Honeycomb catalyst for catalytically incinerating sulfur containing gases and preparation method

A technology of catalytic incineration and gas catalysis, which is applied in the direction of catalyst activation/preparation, physical/chemical process catalysts, combustion methods, etc., and can solve the problems of large bed air resistance, low operating space velocity, and poor sulfur resistance of catalytic incineration reactors. problems, to achieve the effects of small air resistance, high operating space velocity, and low catalyst cost

Active Publication Date: 2011-05-04
CHINA PETROLEUM & CHEM CORP +1
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned existing sulfur-containing gas catalytic incineration catalysts have one or more disadvantages of complex components, poor sulfur resistance, high cost, and the need to adopt complex processes. In addition, the above-mentioned catalysts are generally spherical. Catalytic incineration reactor bed layer gas resistance is relatively large, and the operating space velocity is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Measure 50 mL of tetrabutyl titanate into a 500 mL beaker, add 50 mL of absolute ethanol under electromagnetic stirring, and stir evenly at room temperature to prepare solution A. Prepare 100 mL of solution B with volume ratios of 25%, 5%, 10% and 60% of glacial acetic acid, hydrochloric acid, distilled water and absolute ethanol, respectively. Solution A was added dropwise to solution B under electromagnetic stirring, and a light yellow sol was prepared after fully stirring. Boil the honeycomb ceramic carrier in 5% nitric acid solution for 30 minutes, take it out, wash it with distilled water for 5 times, and dry it. After immersing the processed honeycomb ceramics in the sol for 2 minutes, take it out slowly, dry it at 105°C, then bake it in a muffle furnace at 500°C for 2 hours, cool it down to room temperature naturally, repeat the above steps 6 times, and obtain the desired titanium dioxide coating thick carrier.

[0019] Weigh 100g oxalic acid (C 2 h 2 o 4 2H...

Embodiment 2

[0025] The titanium dioxide powder of 300g, the methyl cellulose powder of 5g and the ammonium metavanadate of 20g are mixed and ground 45min in ball mill, add silver nitrate (AgNO 3 ) solution [5g AgNO 3 Dissolve in dilute nitric acid (2ml nitric acid + 14ml distilled water)], continue to grind for 15 minutes, and add distilled water to make the ground material evenly mixed into a paste with appropriate hardness, put the paste into a honeycomb mold for extrusion molding, and dry at 60°C 5h and 105°C drying for 6h, 250°C for 8h and 500°C for 10h. The specific surface area of ​​the prepared catalyst is 1100m 2 / m 3 , the hole spacing is 3.0mm, and the wall thickness is 0.5mm. The composition of the catalyst is V 2 o 5 4.7%, Ag 1.0%, TiO 2 94.3%.

Embodiment 3

[0027] The titanium dioxide powder of 450g, the vanadium pentoxide powder of 20g, the silver nitrate powder of 7g, the polyacrylamide of 6g and the gac powder of 2g are mixed and ground 45min in ball mill, while grinding, slowly add ethanolamine solution (ethanolamine and distilled water volume ratio of 1:5) to make a paste with appropriate hardness, put the paste into a honeycomb mold for extrusion molding, dry at 60°C for 7 hours and 105°C for 4 hours, bake at 250°C for 8 hours and bake at 500°C for 10 hours . The specific surface area of ​​the prepared catalyst is 960m 2 / m 3 , the hole spacing is 3.0mm, and the wall thickness is 0.5mm. The composition of the catalyst is V 2 o 5 4.2%, Ag 0.9%, TiO 2 94.9%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a honeycomb catalyst for catalytically incinerating sulfur containing gases and a preparation method. The catalyst is a honeycomb monomer and comprises the following active ingredients by weight percent: 1.0-15% of oxide of vanadium, 0.1-5.0% of silver and 80-99% of titanium dioxide. The preparation method is characterized by dipping vanadium and silver on a honeycomb titanium dioxide carrier. The catalyst has the characteristics of high performance, low cost, simple adaptable process, high removal rates of hydrogen sulfide and carbonyl sulfide and the like, and can be used for incinerating compounds in the gases, such as hydrogen sulfide, carbon disulfide, carbonyl sulfide and the like.

Description

technical field [0001] The invention relates to a honeycomb sulfide-containing waste gas catalytic incineration catalyst and a preparation method thereof, which is suitable for the treatment of various waste gas containing sulfur compounds such as hydrogen sulfide, carbon disulfide and carbonyl sulfide, and can convert the above-mentioned sulfide into odor and toxicity. Low sulfur dioxide, especially suitable for catalytic incineration treatment of sulfur recovery Claus process exhaust gas and geothermal power plant exhaust gas. Background technique [0002] Hydrogen sulfide and organic sulfides (such as carbon disulfide, carbonyl sulfide, etc.) are a class of odorous pollutants with varying degrees of toxicity to the human body, mainly from industrial exhaust gases such as oil refining, natural gas, chemical industry, sewage treatment, and geothermal power generation. Pollutant discharge standard (GB 14554-93) strictly limits its discharge. Taking an oil refinery as an exa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/68B01J35/04B01J37/02B01J37/04B01D53/86B01D53/52B01D53/48F23G7/07
Inventor 李凌波刘忠生
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More