Palladium/active carbon catalyst and application thereof in synthesizing N,N'-dibenzylethylenediamine

A technology of dibenzylethylenediamine and activated carbon, which can be used in the preparation of organic compounds, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., and can solve the uneven and wide distribution of metal active components , Restricting the activity, selectivity and stability of supported metal catalysts, low metal utilization rate and other issues, to achieve the effect of improving metal utilization rate

Active Publication Date: 2011-09-14
嘉善县国创新能源研究院
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Supported metal catalysts prepared by traditional methods cannot effectively adjust and control the morphology of metal particles on the surface of the support, that is, the metal active components are often dispersed on the surface of the support in the form of uneven and wide distribution, and the number of active metal active sites on the surface of the support does not vary. There is no year-on-year increase with the increase of metal loading, and a considerable part of the metal particles accumulates without exerting its proper catalytic performance, which makes the metal utilization rate low and restricts the activity, selectivity and stability of the supported metal catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Palladium/active carbon catalyst and application thereof in synthesizing N,N'-dibenzylethylenediamine
  • Palladium/active carbon catalyst and application thereof in synthesizing N,N'-dibenzylethylenediamine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Weigh 10g of activated carbon, the specific surface area of ​​activated carbon is 1600m 2 / g, activated carbon was soaked in 120 milliliters of NaCl solution with a concentration of 0.5mol / l for 2 hours, filtered, and washed with deionized water until no chloride ions were detected. Then the treated activated carbon was formulated into 100ml slurry with a temperature of 60°C, and 10ml of H2PdCl4 solution (Pd content was 0.02g / ml) was slowly added dropwise, stirred for 4h, and the pH value of the solution was adjusted to weakly alkaline with 10% NaOH solution. (pH=7.1), and the temperature was lowered to room temperature, filtered, and washed with deionized water until neutral. The unreduced catalyst was prepared into a 150 ml slurry at 30° C., and then 2 ml of 55% hydrazine hydrate solution was slowly added dropwise, and the stirring was continued for 2 hours. The reduced catalyst was filtered, washed with deionized water until neutral, and finally dried in the air at ...

Embodiment 2

[0029] Weigh 10g of activated carbon, the specific surface area of ​​activated carbon is 1600m 2 / g, activated carbon was immersed in 120 milliliters of NaCl solution with a concentration of 1.0mol / l for 2 hours, filtered, and washed with deionized water until no chloride ions were detected. Then the treated activated carbon was formulated into a 100ml slurry at a temperature of 70°C, and 20ml of H 2 PdCl 4 Solution (Pd content is 0.02g / ml), stirred for 6h, adjusted the pH value of the solution to weak alkaline (pH=8) with 10% NaOH solution, and lowered the temperature to room temperature, filtered, and washed with deionized water until neutral . The unreduced catalyst was prepared into a 150ml slurry at 30°C, and then 2ml of 55% hydrazine hydrate solution was slowly added dropwise, and the stirring was continued for 2 hours. The reduced catalyst was filtered, washed with deionized water until neutral, and finally dried in the air at room temperature, and the wet sample was ...

Embodiment 3

[0031] Weigh 10g of activated carbon, the specific surface area of ​​activated carbon is 1600m 2 / g, activated carbon was soaked in 120 ml of NaCl solution with a concentration of 1.5 mol / l for 2 hours, filtered, and washed with deionized water until no chloride ions were detected. Then the treated activated carbon was formulated into a 100ml slurry at a temperature of 80°C, and 20ml of H 2 PdCl 4 Solution (Pd content is 0.02g / ml), stirred for 6h, adjusted the pH value of the solution to weak alkaline (pH=8) with 10% NaOH solution, and lowered the temperature to room temperature, filtered, and washed with deionized water until neutral . The unreduced catalyst was prepared into a 150ml slurry at 30°C, and then 2ml of 55% hydrazine hydrate solution was slowly added dropwise, and the stirring was continued for 2 hours. The reduced catalyst was filtered, washed with deionized water until neutral, and finally dried in the air at room temperature, and the wet sample was taken and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a palladium / active carbon catalyst and application thereof in synthesizing N,N'-dibenzylethylenediamine. The palladium / active carbon catalyst is prepared by the following steps of: impregnating active carbon by using aqueous solution of sodium halide, filtering, and washing a filter cake until halogen ions are absent; impregnating the treated active carbon by using aqueoussolution of H2PdCl4; and regulating the pH value of the solution until the solution is alkaline, filtering, washing a filter cake until the filter cake is neutral, and reducing the filter cake by using a reducing agent, and drying the obtained neutral product to obtain the palladium / active carbon catalyst. The palladium / active carbon catalyst has controllable size, most palladium particles in thecatalyst have the particle size of 2 to 5nm, the catalyst is used for synthesizing the N,N'-dibenzylethylenediamine by N,N'-dibenzylidene ethylenediamine through catalytic hydrogenation reduction, and has high activity, selectivity and stability; moreover, the catalyst is easy to prepare, environment-friendly and suitable for industrial application, and precious metal palladium is easy to recover.

Description

(1) Technical field [0001] The invention relates to a palladium activated carbon catalyst and its application in the preparation of N, N'-dibenzylethylenediamine by catalytic hydrogenation of N,N'-dibenzylideneethylenediamine. (2) Background technology [0002] N, N'-dibenzylethylenediamine diacetate (abbreviated as DBED), is widely used in the production of long-acting penicillin G, long-acting penicillin V, long-acting ampicillin and long-acting cephalosporins and other drugs. It is an important high value-added pharmaceutical intermediate, and the output value of antibiotic drugs synthesized with it is hundreds of millions. [0003] At present, the domestic DBED synthesis method basically adopts the organic synthesis method using benzyl chloride and ethylenediamine as raw materials. This route has the advantages of simple process, short process, and small investment, and is currently a relatively mature and widely used synthetic process. However, the yield of the synthe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J23/44B01J35/10C07C211/27C07C209/70
Inventor 李小年马磊袁俊峰卢春山张群峰许孝良
Owner 嘉善县国创新能源研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com