Method for preparing DSSC (Dye Sensitized Solar Cell) with double-helix structure

A solar cell, double helix structure technology, applied in photosensitive devices, circuits, photovoltaic power generation, etc., can solve the limitations of breakthrough progress and expansion of application fields, dye-sensitized solar cells have good low-light performance, low light utilization, etc. problems, to achieve the effect of improving long-term stability, promoting the process of industrialization, and good low-light performance

Inactive Publication Date: 2012-05-23
IRICO
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its poor long-term stability and the low utilization rate of solar cells to light, it is a prerequisite for its industrialization to improve its long-term stability and increase its light utilization rate [Kuang, D.; Wang, P .; Ito, S.; Zakeeruddin, S.M.; Gra¨tzel, M.J. Am. Chem. Soc. 2006, 128, 7732.]
[0003] However, for a long time, DSSC cells have been in the form of flat plates, so the battery area is relatively large, and it is difficult to take advantage of the low-light performance of dye-sensitized solar cells, which largely limits the breakthrough of its technology and the expansion of its application fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing DSSC (Dye Sensitized Solar Cell) with double-helix structure
  • Method for preparing DSSC (Dye Sensitized Solar Cell) with double-helix structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Step 1: Preparation of photoanode

[0027] 1) Preparation of titania sol precursor solution: first mix 0.1 mol titanyl sulfate and water at a ratio of 2 mol / L titanium ion concentration at 15-20 ° C, then let stand for 12 hours to clarify, filter and mix with 1 mol / L ammonia water The co-precipitation was titrated into 200ml deionized water until the pH value was equal to 7, and the obtained white precipitate was washed by centrifugation until it was washed with Ba(NO 3 ) 2 The solution had no detectable residual SO 4 2- ions, and then at 60°C, the white precipitate was pressed by Ti 4+ : oxalic acid: the molar ratio of hydrogen peroxide is 1: 5: 5 to dissolve, then the pH value of this solution is adjusted to 7-8 with ammonia water, after standing for 10 hours, the titanium dioxide sol precursor solution is obtained;

[0028] 2) The helical Ti anode (such as figure 1 As shown in (a), it was ultrasonically treated three times with ethanol and acetone respectively, ...

Embodiment 2

[0034] Step 1: Preparation of photoanode

[0035] 1) Preparation of titania sol precursor solution: first, 0.1mol of TiCl 4 with 400ml of 1mol / L NaHCO 3 Co-precipitate and titrate the white precipitate obtained in 100ml deionized water, centrifuge and wash three times, and then press Ti 4+ : citric acid: the molar ratio of hydrogen peroxide is 1: 5: 6 to dissolve, then the pH value of this solution is adjusted to 7-8 with ammonia water, after standing for 15 hours, the titanium dioxide sol precursor solution is obtained;

[0036] 2) The helical Ti anode was ultrasonically treated three times with ethanol and acetone respectively, then placed in the titanium dioxide sol precursor solution, hydrothermally treated in a hydrothermal kettle at 250°C for 8h; then heat-treated at 200°C for 4h to obtain a titanium dioxide-coated The pretreatment photoanode is then soaked in the dye (the dye is selected as black dye), soaked for 24h and then taken out to wash off the dye on the surfa...

Embodiment 3

[0042] Step 1: Preparation of photoanode

[0043] 1) Preparation of titania sol precursor solution: first titrate the white precipitate obtained in 200 ml of deionized water with 0.1 mol of titanium sulfate and 400 ml of 1 mol / L NaOH co-precipitation, centrifuge and wash three times, and then at 80° C. Ti 4+ : tartaric acid: the mol ratio of hydrogen peroxide is 1: 10: 10 is dissolved, and then the pH value of this solution is adjusted to 7-8 with ammoniacal liquor, promptly obtains titania sol precursor solution after standing for 12 hours;

[0044]2) The spiral Ti anode was ultrasonically treated three times by ethanol and acetone respectively, then placed in the titanium dioxide sol precursor solution, and hydrothermally treated in a hydrothermal kettle at 160°C for 18h; then heat-treated at 200°C for 4h to obtain a titanium dioxide-coated The pretreatment photoanode, then soak it in the dye (dye selection N719), after soaking for 24h, take out the dye on the surface and r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a DSSC (Dye Sensitized Solar Cell) with a double-helix structure, which comprises the steps of: firstly, preparing a photo anode through preparing a titanium dioxide sol precursor solution and treating by using a helical Ti anode; secondly, preparing a cathode by using helical Ti; and thirdly, carrying out cell assembly sealing on the prepared photoanode and the cathode to prepare the DSSC. The DSSC prepared by using the method has effectively improved long-term stability, can improve the utilization ratio of the light rays by the solar cell, and is beneficial to the development of good low light level, thereby being helpful to promote the industrialized procedure of the DSSC.

Description

technical field [0001] The invention belongs to the field of new material technology and new energy technology; in particular, it relates to a dye-sensitized solar cell and a preparation method of a dye-sensitized solar cell with a double helix structure used in photocatalysis-related fields. Background technique [0002] Dye-sensitized solar cells have become a research hotspot in the field of solar cells due to their low cost, simple preparation process conditions and good environmental compatibility. However, due to its poor long-term stability and the low utilization rate of solar cells to light, it is a prerequisite for its industrialization to improve its long-term stability and increase its light utilization rate [Kuang, D.; Wang, P .; Ito, S.; Zakeeruddin, S.M.; Gra¨tzel, M.J. Am. Chem. Soc. 2006, 128, 7732.]. [0003] However, for a long time, DSSC cells have been in the form of flat plates, so the battery area is relatively large, and it is difficult to take advan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G9/20H01G9/04H01G9/08H01M14/00H01L51/48
CPCY02E10/542Y02E10/50Y02E10/549Y02P70/50
Inventor 刘文秀
Owner IRICO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com