Colored kiln-transformation ceramic product and manufacturing process thereof

A production process and colorful kiln technology, applied to clay products, other household utensils, household utensils, etc., can solve the problems of single color and low yield rate of qualified products, and achieve round luster, high yield rate, and beautiful colors Effect

Inactive Publication Date: 2011-09-07
路今铧
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, according to this process, the yield of qualified products is still low, and the color is monotonous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This kind of colorful kiln-transformed ceramics includes an embryo body and a glaze layer, wherein the embryo mud used to make the embryo body is composed of the following parts by weight: 30 parts of Zibo pottery clay, 10 parts of Zibo Jiaoge, 15 parts of Laizhou quartz, and Laizhou feldspar 15 parts, Shanxi Datong soil 10 parts, Yunnan kaolin 12 parts, aluminum powder 8 parts.

[0023] The glaze a of this colorful kiln-changing ceramic is composed of the following parts by weight: 30 parts of feldspar, 8 parts of dolomite, 30 parts of quartz, 3 parts of vat soil, 5 parts of barium carbonate, 1 part of talc, and 10 parts of frit 1 part, 1 part of zinc oxide, 1 part of copper oxide, 5 parts of iron oxide.

[0024] Glaze b is composed of the following parts by weight: 30 parts of feldspar, 15 parts of dolomite, 20 parts of quartz, 3 parts of pot soil, 10 parts of barium carbonate, 1 part of talc, 15 parts of frit, and 1 part of zinc oxide , 5 parts of copper oxide, 1 pa...

Embodiment 2

[0031] This colorful kiln-transformed ceramic includes an embryo body and a glaze layer, wherein the embryo mud used to make the embryo body is composed of the following parts by weight: 32 parts of Zibo pottery clay, 12 parts of Zibo Jiaoge, 10 parts of Laizhou quartz, and Laizhou feldspar 12 parts, Shanxi Datong soil 10 parts, Yunnan kaolin 12 parts, aluminum powder 12 parts.

[0032] The glaze a of this kind of colorful kiln-changing ceramics is composed of the following parts by weight: 35 parts of feldspar, 10 parts of dolomite, 40 parts of quartz, 5 parts of large pot soil, 10 parts of barium carbonate, 5 parts of talc, and 10 parts of frit Parts, 2 parts of zinc oxide, 1 part of copper oxide, 5 parts of iron oxide.

[0033]Glaze b is composed of the following parts by weight: 35 parts of feldspar, 15 parts of dolomite, 20 parts of quartz, 5 parts of pot soil, 10 parts of barium carbonate, 5 parts of talc, 15 parts of frit, and 2 parts of zinc oxide , 5 parts of copper ...

Embodiment 3

[0041] This colorful kiln-transformed ceramic includes an embryo body and a glaze layer, wherein the embryo mud used to make the embryo body is composed of the following parts by weight: 35 parts of Zibo pottery clay, 15 parts of Zibo Jiaoge, 12 parts of Laizhou quartz, and Laizhou feldspar 12 parts, 8 parts of Shanxi Datong soil, 10 parts of Yunnan kaolin, 8 parts of aluminum powder.

[0042] The glaze a of this kind of colorful kiln-changing ceramics is composed of the following parts by weight: 35 parts of feldspar, 10 parts of dolomite, 30 parts of quartz, 3 parts of large pot soil, 5 parts of barium carbonate, 5 parts of talc, and 10 parts of frit Parts, 2 parts of zinc oxide, 1 part of copper oxide, 5 parts of iron oxide.

[0043] Glaze b is composed of the following parts by weight: 35 parts of feldspar, 15 parts of dolomite, 25 parts of quartz, 5 parts of pot soil, 10 parts of barium carbonate, 5 parts of talc, 20 parts of frit, and 2 parts of zinc oxide , 5 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a colored kiln-transformation ceramic product and a manufacturing process thereof and belongs to the field of ceramic art manufacture. The colored kiln-transformation ceramic product comprises a blank body and a glazing layer and is made by a special burning process. The invention is characterized in that: the blank paste comprises the following ingredients (by weight): 35parts of pottery clay (produced in the Zibo city), 15 parts of flint clay (produced in the Zibo city), 12 parts of quartz (produced in the Laizhou city), 12 parts of feldspar (produced in the Laizhoucity), 8 parts of soil (produced in the Datong city of the Shanxi province), 10 parts of kaolin (produced in the Yunnan province), and 8 parts of aluminum powders. The glazing material comprises the following ingredients (by weight): 35 parts of feldspar, 10 parts of dolomite, 10 parts of quartz, 3 parts of vat soil, 5 parts of barium carbonate, 5 parts of talc, 20 parts of fusion cake, 2 parts of zinc oxide, 1 part of copper oxide and 5 parts of ferric oxide. The colored kiln-transformation ceramic product is made by performing dry-method pulverization and firing in a firing atmosphere with a certain firing temperature curve. The ceramic product has rich and changeable color, integrates the visual effects of miscibility and fluidity of a variety of coloring agents, is the most beautiful ceramic treasure in ceramic history, and is called by multiple experts as a great innovation in China ceramic history.

Description

technical field [0001] The colorful kiln-transformed ceramics and its production process belong to the field of ceramic art production, and specifically relate to a production process of high-end colorful kiln-transformed ceramics. Background technique [0002] When firing porcelain, anyone who finds that the shape or glaze color is not the expected shape or glaze color after opening the kiln, so that the handed down porcelain sometimes has a special situation, can be said to be "kiln transformation". "Barnyard History Compilation" said: "Porcelain has the same quality, then becomes a different quality, and the same color, then becomes a different color, the combination of water and soil, which cannot be added by human coincidence, is called kiln transformation." It can be roughly divided into several types such as deformation, discoloration, and deterioration. The history of kiln changes can be traced back to the Western Zhou Dynasty. At that time, opalescent spots appeare...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/00C04B33/04C04B33/34C04B41/86
Inventor 路今铧路晗
Owner 路今铧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com