Functional master batch for antisticking BOPA film and production process thereof

A functional masterbatch and anti-blocking technology, applied in the field of biaxially oriented BOPA film functional masterbatch, can solve the problems of difficulty in separation, film scrap, film adhesion, etc., to reduce surface polarity, reduce friction coefficient, and improve roughness. Effect

Active Publication Date: 2011-10-05
GUANGDONG MODERN HIGH TECH FIBER CO LTD
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The most common catastrophic problems encountered in the production and use of BOPA films are due to the influence of static electricity, temperature, pressure and other factors, as well as the migration and penetration of short-chain molecules between the two layers of the film or due to the smooth surface of the film. Film adhesion occurs and it is difficult to separate, and in severe cases, the entire roll of film will be scrapped
In particular, modern plastic processing is developing towards automation, high speed and high quality. The faster the processing speed, the easier it is to generate static electricity due to friction, and the easier it is for films to stick together, which seriously hinders high-speed production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Example 1: An anti-blocking BOPA film functional masterbatch, the raw material weight ratio of its preparation is: PA6: 95%; POSS-1: 5%. According to the ratio, the above raw materials are added into the twin-screw by using a precision weight-loss self-measurement feeding system, and then the melt is extruded and granulated. The speed is 50~100 kg / hour, and the speed of the granulator is 16~21HZ. Put the prepared masterbatch in a vacuum dryer at 100~150℃, and dry it for 16~24 hours to get the finished masterbatch.

Embodiment 2

[0016] Example 2: An anti-blocking BOPA film functional masterbatch, the raw material weight ratio of which is prepared is: PA6: 90%; POSS-1: 10%. According to the ratio, the above raw materials are added into the twin-screw by using a precision weight-loss self-measurement feeding system, and then the melt is extruded and granulated. The speed is 50~100 kg / hour, and the speed of the granulator is 16~21HZ. Put the prepared masterbatch in a vacuum dryer at 100~150℃, and dry it for 16~24 hours to get the finished masterbatch.

Embodiment 3

[0017] Example 3: An anti-blocking BOPA film functional masterbatch, the raw material weight ratio of its preparation is: PA6: 95%; POSS-2: 5%. According to the ratio, the above raw materials are added into the twin-screw by using a precision weight-loss self-measurement feeding system, and then the melt is extruded and granulated. The speed is 50~100 kg / hour, and the speed of the granulator is 16~21HZ. Put the prepared masterbatch in a vacuum dryer at 100~150℃, and dry it for 16~24 hours to get the finished masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a functional master batch for an antisticking BOPA film and a production method thereof, and the master batch is used to prepare a biaxial stretching BOPA film. The functional master batch is prepared by the following raw materials by weight: 90-95% of PA; and 5-10% of cage-shaped polyhedral oligomeric silsesquioxane (POSS), wherein the typical molecular formula of POSS is R7R' (SiO1.5)8, and the beneficial effects are that POSS is used as an antisticking agent, and fine aggregated micro-areas are formed on the surface of the BOPA film by the nano effects of POSS, which increase the roughness of the film surface and decrease the friction coefficient between films; on the other hand, the addition of POSS can reduce the surface polarity of the BOPA film, increase the hydrophobicity of the BOPA film, decrease the penetration of water, and thus improve the barrier property of the BOPA film, and has no adverse effect on mechanical properties; additionally, no other additive is required to be added during the production process of the master batch.

Description

technical field [0001] The invention relates to a biaxially stretched BOPA film functional masterbatch and a production method thereof. The masterbatch can be used to prepare a biaxially stretched BOPA film and is used in the field of plastic packaging. Background technique [0002] Biaxially oriented nylon film (BOPA) is an important material for the production of various composite packaging materials, and has become the third largest packaging material after polypropylene biaxially oriented film (BOPP) and polyester biaxially oriented film (BOPET). As a high barrier film base material, BOPA has higher barrier performance than polypropylene biaxially oriented film BOPP film, and BOPA film has high resistance to cracking, impact resistance, tensile strength and puncture resistance. The best, with excellent softness, good puncture resistance, wide application range (-60°C~150°C), acid, alkali, grease and various common organic solvents, especially excellent grease resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K5/549C08J3/22
Inventor 郭清海江建明金俊弘李光杨胜林
Owner GUANGDONG MODERN HIGH TECH FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com