits, photovoltaic power generation, electrical components, etc., can solve the problems of poor fluoropolymer layer compactness, short storage time of fluororesin solution, environmental pollution, etc., and achieves low performance requirements, reducing Pollution and personal injury, the effect of reducing corrosion

Active Publication Date: 2012-10-24
乐凯胶片股份有限公司
View PDF3 Cites 37 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the use of solvent-based fluororesin, there are disadvantages such as short storage time of fluororesin solution and environmental pollution; the fluoropolymer layer of the back plate has poor compactness and is easy to powder.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly solar cell back film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] 15 parts of polyvinylidene fluoride (manufactured by Aldrich),

[0043] 5 parts of amine modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0044] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0045] 7.5 parts of hydroxyl modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0046] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0047] 1.5 parts of polytetrafluoroethylene powder (made by Solvay solexis),

[0048] 40 parts of water,

[0049] 1 part of N-methylpyrrolidone (manufactured by Nanjing Ruize Fine Chemical Co., Ltd.),

[0050] Add 40 parts of water to a container equipped with a stirring device, add 1 part of cosolvent N-methylpyrrolidone to the water and stir evenly, then add 15 parts of polyvinylidene fluoride and 5 parts of amine modified polyvinylidene fluoride Ethylene-tetrafluoroethylene-hexafluoropropylene resin, 7.5 parts of hydroxyl-modified polyvinylidene fluoride-tetrafluoroethylen...

Embodiment 2

[0053] 35 parts of polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene,

[0054] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0055] 10 parts of carboxyl modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0056] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0057] 8 parts of hydroxyl modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0058] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0059] Acrylate polymer particles (made by Solvay solexis) 2.5 parts,

[0060] 70 parts of water,

[0061] 5 parts of dipropylene glycol methyl ether (manufactured by LyondellBasell),

[0062] Add 70 parts of deionized water into a container equipped with a stirring device, add 5 parts of co-solvent dipropylene glycol methyl ether into the water and stir evenly, then add 35 parts of polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene, 10 parts Carboxyl modified polyvinylidene fluoride...

Embodiment 3

[0065] Polyvinylidene fluoride-hexafluoropropylene (3M Dyneon) 30 parts,

[0066] 8 parts of aziridine modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0067] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0068] 12 parts of hydroxyl modified polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin,

[0069] (Made by Lucky Film Co., Ltd. of China Lucky Film Group)

[0070] 3 parts of polyamide pellets (made by Solvay solexis),

[0071] 40 parts of water,

[0072] 4 parts of propylene glycol butyl ether (manufactured by Dow Chemical),

[0073] Add 40 parts of water to a container equipped with a stirring device, add 4 parts of cosolvent propylene glycol butyl ether into the water and stir evenly, then change 30 parts of polyvinylidene fluoride-hexafluoropropylene and 8 parts of aziridine to Polyvinylidene fluoride-tetrafluoroethylene-hexafluoropropylene resin, 12 parts of hydroxyl-modified polyvinylidene fluoride-tetrafluoroethylene...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

An environment-friendly solar cell back film comprises a substrate, a fluorine-containing polymer layer and an adhesive layer, wherein the fluorine-containing polymer layer is obtained by coating waterborne fluororesin coating solution on the surface of the substrate by means of curing, and the waterborne fluororesin coating solution comprises, by weight, 15-35 parts of fluororesin, 5-10 parts of modified resin A, 6-12 parts of modified resin B, 0.5-3 parts of polymer filler, 40-70 parts of water and 1-5 parts of cosolvents, wherein the weight ratio of the modified resin A to the modified resin B is 1:0.8-1:1.5. The environment-friendly solar cell back film is environment-friendly, low in production cost, excellent in performance, high in peeling strength and good in water resistance and weather resistance.

Description

technical field [0001] The invention relates to the technical field of photovoltaic cells, in particular to a solar cell back film containing a water-based fluororesin coating. Background technique [0002] As a green alternative to traditional methods of electricity production, photovoltaic cell modules are used to generate electricity from the sun. Photovoltaic modules are assembled from various semiconductor element systems and must be protected to reduce the impact and damage of environmental effects such as moisture, oxygen and ultraviolet rays. Photovoltaic cell modules usually adopt a structure in which glass or plastic film protective layers are laminated on both sides of the silicon wafer. Due to its excellent strength, weather resistance, UV resistance and moisture resistance, it is made of fluoropolymer film and polyester (PET) film laminated backsheets play an important role in photovoltaic cell modules. [0003] The Chinese patent with application number 20071...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/16C09D127/18C09D127/20C09D127/22C09D7/12H01L31/048B32B27/06B32B27/30H01L31/049
CPCY02E10/50
Inventor 张学建杜彦飞李华锋李兴明董丽荣何彦达
Owner 乐凯胶片股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More