Preparing method of PTFE (polytetrafluoroethylene) composite material filled with nano particles

A technology of nanoparticles and composite materials, which is applied in the field of preparing high-performance nanoparticle-filled PTFE composite materials, which can solve the problems of lower than expected nanoparticle content, loss of nanoparticles, uneven mixing, etc., and achieve solvent recyclability and low pollution , the effect of high mechanical properties

Inactive Publication Date: 2012-07-25
ZHEJIANG UNIV
View PDF7 Cites 41 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the process of mixing PTFE and nanoparticles, people often use dry mixing method, but in the dry mixing process, with the heat generated during stirring, the temperature rises, PTFE will agglomerate, making the mixing uneven, so people start again The jet mill is used to break the agglomeration and improve the uniformity of mixing, but the jet mill...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method of PTFE (polytetrafluoroethylene) composite material filled with nano particles
  • Preparing method of PTFE (polytetrafluoroethylene) composite material filled with nano particles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Example 1: γ-glycidyl ether oxypropyltrimethoxysilane (KH560) modified Al 2 o 3 Fill the preparation method of PTFE composite material, carry out following steps successively:

[0028] 1) Weigh 0.4g of KH560 and dissolve it in 200ml of ethanol, stir for ten minutes, then add 10g of nano-Al 2 o 3 (60 nanometers), ultrasonically stirred at 25-35 ° C for 4 hours, filtered to recover the solvent (ie, ethanol), and the solid was dried at 100 ° C for 4 hours; modified nanoparticles --- modified nano-Al 2 o 3 .

[0029] 2) Weigh a certain amount of modified nano-Al 2 o 3 , added to 500 grams of PTFE, and stirred by hand for 10 minutes to form a pre-mixture (ie pre-mixed powder), wherein the modified nano-Al 2 o 3 The weight contents in the premix are 1%, 3%, 5%, 7% and 9%, respectively.

[0030] 3) Add 800 milliliters of ethanol to the premixture, stir ultrasonically for 40 minutes at a temperature of 25-30°C, filter and recover the ethanol, and dry (dry at 100°C for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparing method of a PTFE (polytetrafluoroethylene) composite material filled with nano particles. The method comprises the following steps of: (1) carrying out surface modification on nano particles by virtue of a coupling agent to obtain modified nano particles; (2) carrying out coarse mixing on PTFE and the modified nano particles to obtain premixing powder, wherein the weight content of the modified nano particles in the premixing powder is 0.1%-50%; (3) adding organic solvent in the premixing powder, carrying out ultrasonic agitation, filtering and drying to obtain PTFE composite powder with uniformly dispersed nano particles, wherein the weight ratio of the organic solvent to the premixing powder is 50-1000%; and (4) carrying out mould-pressing and sintering on the PTFE composite powder to obtain the PTFE composite material filled with nano particles. The PTFE composite material filled with nano particles, prepared by the method, has the characteristics of high mechanical property, high wear-resisting property, low frictional factor and the like.

Description

Technical field [0001] The invention relates to a method for preparing high-performance nanoparticle-filled PTFE composite materials, which are used to prepare PTFE engineering materials with high mechanical properties, high wear resistance and low friction coefficient, and are used in industrial fields such as mechanical bearing, friction and wear, sealing lubrication and so on. . Background technique [0002] Polytetrafluoroethylene (PTFE) resin has excellent high and low temperature resistance, corrosion resistance, aging resistance, high insulation, and non-stick properties. However, due to its poor dimensional stability, poor thermal conductivity, large creep, and low hardness, especially in It is easy to wear under load, which limits its application in the fields of mechanical bearing, friction and wear, and seal lubrication. Therefore, in order to expand the application fields of PTFE, it is necessary to modify its filling, that is, to use the advantages of filling p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/18C08K9/06C08K9/04C08K3/08C08K3/22C08K3/36C08K3/34C08K3/26B29B7/00B29C67/04B29C43/00
Inventor 汪海风杨辉徐意罗仲宽樊先平吴周安王树华
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap