Long-acting antirust grease and preparation method thereof

A grease and long-acting technology, applied in the petroleum industry, lubricating compositions, etc., can solve the problems of difficult disassembly again, poor durability of anti-rust grease, etc., to reduce the cost of oiling, uniform and soft film quality, excellent physical and chemical stability sexual effect

Active Publication Date: 2011-11-02
麻城天安化工股份有限公司
View PDF3 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a long-acting grease that is easy to coat, strong in adhesion, fast in film formation, good in durability, and easy to disassemble again, aiming at the technical problems of poor durability and difficult disassembly of the current antirust grease. Anti-rust grease to meet the requirements of various outdoor working conditions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Long-acting antirust grease and preparation method thereof
  • Long-acting antirust grease and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment 1: Preparation of long-acting antirust grease:

[0031] 1. Formula (parts by weight): 5 parts of base oil N4685; 5 parts of calcium hydroxide; 4 parts of barium petroleum sulfonate; 1.5 parts of Span-80; 1 part of 746 antirust agent; 0.5 parts of butyl-4-methylphenol; 5 parts of n-bromopropane; 0.1 parts of 2.3-dibutanone.

[0032] 2. Process operation steps:

[0033] Add the formulated amount of phenolic modified resin, 2.3-dibutanone into the dissolution and dispersion kettle, after static swelling for 3 to 5 hours, add the formulated amount of n-bromopropane, stir for 3 hours to completely dissolve, the solution is brownish red transparent, add Anti-rust additives in the prescribed amount - a mixture of barium petroleum sulfonate, Span-80, and 746 anti-rust agents, stirred for 1 hour to completely dissolve. After complete dissolution, add 85 parts of base oil N468 of formula quantity.

[0034] Add the formulated amount of 2.6-di-tert-butyl-4-methylpheno...

Embodiment 2-9

[0039] Embodiment 2-9: Preparation of long-acting antirust grease

[0040] 1. Formula (parts by weight)

[0041]

[0042] 2. Process operation steps: add 2.6-di-tert-butyl-4-methylphenol, 40°C for Examples 2-4, 45°C for Examples 5-6, and 50°C for Examples 7-9.

[0043] Add calcium hydroxide example 2~4 is 50 ℃, example 5~6 is 60 ℃, example 7~9 is 70 ℃.

[0044] Other technological operations are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
boiling pointaaaaaaaaaa
freezing pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of chemistry and relates to long-acting antirust grease and a preparation method thereof. The long-acting antirust grease mainly comprises the following components ( by weight): 70 to 90 parts of base oil, 3 to 6 parts of thickening agent, 4.5 to 8 parts of antirust additive, 4 to 8 parts of film-forming agent, 0.5 to 1 part of antioxidant, and 3 to 6 parts of assistant. The antirust grease has the characteristics that: the application of the grease is easy; the durability is high; the detachment of fasteners at next time is easy; the application range is wide; and the like. The long-acting antirust grease is suitable for outdoor steel fasteners which require anti-corrosion treatment and cannot be coated with paint.

Description

Technical field: [0001] The invention belongs to the field of chemical industry and relates to long-acting antirust oil and a preparation method thereof. Background technique: [0002] Outdoor steel fasteners involve railway rail fastening bolts, bridge telescopic parts, fastening bolts and parts, mining machinery fastening bolts and parts, oil field fastener bolts and parts, etc. These application places are often exposed to the outdoors, exposed to the sun, rain, hot summer and cold winter, and the working conditions are very harsh. Due to frequent disassembly and maintenance, and they cannot be painted for corrosion protection, they must be coated with anti-rust grease to reduce corrosion and prolong service life. [0003] In the past, waste engine oil was often used to brush. The surface material cost is very low, but the durability is poor, the frequency of brushing is high, the labor cost is high, the rust resistance is poor, and the pollution is large. With the impro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/00C10N30/12C10N50/10
Inventor 胡砚韬
Owner 麻城天安化工股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com