Ultrahigh-glowing filament temperature and flame-retardant reinforced PBT (polybutylece terephthalate) composite material and preparation method thereof

A glow wire temperature, composite material technology, applied in the field of PBT composite material and its preparation, can solve the problems of high price, no value for widespread use, no product, etc., and achieves low cost, good application value and market prospect, easy-to-control effects

Inactive Publication Date: 2012-03-28
中山市纳普工程塑料有限公司
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But at present, there is no corresponding product in China, and although the performance of imported products is high, the price is extremely expensive, and it does not have the value of widespread promotion and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Raw materials and ratio:

[0024] PBT: intrinsic viscosity 0.8Dl / g, 41%;

[0025] Brominated flame retardant: Decabromodiphenylethane, trade name: Yabao 8010, 13%;

[0026] Phosphorus nitrogen flame retardant: melamine and triphenyl phosphate are mixed at 1:1, 7%;

[0027] Inorganic flame retardant: aluminum hydroxide and magnesium hydroxide mixed in 1:1, 5%;

[0028] Toughening agent: ethylene-methyl acrylate copolymer, 2.5%;

[0029] Antioxidant: Ciba 1076, 0.4%;

[0030] Lubricant: OP wax, 1.1%;

[0031] Glass fiber: 990 glass fiber produced by Jushi Group Co., Ltd., 30%; the commercially available glass fiber product itself has been surface-treated, but this invention is treated with a coupling agent, coupling agent: γ-aminopropyltriethoxy Silane, domestic model: KH550, dosage: 1% of glass fiber weight. This surfactant is used in a small amount and is not included in the total amount of the formula.

[0032] Production method: Put the weighed plastics and add...

Embodiment 2

[0034] PBT: intrinsic viscosity is 0.95Dl / g, 47%;

[0035] Brominated flame retardant: brominated styrene, trade name: Yabao 7010, 15%;

[0036] Phosphorus nitrogen flame retardant: melamine, 8%;

[0037] Inorganic flame retardant: antimony trioxide, 6%;

[0038] Toughener: EPDM grafted maleic anhydride, 2.5%,

[0039] Antioxidant: a mixture of Ciba 1076 and Ciba 168 at a ratio of 1:1, 0.3%;

[0040] Lubricant: OP wax, 1.2%;

[0041] Glass fiber: 988A glass fiber produced by Jushi Group Co., Ltd., 20%; the surface of commercially available glass fiber is treated with a coupling agent, coupling agent: γ-aminopropyltriethoxysilane, domestic model: KH550, dosage: glass 1% of fiber weight.

[0042] Production method: Put the weighed plastics and additives into the high mixer and mix for 3 minutes to obtain a uniform mixture, then control the processing temperature of the twin-screw extruder at 230-245°C, the screw speed at 300 rpm, and place the mixture in A twin-screw extru...

Embodiment 3

[0044] PBT: Intrinsic viscosity is 1.0Dl / g, 28%;

[0045] Brominated flame retardant: bromotriazine, trade name: Dead Sea bromine FR245, 17%;

[0046] Phosphorus nitrogen flame retardant: melamine derivative MCA, 9%;

[0047] Inorganic flame retardant: magnesium hydroxide, 6%;

[0048] Toughening agent: ethylene-methyl acrylate copolymer, 3.5%;

[0049] Antioxidant: a mixture of Ciba 1076 and Ciba 168 at a ratio of 1:1, 0.3%;

[0050] Lubricant: EBS, 1.2%;

[0051] Glass fiber: 990 glass fiber produced by Jushi Group Co., Ltd., 35%; commercially available glass fiber without additional surface treatment.

[0052] Production method: Put the weighed plastics and additives into a high mixer and mix for 4 minutes to obtain a uniform mixture, then control the processing temperature of the twin-screw extruder at 230-245°C, the screw speed at 320 rpm, and place the mixture in A twin-screw extruder is used for granulation, and the product is obtained by adding 35% by weight of gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a macromolecular material and a preparation method thereof, in particular to a PBT (polybutylece terephthalate) composite material and a preparation method thereof. The PBT composite material comprises the following components in percentage by weight: 20-25 percent of polybutylene terephthalate, 6-20 percent of bromine containing flame retardant, 5-15 percent of phosphorus and nitrogen containing flame retardant, 5-15 percent of inorganic flame retardant, 20-40 percent of glass fiber, 2-8 percent of toughening agent, 0.2-0.4 percent of antioxidant and 0.3-2 percent of lubricating dispersant. The preparation method comprises the following steps of weighing the components in the percentage by weight; putting plastic and adjuvant into a high-speed mixing machine, mixing the plastic and the adjuvant for 2-5 minutes and discharging a mixture; controlling a double-screw extruder to extrude and granulate the mixture; and adding glass fiber in the extruding process to obtain the PBT composite material. The flame-retardant property and the strength of the PBT composite material are obviously improved; using requirements of more occasions can be met; the PBT composite material has high application value and good market prospect; and the used raw materials are the conventional products in the field of engineering plastics and are low in cost.

Description

technical field [0001] The invention relates to a polymer material and a preparation method, in particular to a PBT composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is a thermoplastic engineering plastic widely used at present. It is widely used in electronic appliances because of its excellent heat resistance, weather resistance, and chemical resistance. With the development of modification technology, glass fiber reinforcement and mineral filling can effectively improve the shrinkage defect and greatly increase its application range. [0003] After its flame retardant modification, it is widely used in low-voltage electronic and electrical components. With the EU's increasingly stringent glow wire standards for electronic products in extreme environments, from the initial 750°C for 30s to the current 850°C for 30s, it can be seen that the resistance The fuel standards are gradually increasing. Therefore, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K13/04C08K7/14C08K13/06C08K9/06B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 杨继法何景连
Owner 中山市纳普工程塑料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com