A kind of far-infrared carbon fiber low-temperature conductive heating paper and preparation method thereof

A far-infrared carbon fiber and carbon fiber technology, which is applied in special paper, synthetic cellulose/non-cellulose material pulp/paper, fiber raw material processing, etc., can solve the problem of uneven heating on the surface of electrothermal materials, excessive leakage current on the surface of finished products, and heating Unstable performance and other problems, to achieve the effect of improving human microcirculation, easy to transfer, and low current density

Inactive Publication Date: 2016-03-09
SHANGHAI RELI TECH GRP CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a far-infrared carbon fiber low-temperature conductive heating paper and its preparation method, which can solve the problem of uneven heating on the surface of existing electric heating materials, excessive temperature difference, unstable heating performance, low service life, and leakage current on the surface of finished products. Too large and other problems, used to make electric heating elements for plane heating

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of far-infrared carbon fiber low-temperature conductive heating paper and preparation method thereof
  • A kind of far-infrared carbon fiber low-temperature conductive heating paper and preparation method thereof
  • A kind of far-infrared carbon fiber low-temperature conductive heating paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0055] Please see attached figure 1 , attached figure 2 and attached image 3 Shown, the preparation method of a kind of far-infrared carbon fiber low-temperature conductive heating paper of the present invention, this method is raw material with raw material board, carbon fiber, nanometer far-infrared negative ion powder and diffusing agent, is made far-infrared carbon fiber low-temperature conductive by wet papermaking process Fever paper. The method at least includes the following steps:

[0056] Step 1, soak the raw pulp board in water for 10 minutes to 15 minutes, and then add it to the beater. The raw pulp board is soaked to make the plant fiber absorb water and swell, and the pulp formed by it is beaten; the pulp beating time is 60 minutes - between 120 minutes.

[0057] Step 2, preparing carbon fibers.

[0058] In step 2.1, polyacrylonitrile carbon fibers with a diameter of 4 μm to 10 μm and a length of 2 mm to 5 mm are mixed with polyacrylonitrile carbon fibers ...

Embodiment 1

[0077] Select directly commercially available pulp, the weight of which is 94% of the total weight, put the raw pulp board into water and soak for 10 minutes, put it into a beater and beat the pulp, after the pulp is beaten for 75 minutes, add water phase treatment and disperse Carbon fiber solution and nanometer far-infrared negative ion powder accounting for 1% of the total weight. The weight of carbon fiber is 4.5% of the total weight, the diffusion agent is made of polyethylene oxide and anionic polyacrylamide mixed at a weight ratio of 1:1, the weight of the diffusion agent mixture is 2% of the total weight, and the concentration of the diffusion agent solution is 5 %, using the above water phase dispersion to obtain a carbon fiber solution with good dispersibility, uniformity and hydrophilicity. Continue beating for 45 minutes, and the beating degree of the mixed slurry is stopped at 25 ° SR. Then 80 minutes after the homogenization of the mixed slurry, the homogenizati...

Embodiment 2

[0079] Identical as example 1 method, the weight of pulp is 89.5% of gross weight, and the weight of carbon fiber is 6% of gross weight, and the weight of diffusion agent mixture is 3.5% of gross weight, and the weight of nanometer far-infrared anion powder is 1% of gross weight %. The main technical indicators of the carbon fiber far-infrared low-temperature conductive heating paper made by this program: the resistance value of the carbon fiber far-infrared low-temperature conductive heating paper is 400-440Ω / m2, the resistivity is 10-20Ω cm, and the fixed weight is 55-60g / m ㎡, can be widely used in far-infrared low-temperature plane heating materials.

[0080]In summary, the heating element of the far-infrared carbon fiber low-temperature conductive heating paper of the present invention has a large surface area, and its entire surface is a heating surface and a heat dissipation surface, so the heat is even, and the surface temperature can reach 50°C-60°C, and the heat It i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

A far infrared carbon fiber low temperature conductive heating paper comprises an original pulp board, carbon fibers, nano far infrared negative ion powder and a diffusant. According to the invention, paper pulp is beaten and added with carbon fibers treated with carbonization processing, water phase processing and hydrophilism processing for dipping; after homogenizing and beating again, resistor of a mixed slurry is measured, and mixed slurry with a resistor within 2%-10% is manufactured into paper. The far infrared carbon fiber low temperature conductive heating paper prepared by the invention can heat uniformly, has high thermal conversion efficiency, near zero electromagnetic radiation, extremely small current density, and is safe for usage. In addition, the radiated far infrared light wave can activate water molecules in human body, raise blood oxygen content, enhance cell vitality, improve human body microcirculation and promote metabolism.

Description

technical field [0001] The invention relates to a conductive heating paper, in particular to a far-infrared carbon fiber low-temperature conductive heating paper and a preparation method thereof. Background technique [0002] At present, far-infrared electric heating products are developing rapidly, but there are many defects in the industrialized products made of them, mainly in: the surface of the heating material generates uneven heat, the temperature difference is too large, the heating performance is unstable, and the service life is low , The surface leakage current of the finished electrothermal material is too large. These defects make the product quality questioned by consumers, and also bring great safety hazards. [0003] An infrared heating paper using polyacrylonitrile-reinforced carbon fiber as an infrared heat source in the prior art. It is made of hollow pulp as a base, and then a certain amount of short carbon fiber with an infrared protective film is added ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D21H27/00D21H13/50D21H21/52D21H21/14
Inventor 全俊成
Owner SHANGHAI RELI TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com